Title: In Situ TEM Concurrent and Successive Au Self-Ion Irradiation and He Implantation

The development of advanced computational methods used for predicting performance lifetimes of materials exposed to harsh radiation environments are highly dependent on fundamental understanding of solid-radiation interactions that occur within metal components. In this work, we present successive and concurrent in situ TEM dual-beam self-ion irradiation of 2.8MeV Au4+ and implantation of 10 keV He1+, utilizing a new facility at Sandia National Laboratories. These experiments, using a model material system, provide direct real-time insight into initial interactions of displacement damage and fission products that simulate damage from neutron exposure. In successive irradiation, extensive dislocation loop and stacking fault tetrahedra damage was formed and could be associated with individual ion strikes, but no evidence of cavity formation was observed. In contrast, concurrent irradiation to the same dose resulted in the onset of cavity formation at the site of a heavy-ion strike. This direct real-time observation provides insight into the complex interplay between the helium and vacancy dynamics.
 [1] ;  [2] ;  [1]
  1. University of California, Berkeley & LBNL
  2. Sandia National Laboratories (SNL)
Publication Date:
OSTI Identifier:
DOE Contract Number:
Resource Type:
Journal Article
Resource Relation:
Journal Name: Materials Transactions; Journal Volume: 55; Journal Issue: 3
Japan Institute of Metals and Materials
Research Org:
Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
Sponsoring Org:
USDOE Office of Science (SC)
Country of Publication:
United States