Hard X-ray Fluorescence Measurements of Heteroepitaxial Solid Oxide Fuel Cell Cathode Materials
Commonly, SOFCs are operated at high temperatures (above 800°C). At these temperatures expensive housing is needed to contain an operating stack as well as coatings to contain the oxidation of the metallic interconnects. Lowering the temperature of an operating device would allow for more conventional materials to be used, thus lowering overall cost. Understanding the surface chemical states of cations in the surface of the SOFC cathode is vital to designing a system that will perform well at lower temperatures. The samples studied were grown by pulsed laser deposition (PLD) at the Environmental Molecular Sciences Laboratory (EMSL) at Pacific Northwest National Laboratory (PNNL). 20% strontium doped lanthanum manganite (LSM-20) was grown on YSZ and NGO (neodymium gallate). The films on YSZ have a fiber texture. LSM-20 on NGO is heteroepitaxial. Lanthanum strontium cobalt ferrite (LSCF-6428) films were grown on LAO and YSZ with a GDC barrier layer. Total X-ray Reflection Fluorescence (TXRF) was used to depth profile the samples. In a typical experiment, the angle of the incident beam is varied though the critical angle. Below the critical angle, the x-ray decays as an evanescent wave and will only penetrate the top few nanometers. TXRF experiments done on LSM films have suggested strontium segregates to the surface and form strontium enriched nanoparticles (1). It should be pointed out that past studies have focused on 30% strontium A-site doping, but this project uses 20% strontium doped lanthanum manganite. XANES and EXAFS data were taken as a function of incoming angle to probe composition as a function of depth. XANES spectra can be difficult to analyze fully. For other materials density functional theory calculations compared to near edge measurements have been a good way to understand the 3d valence electrons (2).
- Research Organization:
- Pacific Northwest National Lab. (PNNL), Richland, WA (United States). Environmental Molecular Sciences Lab. (EMSL)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC05-76RL01830
- OSTI ID:
- 1064578
- Report Number(s):
- PNNL-SA-84456; 30429; KP1704020
- Journal Information:
- ECS Transactions, 41(11):19-24, Journal Name: ECS Transactions, 41(11):19-24
- Country of Publication:
- United States
- Language:
- English
Similar Records
SURFACE SEGREGATION STUDIES OF SOFC CATHODES: COMBINING SOFT X-RAYS AND ELECTROCHEMICAL IMPEDENCE SPECTROSCOPY
An intermediate-temperature solid oxide fuel cell with electrospun nanofiber cathode