Correlation between in-field critical currents in Zr-added (Gd, Y)Ba2Cu3Ox superconducting tapes at 30 and 77 K
Critical current (I-c) values of 1384 Lambda/12 mm, corresponding to a critical current density of 12.47 MA cm(-2) and a pinning force of 374 GN m(-3), have been achieved at 30 K, 3 T in the orientation of field parallel to the c axis (B parallel to c) in (Gd, Y)BaCuO tapes with 15 mol% Zr addition made by metal organic chemical vapor deposition (MOCVD). These tapes show pinning force levels as high as 453 GN m(-3) at 30 K. An analysis of the properties of 24-28 (Gd, Y)BaCuO tapes with 15 mol% Zr addition showed a lack of correlation between their critical currents at 30 K, 3 T (B parallel to c) and I-c values both at 77 K, zero field and at 77 K, 1 T (B parallel to c). However, a strong correlation was found between the critical currents at 30 K, 3 T and at 77 K, 3 T (B parallel to c). It has also been discovered that the minimum critical current (I-c, (min)) value at 77 K, 3 T has no influence on the I-c,I- (min) value at 30 K, 3 T, and it in turn depends on the ratio of the I-c values in the orientations of field parallel and perpendicular to the c axis at 77 K, 3 T.
- Sponsoring Organization:
- USDOE Advanced Research Projects Agency - Energy (ARPA-E)
- DOE Contract Number:
- DE-AR0000196
- OSTI ID:
- 1211370
- Journal Information:
- Superconductor Science and Technology, Vol. 27, Issue 5; ISSN 0953-2048
- Country of Publication:
- United States
- Language:
- English
Similar Records
Enhanced critical currents in (Gd,Y)Ba2Cu3Ox superconducting tapes with high levels of Zr addition
The low-temperature, high-magnetic-field critical current characteristics of Zr-added (Gd, Y)Ba2Cu3Ox superconducting tapes