Title: Final Report - Effects of High Spinel and Chromium Oxide Crystal Contents on Simulated HLW Vitrification in DM100 Melter Tests, VSL-09R1520-1, Rev. 0, dated 6/22/09

The principal objective of the work was to evaluate the effects of spinel and chromium oxide particles on WTP HLW melter operations and potential impacts on melter life. This was accomplished through a combination of crucible-scale tests, settling and rheological tests, and tests on the DM100 melter system. Crucible testing was designed to develop and identify HLW glass compositions with high waste loadings that exhibit formation of crystalline spinel and/or chromium oxide phases up to relatively high crystal contents (i.e., > 1 vol%). Characterization of crystal settling and the effects on melt rheology was performed on the HLW glass formulations. Appropriate candidate HLW glass formulations were selected, based on characterization results, to support subsequent melter tests. In the present work, crucible melts were formulated that exhibit up to about 4.4 vol% crystallization.
Authors:
; ; ; ; ;
Publication Date:
OSTI Identifier:
1105976
Report Number(s):
ORP-56294 Rev 0
VSL-09R1520-1 Rev 0
DOE Contract Number:
DE-AC27-08RV14800
Resource Type:
Technical Report
Research Org:
HNF (Hanford Site (HNF), Richland, WA (United States))
Sponsoring Org:
USDOE Office of Environmental Management (EM)
Contributing Orgs:
Department of Energy - Office of River Protection, The Catholic University of America
Country of Publication:
United States
Language:
English
Subject:
12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE WASTES FROM NUCLEAR FACILITIES