Structural characterization, thermal, spectroscopic and magnetic studies of the (C{sub 3}H{sub 12}N{sub 2}){sub 0.75}[Mn{sub 1.50}{sup II}Fe{sub 1.50}{sup III}(AsO{sub 4})F{sub 6}] and (C{sub 3}H{sub 12}N{sub 2}){sub 0.75}[Co{sub 1.50}{sup II}Fe{sub 1.50}{sup III}(AsO{sub 4})F{sub 6}] compounds
- Departamento de Mineralogia y Petrologia, Universidad del Pais Vasco/EHU, Apdo. 644, E-48080 Bilbao (Spain)
- Departamento de Quimica Inorganica, Universidad del Pais Vasco/EHU, Apdo. 644, E-48080 Bilbao (Spain)
- Departamento de Fisica Aplicada II, Facultad de Ciencia y Tecnologia, Universidad del Pais Vasco/EHU, Apdo. 644, E-48080 Bilbao (Spain)
The (C{sub 3}H{sub 12}N{sub 2}){sub 0.94}[Mn{sub 1.50}Fe{sub 1.50}{sup III}(AsO{sub 4})F{sub 6}] and (C{sub 3}H{sub 12}N{sub 2}){sub 0.75}[Co{sub 1.50}Fe{sub 1.50}{sup III}(AsO{sub 4})F{sub 6}] compounds 1 and 2 have been synthesized using mild hydrothermal conditions. These phases are isostructural with (C{sub 3}H{sub 12}N{sub 2}){sub 0.75}[Fe{sub 1.5}{sup II}Fe{sub 1.5}{sup III}(AsO{sub 4})F{sub 6}]. The compounds crystallize in the orthorhombic Imam space group. The unit cell parameters calculated by using the patterns matching routine of the FULPROOF program, starting from the cell parameters of the iron(II),(III) phase, are: a 7.727(1) A, b = 11.047(1) A, c = 13.412(1) A for 1 and a = 7.560(1) A, b 11.012(1) A, c = 13.206(1) A for 2, being Z = 8 in both compounds. The crystal structure consists of a three-dimensional framework constructed from edge-sharing [M{sup II}(1){sub 2}O{sub 2}F{sub 8}] (M = Mn, Co) dimeric octahedra linked to [Fe{sup III}(2)O{sub 2}F{sub 4}] octahedra through the F(1) anions and to the [AsO{sub 4}] tetrahedra by the O(1) vertex. This network gives rise two kinds of chains, which are extended in perpendicular directions. Chain 1 is extended along the a-axis and chain 2 runs along the c-axis. These chains are linked by the F(1) and O(1) atoms and establish cavities delimited by eight or six polyhedra along the [1 0 0] and [0 0 1] directions, respectively. The propanediammonium cations are located inside these cavities. The thermal study indicates that the structures collapse with the calcination of the organic dication at 255 and 285 deg. C for 1 and 2, respectively. The Moessbauer spectra in the paramagnetic state indicate the existence of two crystallographically independent positions for the iron(III) cations and a small proportion of this cation in the positions of the divalent Mn(II) and Co(II) ones. The IR spectrum shows the protonated bands of the H{sub 2}N- groups of the propanediamine molecule and the characteristic bands of the [AsO{sub 4}]{sup 3-} arsenate oxoanions. In the diffuse reflectance spectra, it can be observed the bands characteristic of trivalent iron(III) cation and divalent Mn(II) and Co(II) ones in a distorted octahedral symmetry. The calculated Dq and B-Racah parameters for the cobalt(II) phase are 710 and 925 cm{sup -1}, respectively. The ESR spectra of compound 1 maintain isotropic with variation in temperature, being g = 1.99. Magnetic measurements for both compounds indicate that the main magnetic interactions are antiferromagnetic in nature. However, at low temperatures small ferromagnetic components are detected, which are probably due to a spin decompensation of the two different metallic cations. The hysteresis loops give values of the remnant magnetization and coercive field of 84.5, 255 emu/mol and 0.01, 0.225 T for phases 1 and 2, respectively.
- OSTI ID:
- 21144006
- Journal Information:
- Materials Research Bulletin, Vol. 43, Issue 5; Other Information: DOI: 10.1016/j.materresbull.2007.05.016; PII: S0025-5408(07)00203-6; Copyright (c) 2007 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Mild hydrothermal synthesis, crystal structure, thermal behavior, spectroscopic and magnetic properties of the (NH{sub 4})[Fe(AsO{sub 4}){sub 1-x}(PO{sub 4}){sub x}F] (x=0.3, 0.6, 0.8) series. Thermal transformation of (NH{sub 4})[Fe(AsO{sub 4}){sub 0.7}(PO{sub 4}){sub 0.3}F] into the textural porous orthorhombic Fe(AsO{sub 4}){sub 0.7}(PO{sub 4}){sub 0.3}
Fe{sub 2}(AsO{sub 4})F: A new three-dimensional condensed fluoro-arsenate iron(II) compound with antiferromagnetic interactions
Related Subjects
ABSORPTION SPECTROSCOPY
ANTIFERROMAGNETISM
ARSENATES
CALCINATION
CATIONS
COBALT COMPOUNDS
ELECTRON SPIN RESONANCE
INFRARED SPECTRA
IRON COMPOUNDS
MAGNETIC PROPERTIES
MANGANESE COMPOUNDS
MOESSBAUER EFFECT
ORTHORHOMBIC LATTICES
PARAMAGNETISM
SPACE GROUPS
THERMAL GRAVIMETRIC ANALYSIS
X-RAY DIFFRACTION