Microstructural Development and Mechanical Properties for Reactive Air Brazing of ZTA to Ni Alloys using Ag-CuO Braze Alloys
Reactive air brazing (RAB) is a potential joining technique to join metal alloys to ceramics for a variety of applications. In the current study, nickel (Ni) alloys were heat treated to form an oxide layer prior to RAB joining to zirconia toughened alumina (ZTA). The Ni alloys evaluated were Nicrofer 6025 HT, Inconel 600, Inconel 693, Haynes 214 and Inconel 601. The ZTA studied had compositions of 0 to 15 wt% zirconia and 0 to 14 wt% glass. Four point-bend tests were performed to evaluate the joint strength of ZTA/ZTA and ZTA/nickel alloys brazed with Ag-2wt% CuO braze alloys. It was determined that the joint strength is not a function of the ZTA composition, but that the strength is a strong function of the chemistry and microstructure of the oxide layer formed on the nickel alloy. It was determined that an increase in the aluminum content of the Ni alloy resulted in an increase of the thickness of alumina in the oxide layer and was directly proportional to the bond strength with the exception of Inconel 601 which exhibited relatively high joint strengths even though it had a relatively low aluminum content.
- Research Organization:
- Pacific Northwest National Lab. (PNNL), Richland, WA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC05-76RL01830
- OSTI ID:
- 1170090
- Report Number(s):
- PNNL-SA-102575; AA6010000
- Journal Information:
- Advanced Engineering Materials, 16(12):1448-1455, Journal Name: Advanced Engineering Materials, 16(12):1448-1455
- Country of Publication:
- United States
- Language:
- English
Similar Records
Development of Brazing Technology for Use in High- Temperature Gas Separation Equipment
Mechanical properties and dual atmosphere tolerance of Ag-Al based braze