Effect of Aging on the NOx Storage and Regeneration Characteristics of Fully Formulated Lean NOx Trap Catalysts
- University of Kentucky
- ORNL
In order to elucidate the effect of washcoat composition on lean NO{sub x} trap (LNT) aging characteristics, fully formulated monolithic LNT catalysts containing varying amounts of Pt, Rh and BaO were subjected to accelerated aging on a bench reactor. Subsequent catalyst evaluation revealed that in all cases aging resulted in deterioration of the NO{sub x} conversion as a consequence of impaired NO{sub x} storage and NO{sub x} reduction functions, while increased selectivity to NH{sub 3} was observed in the temperature range 250--450 C. Elemental analysis, H{sub 2} chemisorption and TEM data revealed two main changes which account for the degradation in LNT performance. First, residual sulfur in the catalysts, associated with the Ba phase, decreased catalyst NO{sub x} storage capacity. Second, sintering of the precious metals in the washcoat occurred, resulting in decreased contact between the Pt and Ba, and hence in less efficient NO{sub x} spillover from Pt to Ba during NO{sub x} adsorption, as well as decreased rates of reductant spillover from Pt to Ba and reverse NO{sub x} spillover during catalyst regeneration. For the aged catalysts, halving the Pt loading from 100 to 50 g/ft{sup 3} was found to result in a significant decrease in overall NO{sub x} conversion, while for catalysts with the same 100 g/ft{sup 3} Pt loading, increasing the relative amount of Pt on the NO{sub x} storage components (BaO and La-stabilized CeO{sub 2}), as opposed to an Al{sub 2}O{sub 3} support material (where it was co-located with Rh), was found to be beneficial. The effect of Rh loading on aged catalyst performance was found to be marginal within the range studied (10--20 g/ft{sup 3}), as was the effect of BaO loading in the range 30--45 g/L.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States). Fuels, Engines and Emissions Research Center (FEERC); Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States). National Transportation Research Center (NTRC)
- Sponsoring Organization:
- Work for Others (WFO); USDOE
- DOE Contract Number:
- DE-AC05-00OR22725
- OSTI ID:
- 1010998
- Journal Information:
- Applied Catalysis B, Vol. 103, Issue 3-4; ISSN 0926-3373
- Country of Publication:
- United States
- Language:
- English
Similar Records
Nature and spatial distribution of sulfur species in a sulfated barium-based commercial lean NOx trap catalyst
EFFECT OF ENGINE-BASED THERMAL AGING ON SURFACE MORPHOLOGY AND PERFORMANCE OF LEAN NOX TRAPS