Title: Alpha phase precipitation from phase-separated beta phase in a model Ti-Mo-Al alloy studied by direct coupling of transmission electron microscopy and atom probe tomography

The benefit of direct coupling of APT with TEM dark field imaging to investigate early stages of phase transformation in multicomponent alloys is demonstrated by analyzing alpha phase precipitated in a model Ti-10 at% Mo-10 at% Al alloy during annealing at 400oC. Through such a direct coupling approach a thermodynamically unexpected solute partitioning trend between beta matrix and alpha precipitate is observed in the early stages of precipitation, which is explained based on possible nucleation of alpha phase in the Ti rich (Mo and Al depleted regions) created as a result of phase separation in beta matrix. On further higher temperature annealing at 600oC for 1 hour, the alpha precipitates were shown to grow and get enriched in Al and further depleted in Mo reaching the thermodynamic equilibrium.
; ;
Publication Date:
OSTI Identifier:
Report Number(s):
DOE Contract Number:
Resource Type:
Journal Article
Resource Relation:
Journal Name: Scripta Materialia, 69(7):513-516
Research Org:
Pacific Northwest National Laboratory (PNNL), Richland, WA (US), Environmental Molecular Sciences Laboratory (EMSL)
Sponsoring Org:
Country of Publication:
United States
Environmental Molecular Sciences Laboratory