Roll Casting of Al-25%Si
- Osaka Institute of Technology, Omiya Asahiku Osaka city 535-8585 (Japan)
- Graduate School of Osaka Institute of Technology, Omiya Asahiku Osaka city 535-8585 (Japan)
- Gunma University, Kiryu city, 376-8515 (Japan)
Strip casting of Al-25%Si strip was tried using an unequal diameter twin roll caster. The diameter of the lower roll (large roll) was 1000 mm and the diameter of the upper roll (small roll) was 250 mm. Roll material was mild steel. The sound strip could be cast at the speeds ranging from 8 m/min to 12 m/min. The strip did not stick to the roll without the parting material. The primary Si, which existed at centre area of the thickness direction, was larger than that which existed at other area. The size of the primary Si was smaller than 0.2 mm. Eutectic Si was smaller 5 {mu}m. The as-cast strip was ranging from 2 mm to 3 mm thick and its width was 100 mm. The as-cast strip could be hot rolled down to 1 mm. The hot rolled strip was cold rolled. The primary Si became smaller and the pore occurred around the primary Si after the rolling.
- OSTI ID:
- 21516720
- Journal Information:
- AIP Conference Proceedings, Vol. 1353, Issue 1; Conference: ESAFORM 2011: 14. international ESAFORM conference on material forming, Belfast, Northern Ireland (United Kingdom), 27-29 Apr 2011; Other Information: DOI: 10.1063/1.3589709; (c) 2011 American Institute of Physics; ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Microstructure Evolution During Spray Rolling and Heat Treatment of 2124 Al
Roll Casting of Aluminum Alloy Clad Strip
Related Subjects
ALUMINIUM ALLOYS
CASTING
CASTINGS
HOT WORKING
ROLLING
SILICON ALLOYS
SOUND WAVES
STEELS
THERMAL CONDUCTIVITY
THICKNESS
VELOCITY
ALLOYS
CARBON ADDITIONS
DIMENSIONS
FABRICATION
IRON ALLOYS
IRON BASE ALLOYS
MATERIALS WORKING
PHYSICAL PROPERTIES
THERMODYNAMIC PROPERTIES
TRANSITION ELEMENT ALLOYS