Title: The Role of Fullerene Mixing Behavior in the Performance of Organic Rhotovoltaics: PCBM in Low-Bandgap Polymers.

This manuscript reports the mixing behavior, interdiffusion, and depth profile of 1-[3-(methoxycarbonyl)propyl]-1-phenyl-[6,6]C 61 (PCBM):low-bandgap (LBG) polymer thin fi lms that are formed by thermally annealing initial bilayers. The extent of mixing of PCBM is higher in polymers that include the 2,1,3-benzothiadiazole (BT) unit than in polymers that incorporate the 2,1,3-benzooxadiazole (BO) unit. This difference is ascribed to the enhanced mixing behavior of PCBM with the benzothiadiazole functionality than with benzooxadiazole functionality, which is attributed to preferred intermolecular interactions. The increased polymer/fullerene mixing is found to be crucial for optimal device performance. A decrease of polymer/fullerene mixing reduces the donor/acceptor interface, which lowers the probability of exciton dissociation and charge generation. Moreover, low PCBM mixing provides limited pathways for electron transport out of a miscible region, due to long distances between adjacent PCBM in such a miscible phase. This inhibits electron transport and increases the recombination of free charge carriers, resulting in a decrease in short circuit current and device performance. These results further exemplify the importance of the thermodynamic mixing behavior of the polymer:fullerene pair in designing next-generation conjugated polymers for organic photovoltaic (OPV) applications, as this controls the fi nal morphology of the OPV active layer.
 [1] ;  [2] ;  [1] ;  [3] ;  [3] ;  [1]
  1. ORNL
  2. Konarka Technologies
  3. University of California, Santa Barbara
Publication Date:
OSTI Identifier:
DOE Contract Number:
Resource Type:
Journal Article
Resource Relation:
Journal Name: Advanced Functional Materials; Journal Volume: 24; Journal Issue: 1
Research Org:
Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States). Spallation Neutron Source (SNS)
Sponsoring Org:
USDOE Office of Science (SC)
Country of Publication:
United States