UCSB ATR-NSUF Irradiation DMC Sample Inspection Report
- Los Alamos National Lab. (LANL), Los Alamos, NM (United States)
A variety of tensile samples of Ferritic and Oxide Dispersion Strengthened (ODS or nanoferritic) steels were placed the ATR reactor over 2 Years achieving doses of roughly 4-6 dpa at temperatures of roughly 290°C. After irradiation, samples were shipped from the MFC hot cells at Idaho National Laboratory (INL) to the Wing 9 hot cells in the CMR facility at Los Alamos National Laboratory. Samples were cleaned to removed alpha contamination from the MFC hot cells, and then, as needed removed from their irradiation containers, sorted and inspected. This report will summarize the inspection of the Disc Multipurpose Coupon (DMC) inspection from packet 7-1.
- Research Organization:
- Los Alamos National Laboratory (LANL), Los Alamos, NM (United States)
- Sponsoring Organization:
- USDOE National Nuclear Security Administration (NNSA)
- DOE Contract Number:
- AC52-06NA25396
- OSTI ID:
- 1170627
- Report Number(s):
- LA-UR-15-20825
- Country of Publication:
- United States
- Language:
- English
Similar Records
High Temperature Mechanical Properties, Fractography and Synchrotron Studies of ATF clad materials from the UCSB-NSUF Irradiations.
Post Irradiation Examination of Fast Neutron Irradiated 14YWT Tubes at Nuclear Science User Facilities
AGC-2 Disassembly Report
Technical Report
·
Mon Feb 23 00:00:00 EST 2015
·
OSTI ID:1170627
+2 more
Post Irradiation Examination of Fast Neutron Irradiated 14YWT Tubes at Nuclear Science User Facilities
Journal Article
·
Sat Jul 01 00:00:00 EDT 2017
· Transactions of the American Nuclear Society
·
OSTI ID:1170627
+4 more
AGC-2 Disassembly Report
Technical Report
·
Thu May 01 00:00:00 EDT 2014
·
OSTI ID:1170627