Title: (U) Analysis of shock-initiated PBX-9501 through porous CeO2

The attenuation properties of an impact initiated PBX-9501 explosive through several thicknesses of CeO2 powder is investigated. The CeO2 is at an initial porous density of 4.0 g/cm3 , roughly 55 % of theoretical maximum density. Measurements of the input (into the powder) and propagated (through the powder) wave profiles are measured using optical velocimetry. Results show a reduction of the average wave speed, CX, and peak steady-state material velocity, uP , with increasing powder thickness from 1.5 - 5.0 mm.
Authors:
 [1] ;  [1] ;  [1]
  1. Los Alamos National Lab. (LANL), Los Alamos, NM (United States)
Publication Date:
OSTI Identifier:
1210219
Report Number(s):
LA-UR--15-25788
DOE Contract Number:
AC52-06NA25396
Resource Type:
Technical Report
Research Org:
Los Alamos National Lab. (LANL), Los Alamos, NM (United States)
Sponsoring Org:
USDOE
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE PBX-9501; cerium dioxide; powder