Production of ultra thin grain oriented silicon steel sheets
Journal Article
·
· IEEE Transactions on Magnetics
- Tohoku Univ., Sendai (Japan). Research Inst. of Electrical Communication
Grain texture and magnetic properties of ultra thin silicon steel sheets were investigated. The sheets were produced using two kinds of starting materials. One was conventional grain oriented silicon steel sheet and the other was hot rolled silicon steel. Ultra thin sheets were obtained by cold rolling with intermediate annealing. By annealing in a high vacuum a recrystallization using surface energy occurred and very sharp (110)[001] texture was obtained in sheets of 5--8 {micro}m thick. The B{sub 8} of the ultra thin silicon steel sheets obtained were over 1.95 T.
- OSTI ID:
- 186963
- Report Number(s):
- CONF-950404-; ISSN 0018-9464; TRN: IM9609%%236
- Journal Information:
- IEEE Transactions on Magnetics, Vol. 31, Issue 6Pt2; Conference: Conference on magnetism and magnetic materials, San Antonio, TX (United States), 18-21 Apr 1995; Other Information: PBD: Nov 1995
- Country of Publication:
- United States
- Language:
- English
Similar Records
Reduction of iron loss in thin grain-oriented silicon steel sheets
Characterization of microstructure, texture and magnetic properties in twin-roll casting high silicon non-oriented electrical steel
Microstructure, texture evolution and magnetic properties of strip-casting non-oriented 6.5 wt.% Si electrical steel doped with cerium
Journal Article
·
Mon Sep 01 00:00:00 EDT 1997
· IEEE Transactions on Magnetics
·
OSTI ID:186963
+1 more
Characterization of microstructure, texture and magnetic properties in twin-roll casting high silicon non-oriented electrical steel
Journal Article
·
Sat Feb 15 00:00:00 EST 2014
· Materials Characterization
·
OSTI ID:186963
+3 more
Microstructure, texture evolution and magnetic properties of strip-casting non-oriented 6.5 wt.% Si electrical steel doped with cerium
Journal Article
·
Fri May 15 00:00:00 EDT 2015
· Materials Characterization
·
OSTI ID:186963
+1 more