Title: In Situ Foaming of Porous (La 0.6 Sr 0.4 ) 0.98 (Co 0.2 Fe 0.8 ) O 3-δ (LSCF) Cathodes for Solid Oxide Fuel Cell Applications

A binder system containing polyurethane precursors was used to in situ foam (direct foam) a (La{sub 0.6}Sr{sub 0.4}){sub 0.98} (Co{sub 0.2} Fe{sub 0.8}) O{sub 3-{ delta}} (LSCF) composition for solid oxide fuel cell (SOFC) cathode applications. The relation between in situ foaming parameters on the final microstructure and electrochemical properties was characterized by microscopy and electrochemical impedance spectroscopy (EIS), respectively. The optimal porous cathode architecture was formed with a 70 vol% solids loading within a polymer precursor composition with a volume ratio of 8:4:1 (isocyanate: PEG: surfactant) in a terpineol-based ink vehicle. The resultant microstructure displayed a broad pore size distribution with highly elongated pore structure.
Authors:
 [1] ;  [1] ;  [2] ;  [3]
  1. US DOE-National Energy Technology Laboratory, 3610 Collins Ferry Road P.O.Box.880 Morgantown West Virginia 26507; Department of Mechanical and Aerospace Engineering, West Virginia University, Morgantown West Virginia 26506
  2. Department of Mechanical and Aerospace Engineering, West Virginia University, Morgantown West Virginia 26506
  3. US DOE-National Energy Technology Laboratory, 3610 Collins Ferry Road P.O.Box.880 Morgantown West Virginia 26507
Publication Date:
OSTI Identifier:
1128518
DOE Contract Number:
FE0004000
Resource Type:
Journal Article
Resource Relation:
Journal Name: International Journal of Applied Ceramic Technology; Journal Volume: 12; Journal Issue: 1
Publisher:
Wiley
Research Org:
National Energy Technology Laboratory - In-house Research; National Energy Technology Laboratory (NETL), Pittsburgh, PA, and Morgantown, WV (United States)
Sponsoring Org:
USDOE
Country of Publication:
United States
Language:
English
Subject:
30 DIRECT ENERGY CONVERSION