Title: Radiation damage in cubic ZrO2 and yttria-stabilized zirconia from molecular dynamics simulations

Here, we perform molecular dynamics simulation on cubic ZrO2 and yttria-stabilized zirconia (YSZ) to elucidate defect cluster formation resulting from radiation damage, and evaluate the impact of Y-dopants. Interstitial clusters composed of split-interstitial building blocks, i.e., Zr-Zr or Y-Zr are formed. Moreover, oxygen vacancies control cation defect migration; in their presence, Zr interstitials aggregate to form split-interstitials whereas in their absence Zr interstitials remain immobile, as isolated single-interstitials. Y-doping prevents interstitial cluster formation due to sequestration of oxygen vacancies.
 [1] ;  [2] ;  [2]
  1. Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
  2. Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Univ. of Tennessee, Knoxville, TN (United States)
Publication Date:
OSTI Identifier:
Grant/Contract Number:
AC05-00OR22725; AC02-05CH11231
Accepted Manuscript
Journal Name:
Scripta Materialia
Additional Journal Information:
Journal Volume: 98; Journal Issue: C; Journal ID: ISSN 1359-6462
Research Org:
Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
Sponsoring Org:
USDOE Office of Science (SC)
Country of Publication:
United States
36 MATERIALS SCIENCE; Radiation Effects; Zirconia; Molecular Dynamics; Defect Cluster