Strong Pinning in Thick YBa2Cu3O7 Layers Mediated by Catalysis of a New Long-period Metastable Cuprate Phase
Catalysts are widely utilized to promote reactions in liquid and gaseous phases but are rarely encountered in solid state synthesis. Here we use catalytically active (001) ceria buffers to modify the structure of the epitaxial high temperature superconductor YBa{sub 2}Cu{sub 3}O{sub 7}. The modification is achieved by catalytically-assisted synthesis of a previously unknown metastable phase. The new phase, a long-period (3.5 nm) perovskite, intercalates into the YBa{sub 2}Cu{sub 3}O{sub 7} matrix without negatively affecting the critical temperature of the film. Analysis of electron microscopy and synchrotron x-ray diffraction data allow identification of the phase as a long-period YBa{sub 2}Cu{sub 3}O{sub 7} derivative formed through short-range cation displacement. The 0.8 {micro}m thick films exhibit strong enhancement of the critical current density, reaching a maximum of 4.2 MA/cm{sup 2} at 77 K. The result emphasizes the critical role of catalysis for synthesis of novel complex materials.
- Research Organization:
- Brookhaven National Lab. (BNL), Upton, NY (United States)
- Sponsoring Organization:
- USDOE SC OFFICE OF SCIENCE (SC)
- DOE Contract Number:
- DE-AC02-98CH10886
- OSTI ID:
- 1041854
- Report Number(s):
- BNL-97532-2012-JA; JAPIAU; TRN: US201212%%266
- Journal Information:
- Journal of Applied Physics, Vol. 108, Issue 11; ISSN 0021-8979
- Country of Publication:
- United States
- Language:
- English
Similar Records
Substrate Surface Decoration With CeO2 Nanoparticles: An Effective Method for Improving Flux Pinning in YBa2Cu3O7 Films
Enhanced Flux Pinning and Critical Currents in YBa2Cu3O7-delta Films by Nanoparticle Surface Decoration: Extension to Coated Conductor Templates
Related Subjects
BARIUM COMPOUNDS
BUFFERS
CATALYSIS
CATALYSTS
CATIONS
CERIUM COMPOUNDS
CLATHRATES
CRITICAL CURRENT
CRITICAL TEMPERATURE
CUPRATES
ELECTRON MICROSCOPY
MAGNETIC FLUX
MODIFICATIONS
PEROVSKITE
SUPERCONDUCTIVITY
SUPERCONDUCTORS
SYNCHROTRONS
SYNTHESIS
TRANSITION TEMPERATURE
TYPE-II SUPERCONDUCTORS
X-RAY DIFFRACTION
YTTRIUM COMPOUNDS