Title: Ultra-High Performance, High-Temperature Superconducting Wires via Cost-effective, Scalable, Co-evaporation Process

Long-length, high-temperature superconducting (HTS) wires capable of carrying high critical current, Ic, are required for a wide range of applications. Here, we report extremely high performance HTS wires based on 5 m thick SmBa2Cu3O7- (SmBCO) single layer films on textured metallic templates. SmBCO layer wires over 20 meters long were deposited by a cost-effective, scalable co-evaporation process using a batch-type drum in a dual chamber. All deposition parameters influencing the composition, phase, and texture of the films were optimized via a unique combinatorial method that is broadly applicable for co-evaporation of other promising complex materials containing several cations. Thick SmBCO layers deposited under optimized conditions exhibit excellent cube-on-cube epitaxy. Such excellent structural epitaxy over the entire thickness results in exceptionally high Ic performance, with average Ic over 1000 A/cm for the entire 22 meter long wire and maximum Ic over 1,500 A/cm for a short 12 cm long tape. The Ic values reported in this work are the highest values ever reported from any lengths of cuprate-based HTS wire or conductor.
 [1] ;  [1] ;  [1] ;  [1] ;  [1] ;  [2] ;  [3] ;  [2] ;  [4] ;  [4]
  1. Korea Electrotechnology Research Institute
  2. University of Wollongong, Australia
  3. Pohang University of Science and Technology (POSTECH), Pohang, Republic of Korea
  4. ORNL
Publication Date:
OSTI Identifier:
DOE Contract Number:
Resource Type:
Journal Article
Resource Relation:
Journal Name: Scientific Reports; Journal Volume: 4; Journal Issue: 4744
Research Org:
Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
Sponsoring Org:
OE USDOE - Office of Electric Transmission and Distribution
Country of Publication:
United States