Elastic and magnetostrictive properties of Tb6Fe1-xCioBi2 (0 < x < 0.375)
- University of Tennessee, Knoxville (UTK)
- ORNL
Elastic moduli and magnetostriction data are reported for polycrystalline Tb{sub 6}Fe{sub 1-x}Co{sub x}Bi{sub 2} (0 {le} x {le} 0.375). The elastic moduli c{sub 11} and c{sub 44} have been measured as a function of temperature (5-300 K) and magnetic field (0-5 T), and reflect the ferromagnetic transition observed in these materials around 250 K. A remarkable elastic softening, which is partially suppressed upon application of a magnetic field, is observed at low temperatures and is believed to be linked to a structural transition that takes place in the Co-doped samples. The soft elastic moduli lead to large magnetostriction below 50 K, reaching a value of 700 ppm at 20 kOe for Tb{sub 6}Fe{sub 0.75}Co{sub 0.25}Bi{sub 2}.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- USDOE Office of Science (SC)
- DOE Contract Number:
- DE-AC05-00OR22725
- OSTI ID:
- 1014240
- Journal Information:
- Journal of Applied Physics, Vol. 109, Issue 7; ISSN 0021-8979
- Country of Publication:
- United States
- Language:
- English
Similar Records
Spin reorientation and magnetoelastic coupling in Tb6Fe1-xCoxBi2 (x = 0, 0.125, 0.25, 0.375) alloy system
Structural and magnetic properties of Tb6Fe1-xCoxBi2 (0 x 0.375) compounds