Correlation between superconductivity and structural properties under high pressure of iron pnictide superconductor Ce[subscript 0.6]Y[subscript 0.4]FeAsO[subscript 0.8]F[subscript 0.2]
- IIT-India
We report here the pressure dependence of the electrical resistivity and magnetic susceptibility of polycrystalline Ce{sub 0.6}Y{sub 0.4}FeAsO{sub 0.8}F{sub 0.2} superconductor in the temperature range 4 K to 300 K up to 8 GPa. In-situ high pressure-low temperature x-ray diffraction was performed at 8 K up to 32 GPa using synchrotron x-rays with helium pressure medium. The results show that the applied pressure slightly increases the T{sub c} up to 1 GPa and then it decreases on further pressure increase. The reduction of superconducting transition temperature occurs with a transition to a collapsed tetragonal phase and may be associated with a possible valence change of Ce.
- Research Organization:
- Argonne National Lab. (ANL), Argonne, IL (United States). Advanced Photon Source (APS)
- Sponsoring Organization:
- FOREIGN
- OSTI ID:
- 1035710
- Journal Information:
- Applied Physics Letters, Vol. 100, Issue 5; ISSN 0003-6951
- Country of Publication:
- United States
- Language:
- ENGLISH
Similar Records
Structural phase transitions in EuFe[subscript 2]As[subscript 2] superconductor at low temperatures and high pressures
Synthesis and characterization of La{sub 0.6}Sr{sub 0.4}Fe{sub 0.8}Cu{sub 0.2}O{sub 3−δ} oxide as cathode for Intermediate Temperature Solid Oxide Fuel Cells
Influence of electrospraying parameters on the microstructure of La{sub 0.6}Sr{sub 0.4}Co{sub 0.2}F{sub 0.8}O{sub 3-{delta}} films for SOFCs
Journal Article
·
Tue Sep 20 00:00:00 EDT 2011
· J. Phys. Condens. Matter
·
OSTI ID:1035710
+2 more
Synthesis and characterization of La{sub 0.6}Sr{sub 0.4}Fe{sub 0.8}Cu{sub 0.2}O{sub 3−δ} oxide as cathode for Intermediate Temperature Solid Oxide Fuel Cells
Journal Article
·
Sat Aug 15 00:00:00 EDT 2015
· Journal of Solid State Chemistry
·
OSTI ID:1035710
+5 more
Influence of electrospraying parameters on the microstructure of La{sub 0.6}Sr{sub 0.4}Co{sub 0.2}F{sub 0.8}O{sub 3-{delta}} films for SOFCs
Journal Article
·
Wed Jul 15 00:00:00 EDT 2009
· Journal of Solid State Chemistry
·
OSTI ID:1035710