Title: Epitaxial growth of iridate pyrochlore Nd2Ir2O7 films

Epitaxial films of the pyrochlore Nd2Ir2O7 have been grown on (111)-oriented yttria-stabilized zirconia (YSZ) substrates by off-axis sputtering followed by post-growth annealing. X-ray diffraction (XRD) results demonstrate phase-pure epitaxial growth of the pyrochlore films on YSZ. Scanning transmission electron microscopy (STEM) investigation of an Nd2Ir2O7 film with a short post-annealing provides insight into the mechanism for crystallization of Nd2Ir2O7 during the post-annealing process. STEM images reveal clear pyrochlore ordering of Nd and Ir in the films. As a result, the epitaxial relationship between the YSZ and Nd2Ir2O7 is observed clearly while some interfacial regions show a thin region with polycrystalline Ir nanocrystals.
 [1] ;  [1] ;  [1] ;  [1] ;  [1] ;  [1] ;  [1] ;  [1]
  1. The Ohio State Univ., Columbus, OH (United States)
Publication Date:
OSTI Identifier:
Grant/Contract Number:
Accepted Manuscript
Journal Name:
Scientific Reports
Additional Journal Information:
Journal Volume: 6; Journal ID: ISSN 2045-2322
Nature Publishing Group
Research Org:
Argonne National Lab. (ANL), Argonne, IL (United States)
Sponsoring Org:
USDOE Office of Science (SC), Basic Energy Sciences (BES) (SC-22)
Country of Publication:
United States
75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND SUPERFLUIDITY; solid-phase synthesis; surfaces, interfaces and thin films