Pore structure development in oxidized IG-110 nuclear graphite
- ORNL
- Tsinghua University
The oxidation-induced porosity development in nuclear graphite has great effect on its mechanical behavior, thus it is very important to understand the pore structure development of nuclear graphite during oxidation. This paper reports on the oxidation kinetics of grade IG-110 nuclear graphite and the porosity development in oxidized samples. The distribution of the oxidized layer in IG-110 specimens oxidized at 600-750 C was studied using optical microscopy coupled with automated image analysis technique, and the mechanism of porosity development was determined. The thickness of oxidized layer decreased with the oxidation temperature but was independent of the weight loss level. Oxidation caused consumption of graphite structure and development of porosity, which was initiated from the binder phase. Statistical analysis indicated that generation and growth of pores was dominant at low temperatures, while merging and collapse of pores was the main effect at high temperatures. Compared with medium-grained PCEA graphite, the fine-grained IG-110 graphite demonstrates deeper penetration of the oxidant because of its higher pore density and lager porosity.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- Work for Others (WFO)
- DOE Contract Number:
- DE-AC05-00OR22725
- OSTI ID:
- 1047626
- Journal Information:
- Journal of Nuclear Materials, Vol. 430, Issue 1-3; ISSN 0022-3115
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of Air Oxidation on Pore Structure Development and Mechanical Properties of Nuclear Graphite
Water vapor oxidation behaviors of nuclear graphite IG-110 for a postulated accident scenario in high temperature gas-cooled reactors