Silica-based waste form for immobilization of iodine from reprocessing plant off-gas streams
A high selectivity and sorption capacity for iodine and a feasible consolidation to a durable SiO2-based waste form makes silver-functionalized silica aerogel (Ag0-aerogel) an attractive choice for the removal and sequestration of iodine compounds from the off-gas of a nuclear fuel reprocessing plant. Hot uniaxial pressing of iodine-loaded Ag0-aerogel (20.2 mass% iodine) at 1200°C for 30 min under 29 MPa pressure provided a partially sintered product with residual open porosity of 16.9% that retained ~93% of sorbed iodine. Highly iodine-loaded Ag0-aerogel was successfully consolidated by hot isostatic pressing at 1200°C with a 30-min hold and under 207 MPa. The fully densified waste form had a bulk density of 3.3 g/cm3 and contained ~39 mass% iodine. The iodine was retained in the form of nano- and micro-particles of AgI that were uniformly distributed inside and along boundaries of fused silica grains.
- Research Organization:
- Pacific Northwest National Lab. (PNNL), Richland, WA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC05-76RL01830
- OSTI ID:
- 1340833
- Report Number(s):
- PNNL-SA-117831; AF5805010
- Journal Information:
- Journal of Nuclear Materials, Vol. 476; ISSN 0022-3115
- Publisher:
- Elsevier
- Country of Publication:
- United States
- Language:
- English
Similar Records
Expanded Analysis of Hot Isostatic Pressed Iodine-Loaded Silver-Exchanged Mordenite
Densification and Immobilization of AgI-Containing Iodine Waste Forms Using Spark Plasma Sintering