The porosity of sol-gel silica thin films for optrode applications
Conference
·
OSTI ID:126239
- Oklahoma State Univ., OK (United States)
Porous silica thin films produced by sol-gel processing are being considered for use in optical sensor (optrode) applications. In this study, thin films were produced by dip-coating onto glass slides. The porosity was then measured indirectly, by determining the amount of methylene blue adsorption on each slide. Using this technique, it has been determined that the {open_quotes}two-step{close_quotes} sol-gel process provides a greater surface area than the acid-catalyzed process. With the two-step process, increasing the amount of solvent (ethanol) and decreasing the rate of slide withdrawal from the sol provided increased surface area when normalized to the mass of the deposit.
- OSTI ID:
- 126239
- Report Number(s):
- CONF-950402-; TRN: 95:006086-0219
- Resource Relation:
- Conference: 209. American Chemical Society (ACS) national meeting, Anaheim, CA (United States), 2-6 Apr 1995; Other Information: PBD: 1995; Related Information: Is Part Of 209th ACS national meeting; PB: 2088 p.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Nanocrystalline sol-gel TiO{sub 2}-SnO{sub 2} coatings: Preparation, characterization and photo-catalytic performance
Physico-chemical aspects of sol-gel thin film deposition: Control of film porosity
Sol-gel processing of silica
Journal Article
·
Wed Feb 15 00:00:00 EST 2012
· Materials Research Bulletin
·
OSTI ID:126239
Physico-chemical aspects of sol-gel thin film deposition: Control of film porosity
Conference
·
Fri Dec 01 00:00:00 EST 1995
·
OSTI ID:126239
Sol-gel processing of silica
Conference
·
Sat Dec 31 00:00:00 EST 1994
·
OSTI ID:126239