Vertical zone melt growth of GaAs
- Naval Research Laboratory, Washington, DC (United States)
A Vertical Zone Melt (VZM) technique has been applied to the single crystal growth of GaAs. A pyrolytic boron nitride crucible and a (100) oriented seed were used along with liquid encapsulation by boric oxide. In the case of GaAs, the ampoule was pressurized with either argon or argensic vapor from elemental arsenic at pressures ranging from 1 to 2 atmospheres. A molten zone length of 22 mm gave a growth interface which is nearly flat and resulted in routine single crystal growth. Temperature gradients of 4{degrees}C/cm. and 9{degrees}C/cm. have produced dislocation densities of <1000/cm{sup 2} and 2000-5000/cm{sup 2} respectively for 34 mm diameter crystals of GaAs. Post growth cooling rates for GaAs have been 35, 160 and 500{degrees}C/hr. The cooling rate has been found to affect the number and size of arsenic precipitates and the EL2 concentration in the GaAs crystal. The effects of these and other growth parameters on the crystalline perfection and electrical properties of the crystals will be discussed.
- OSTI ID:
- 141102
- Report Number(s):
- CONF-930304-; TRN: 93:003688-0777
- Resource Relation:
- Conference: 205. American Chemical Society national meeting, Denver, CO (United States), 28 Mar - 2 Apr 1993; Other Information: PBD: 1993; Related Information: Is Part Of 205th ACS national meeting; PB: 1951 p.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Development and characterization of zone melt growth GaAs for gamma-ray detectors
Characterization of as-grown and annealed GaAs: Structural defects and electrical properties