Partitioning of gadolinium and its induced phase separation in sodium-aluminoborosilicate glasses
Journal Article
·
· Journal of Non-Crystalline Solids
OSTI ID:15011136
Phase separation in sodium-aluminoborosilicate glasses was systematically studied as a function of Gd2O3 concentration with transmission electronic microscopy (TEM), energy dispersive X-ray spectroscopy (EDS) and electronic energy loss spectroscopy (EELS) methods. Dissolving Gd2O3 in sodium-aluminoborosilicate glasses causes phase separation when the Na2O/(Na2O + Al2O3) is between 0.4 and 0.6. Samples of these glasses were examined in the TEM with ELFS. The results are reported.
- Research Organization:
- Pacific Northwest National Lab., Richland, WA (US)
- Sponsoring Organization:
- US Department of Energy (US)
- DOE Contract Number:
- AC05-76RL01830
- OSTI ID:
- 15011136
- Report Number(s):
- PNNL-SA-42078; JNCSBJ; NN6001020; TRN: US0500745
- Journal Information:
- Journal of Non-Crystalline Solids, Vol. 333, Issue 1; Other Information: PBD: 1 Jan 2003; ISSN 0022-3093
- Country of Publication:
- United States
- Language:
- English
Similar Records
Extended electron energy loss fine structure simulation of the local boron environment in sodium aluminoborosilicate glasses containing gadolinium
Extended electron energy loss fine structure simulation of the local boron environment in sodium aluminoborosilicate glasses containing gadolinium
Monte Carlo Simulations of the Corrosion of Aluminoborosilicate Glasses
Journal Article
·
Mon Dec 01 00:00:00 EST 2003
· Journal of Non-crystalline Solids
·
OSTI ID:15011136
+1 more
Extended electron energy loss fine structure simulation of the local boron environment in sodium aluminoborosilicate glasses containing gadolinium
Journal Article
·
Wed Oct 15 00:00:00 EDT 2003
· Journal of Non-crystalline Solids
·
OSTI ID:15011136
+1 more
Monte Carlo Simulations of the Corrosion of Aluminoborosilicate Glasses
Journal Article
·
Tue Jan 01 00:00:00 EST 2013
· Journal of Non-Crystalline Solids
·
OSTI ID:15011136