Dynamic Recovery in Silicate-Apatite Structures Under Irradiation and Implications for Long-Term Immobilization of Actinides
The irradiation responses of Ca{sub 2}La{sub 8}(SiO{sub 4}){sub 6}O{sub 2} and Sr{sub 2}Nd{sub 8}(SiO{sub 4}){sub 6}O{sub 2} with the apatite structure are investigated to predict their long-term behaviour as host phases for immobilization of actinide elements from the nuclear fuel cycle. Different ions and energies are used to study the effects of dose, temperature, atomic displacement rate and ionization rate on irradiation-induced amorphization and recrystallization. The dose for amorphization increases with temperature in two stages, below and above 150 K. In the high temperature stage relevant to actinide immobilization, the increase of amorphization dose with temperature exhibits a strong dependence on the ratio of ionization rate to displacement rate for the different ions. Data analysis using a dynamic model for amorphization reveals that ionization-induced processes, with activation energy of 0.15 {+-} 0.02 eV, dominate dynamic recovery for ions from Ne through Xe. For heavier Au ions or for alpha-recoil nuclei emitted in alpha decay of actinides, ionization becomes less dominant and dynamic recovery is controlled primarily by thermally-driven processes. In post-irradiation annealing studies of amorphous samples, epitaxial thermal recrystallization is observed at 1123 K, and irradiation-enhanced nucleation of nanocrystallites is observed under irradiation with heavier ions. The recrystallization temperature under irradiation decreases with increasing ion mass to a value of {approx} 823 K, which also defines the thermally-driven critical temperature for amorphization under irradiation with heavy ions. Some partial recovery due to alpha particle irradiation at 300 K is observed that suggests a self-healing mechanism in apatite phases containing actinides. Based on the results and dynamic model, the temperature and time dependences of amorphization in silicate-apatite host phases for actinide immobilization are predicted.
- Research Organization:
- Pacific Northwest National Lab. (PNNL), Richland, WA (United States). Environmental Molecular Sciences Lab. (EMSL)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC05-76RL01830
- OSTI ID:
- 1038388
- Journal Information:
- RSC Advances, Vol. 2
- Country of Publication:
- United States
- Language:
- English
Similar Records
Self-radiation damage in actinide host phases of nuclear waste forms. [Ca/sub 2/Nd/sub 8/(SiO/sub 4/)/sub 6/O/sub 2/; Gd/sub 2/Ti/sub 2/O/sub 7/; CaZrTi/sub 2/O/sub 7/]
In situ TEM observation of alpha-particle induced annealing of radiation damage in Durango apatite
Related Subjects
ACTINIDES
ACTIVATION ENERGY
ALPHA DECAY
ALPHA PARTICLES
ANNEALING
APATITES
ATOMIC DISPLACEMENTS
CRITICAL TEMPERATURE
DATA ANALYSIS
HEAVY IONS
IONIZATION
IRRADIATION
NUCLEAR FUELS
NUCLEATION
NUCLEI
RECRYSTALLIZATION
TIME DEPENDENCE
SILICATES
Environmental Molecular Sciences Laboratory