Title: Non-wetting surface-driven high-aspect-ratio crystalline grain growth for efficient hybrid perovskite solar cells

Large-aspect-ratio grains are needed in polycrystalline thin-film solar cells for reduced charge recombination at grain boundaries; however, the grain size in organolead trihalide perovskite (OTP) films is generally limited by the film thickness. Here we report the growth of OTP grains with high average aspect ratio of 2.3–7.9 on a wide range of non-wetting hole transport layers (HTLs), which increase nucleus spacing by suppressing heterogeneous nucleation and facilitate grain boundary migration in grain growth by imposing less drag force. The reduced grain boundary area and improved crystallinity dramatically reduce the charge recombination in OTP thin films to the level in OTP single crystals. Combining the high work function of several HTLs, a high stabilized device efficiency of 18.3% in low-temperature-processed planar-heterojunction OTP devices under 1 sun illumination is achieved. As a result, this simple method in enhancing OTP morphology paves the way for its application in other optoelectronic devices for enhanced performance.
 [1] ;  [1] ;  [1] ;  [1] ;  [1] ;  [1]
  1. Univ. of Nebraska, Lincoln, NE (United States)
Publication Date:
OSTI Identifier:
Grant/Contract Number:
Accepted Manuscript
Journal Name:
Nature Communications
Additional Journal Information:
Journal Volume: 6; Journal Issue: 2; Journal ID: ISSN 2041-1723
Nature Publishing Group
Research Org:
Univ. of Nebraska, Lincoln, NE (United States)
Sponsoring Org:
Country of Publication:
United States
physical sciences; applied physics; materials science