Structure factor changes in supercooled yttria-alumina
Journal Article
·
· AIP Conference Proceedings
- Centre for Advanced Functional Materials and Devices Institute of Mathematics and Physics, Aberystwyth University, Aberystwyth SY23 3BZ (United Kingdom)
- Ecole nationale Superieure de Chemie de paris, 11 rue Pierre et marie Curies, 75231, Paris (France)
- CNRS-CRMHT, 1d avenue de la Rechereche Scietifique, 45071 Orleans cedex 9 (France)
Changes in the structure factor of yttria-alumina liquids have been identified in the supercooled range. Different inter-polyhedral configurations between AlO{sub 4} and YO{sub 6} groups distinguish low density and high density liquid phases. The coexistence of phases at high temperatures have been identified in simultaneous measurements of small angle x-ray scattering.
- OSTI ID:
- 21260240
- Journal Information:
- AIP Conference Proceedings, Vol. 1092, Issue 1; Conference: 6. international conference on synchrotron radiation in materials science, Campinas (Brazil), 20-23 Jul 2008; Other Information: DOI: 10.1063/1.3086244; (c) 2009 American Institute of Physics; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
The Structure of Amorphous and Deeply Supercooled Liquid Alumina
Strength and phase stability of yttria-ceria-doped tetragonal zirconia/alumina composites sintered and hot isostatically pressed in argon-oxygen gas atmosphere
Effect of Yttria Content on the Zirconia Unit Cell Parameters
Journal Article
·
Tue Mar 19 00:00:00 EDT 2019
· Frontiers in Materials
·
OSTI ID:21260240
+6 more
Strength and phase stability of yttria-ceria-doped tetragonal zirconia/alumina composites sintered and hot isostatically pressed in argon-oxygen gas atmosphere
Journal Article
·
Fri Mar 01 00:00:00 EST 1991
· Journal of the American Ceramic Society; (United States)
·
OSTI ID:21260240
Effect of Yttria Content on the Zirconia Unit Cell Parameters
Journal Article
·
Mon Feb 06 00:00:00 EST 2012
· J. Am. Ceram. Soc.
·
OSTI ID:21260240
+2 more