An Electron Microscopy Investigation of the Transient Stage Oxidation Products in an Fe-22Cr Alloy with Ce and La Additions Exposed to Dry Air at 1073 K (800 °C)
In this study, the effects of Ce (270 ppm) and La (120 ppm) mischmetal additions on the transient oxidation of an Fe-22Cr alloy were investigated. The oxidation process was imaged in situ using a confocal scanning laser microscope. The oxidation microstructures were studied by scanning electron microscopy, energy dispersive X-ray analysis, and transmission electron microscopy with the help of focused ion beam in situ lift-out specimen preparation. The Ce and La, referred to as reactive elements, were found in nonmetallic inclusion particles in the forms of oxides, sulfides, and phosphates. An affected zone formed around rare earth (RE)-containing inclusion particles at the alloy free surface during the transient oxidation. This zone consisted of an internal Cr-oxide formed beneath the particle as well as a thinner external oxide scale on the surface compared with the surroundings. The relation of this microstructure to oxidation kinetics is discussed. With time, the RE elements diffused into the scale from the RE particles on the alloy surface during the high-temperature exposure. A diffusion mechanism is presented to describe these observations.
- Research Organization:
- National Energy Technology Laboratory (NETL), Pittsburgh, PA, Morgantown, WV (United States)
- Sponsoring Organization:
- USDOE Office of Fossil Energy (FE)
- OSTI ID:
- 1011353
- Report Number(s):
- NETL-TPR-3171; TRN: US201109%%709
- Journal Information:
- Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science, Vol. 42, Issue 1; ISSN 1073-5623
- Publisher:
- ASM International
- Country of Publication:
- United States
- Language:
- English
Similar Records
On the Relation Between Oxide Ridge Evolution and Alloy Surface Grain Boundary Disorientation in Fe–22 wt % Cr Alloys
As-cast microstructures in U-Pu-Zr alloy fuel pins with 5-8 wt.% minor actinides and 0-1.5 wt% rare-earth elements