Mechanical characterization of 304L-VAR stainless steel in tension with a full coverage of low, intermediate, and high strain rates
Abstract
A 304L-VAR stainless steel is mechanically characterized in tension over a full range of strain rates from low, intermediate, to high using a variety of apparatuses. While low- and high-strain-rate tests are conducted with a conventional Instron and a Kolsky tension bar, the tensile tests at intermediate strain rates are conducted with a fast MTS and a Drop-Hopkinson bar. The fast MTS used in this study is able to obtain reliable tensile response at the strain rates up to 150 s-1, whereas the lower limit for the Drop-Hopkinson bar is 100 s-1. Combining the fast MTS and the Drop-Hopkinson bar closes the gap within the intermediate strain rate regime. Using these four apparatuses, the tensile stress-strain curves of the 304L-VAR stainless steel are obtained at strain rates on each order of magnitude ranging from 0.0001 to 2580 s-1. All tensile stress-strain curves exhibit linear elasticity followed by significant work hardening prior to necking. After necking occurrs, the specimen load decreases, and the deformation becomes highly localized until fracture. The tensile stress-strain response of the 304L-VAR stainless steel exhibits strain rate dependence. The flow stress increases with increasing strain rate and is described with a power law. The strain-rate sensitivity ismore »
- Authors:
-
- Sandia National Laboratories (SNL), Albuquerque, NM, and Livermore, CA (United States)
- Publication Date:
- Research Org.:
- Sandia National Lab. (SNL-CA), Livermore, CA (United States); Sandia National Lab. (SNL-NM), Albuquerque, NM (United States)
- Sponsoring Org.:
- USDOE National Nuclear Security Administration (NNSA)
- OSTI Identifier:
- 1769892
- Alternate Identifier(s):
- OSTI ID: 1809493
- Report Number(s):
- SAND-2019-13706J
Journal ID: ISSN 0167-6636; 681373
- Grant/Contract Number:
- AC04-94AL85000; NA0003525
- Resource Type:
- Accepted Manuscript
- Journal Name:
- Mechanics of Materials
- Additional Journal Information:
- Journal Volume: 152; Journal ID: ISSN 0167-6636
- Publisher:
- Elsevier
- Country of Publication:
- United States
- Language:
- English
- Subject:
- 36 MATERIALS SCIENCE; Mechanical characterization; Strain rate; 304L-VAR stainless Steel; Stress-strain; Tension; Intermediate strain rate
Citation Formats
Jin, Huiqing, Sanborn, Brett, Lu, Wei-Yang, and Song, Bo. Mechanical characterization of 304L-VAR stainless steel in tension with a full coverage of low, intermediate, and high strain rates. United States: N. p., 2021.
Web. doi:10.1016/j.mechmat.2020.103654.
Jin, Huiqing, Sanborn, Brett, Lu, Wei-Yang, & Song, Bo. Mechanical characterization of 304L-VAR stainless steel in tension with a full coverage of low, intermediate, and high strain rates. United States. https://doi.org/10.1016/j.mechmat.2020.103654
Jin, Huiqing, Sanborn, Brett, Lu, Wei-Yang, and Song, Bo. Fri .
"Mechanical characterization of 304L-VAR stainless steel in tension with a full coverage of low, intermediate, and high strain rates". United States. https://doi.org/10.1016/j.mechmat.2020.103654. https://www.osti.gov/servlets/purl/1769892.
@article{osti_1769892,
title = {Mechanical characterization of 304L-VAR stainless steel in tension with a full coverage of low, intermediate, and high strain rates},
author = {Jin, Huiqing and Sanborn, Brett and Lu, Wei-Yang and Song, Bo},
abstractNote = {A 304L-VAR stainless steel is mechanically characterized in tension over a full range of strain rates from low, intermediate, to high using a variety of apparatuses. While low- and high-strain-rate tests are conducted with a conventional Instron and a Kolsky tension bar, the tensile tests at intermediate strain rates are conducted with a fast MTS and a Drop-Hopkinson bar. The fast MTS used in this study is able to obtain reliable tensile response at the strain rates up to 150 s-1, whereas the lower limit for the Drop-Hopkinson bar is 100 s-1. Combining the fast MTS and the Drop-Hopkinson bar closes the gap within the intermediate strain rate regime. Using these four apparatuses, the tensile stress-strain curves of the 304L-VAR stainless steel are obtained at strain rates on each order of magnitude ranging from 0.0001 to 2580 s-1. All tensile stress-strain curves exhibit linear elasticity followed by significant work hardening prior to necking. After necking occurrs, the specimen load decreases, and the deformation becomes highly localized until fracture. The tensile stress-strain response of the 304L-VAR stainless steel exhibits strain rate dependence. The flow stress increases with increasing strain rate and is described with a power law. The strain-rate sensitivity is also strain-dependent, possibly due to thermosoftening caused by adiabatic heating at high strain rates. The 304L-VAR stainless steel shows significant ductility. The true strains at the onset of necking and at failure are determined. The results show that the true strains at both onset of necking and failure decrease with increasing strain rate. The true failure strains are approximately 200% at low strain rates but are significantly lower (~100%) at high strain rates. The transition of true failure strain occurs within the intermediate strain rate range between 10-2 and 102 s-1. A Boltzmann description is used to present the effect of nominal strain rate on true failure strain.},
doi = {10.1016/j.mechmat.2020.103654},
journal = {Mechanics of Materials},
number = ,
volume = 152,
place = {United States},
year = {Fri Jan 01 00:00:00 EST 2021},
month = {Fri Jan 01 00:00:00 EST 2021}
}
Works referenced in this record:
Tensile Testing of Materials at Impact Rates of Strain
journal, June 1960
- Harding, J.; Wood, E. O.; Campbell, J. D.
- Journal of Mechanical Engineering Science, Vol. 2, Issue 2
Effect of Strain Rate on Stress Corrosion Cracking of 316L Austenitic Stainless Steel in Boiling MgCl2 Environment
journal, December 2012
- Hassani, A.; Habibolahzadeh, A.; Javadi, A. H.
- Journal of Materials Engineering and Performance, Vol. 22, Issue 6
Behavior of Type 316 Austenitic Stainless Steel Under Slow Strain Rate Technique Conditions in Lithium Bromide Heavy Brine Environments
journal, January 1996
- Itzhak, D.; Elias, O.; Greenberg, Y.
- CORROSION, Vol. 52, Issue 1
Simulation of the impact of internal pressure on the integrity of a hydrogen-charged Type-316L stainless steel during slow strain rate tensile test
journal, April 2018
- Sezgin, Jean-Gabriel; Yamabe, Junichiro
- International Journal of Hydrogen Energy, Vol. 43, Issue 17
Correction of specimen strain measurement in Kolsky tension bar experiments on work-hardening materials
journal, October 2019
- Song, Bo; Sanborn, Brett; Susan, Donald
- International Journal of Impact Engineering, Vol. 132
Dislocation‐mechanics‐based constitutive relations for material dynamics calculations
journal, March 1987
- Zerilli, Frank J.; Armstrong, Ronald W.
- Journal of Applied Physics, Vol. 61, Issue 5
High speed tensile test of steel sheets for the stress-strain curve at the intermediate strain rate
journal, March 2009
- Huh, H.; Lim, J. H.; Park, S. H.
- International Journal of Automotive Technology, Vol. 10, Issue 2
An Apparatus for Tensile Characterization of Materials within the Upper Intermediate Strain Rate Regime
journal, March 2019
- Song, B.; Sanborn, B.; Heister, J. D.
- Experimental Mechanics, Vol. 59, Issue 7
Characterization of Dynamic Tensile Testing Using Aluminum Alloy 6061-T6 at Intermediate Strain Rates
journal, October 2011
- Zhu, Deju; Mobasher, Barzin; Rajan, S. D.
- Journal of Engineering Mechanics, Vol. 137, Issue 10
High temperature microstructural evolution of 304L stainless steel as function of pre-strain and strain rate
journal, May 2010
- Lee, Woei-Shyan; Lin, Chi-Feng; Chen, Tao-Hsing
- Materials Science and Engineering: A, Vol. 527, Issue 13-14
Dynamic tensile testing of plastic materials
journal, April 2008
- Xiao, Xinran
- Polymer Testing, Vol. 27, Issue 2
Effects of prestrain on high temperature impact properties of 304L stainless steel
journal, April 2010
- Lee, Woei-Shyan; Lin, Chi-Feng; Chen, Tao-Hsing
- Journal of Materials Research, Vol. 25, Issue 4
Effect of strain rate on the strain-induced γ → α′-martensite transformation and mechanical properties of austenitic stainless steels
journal, February 2005
- Talonen, Juho; Hänninen, Hannu; Nenonen, Pertti
- Metallurgical and Materials Transactions A, Vol. 36, Issue 2
Experimental survey on the behaviour of AISI 304 steel sheets subjected to perforation
journal, December 2010
- Rodríguez-Martínez, J. A.; Rusinek, A.; Pesci, R.
- Thin-Walled Structures, Vol. 48, Issue 12
Dynamic Tensile Characterization of a 4330-V Steel with Kolsky Bar Techniques
journal, June 2013
- Song, B.; Antoun, B. R.; Jin, H.
- Experimental Mechanics, Vol. 53, Issue 9
A Novel Splitting-Beam Laser Extensometer Technique for Kolsky Tension Bar Experiment
journal, January 2015
- Nie, Xu; Song, Bo; Loeffler, Colin M.
- Journal of Dynamic Behavior of Materials, Vol. 1, Issue 1
Experimental study on the martensitic transformation in AISI 304 steel sheets subjected to tension under wide ranges of strain rate at room temperature
journal, July 2011
- Rodríguez-Martínez, J. A.; Pesci, R.; Rusinek, A.
- Materials Science and Engineering: A, Vol. 528, Issue 18
Influence of strain rate on tensile characteristics of SUS304 metastable austenitic stainless steel
journal, November 2013
- Li, Xifeng; Chen, Jun; Ye, Liyan
- Acta Metallurgica Sinica (English Letters), Vol. 26, Issue 6
Effect of strain rate on quasistatic tensile flow behaviour of solution annealed 304 austenitic stainless steel at room temperature
journal, May 2010
- Kundu, Amrita; Chakraborti, Pravash Chandra
- Journal of Materials Science, Vol. 45, Issue 20
Strain rate behaviour in tension of austenitic stainless steel used for reinforcing bars
journal, October 2012
- Cadoni, Ezio; Fenu, Luigi; Forni, Daniele
- Construction and Building Materials, Vol. 35
Dynamic plasticity: Macroscopic and microscopic aspects
journal, July 1973
- Campbell, J. D.
- Materials Science and Engineering, Vol. 12, Issue 1
Effect of Irradiation on the Strain Rate Dependence of Type 304 Stainless-Steel Mechanical Properties
journal, October 1972
- Steichen, J. M.
- Nuclear Technology, Vol. 16, Issue 1
Correspondence of fracture surface features with mechanical properties in 304LN stainless steel
journal, November 2008
- Das, Arpan; Sivaprasad, S.; Chakraborti, P. C.
- Materials Science and Engineering: A, Vol. 496, Issue 1-2
Dynamical behaviour and microstructural evolution of a nitrogen-alloyed austenitic stainless steel
journal, May 2008
- Fréchard, S.; Redjaïmia, A.; Lach, E.
- Materials Science and Engineering: A, Vol. 480, Issue 1-2
Impact properties and microstructure evolution of 304L stainless steel
journal, June 2001
- Lee, Woei-Shyan; Lin, Chi-Feng
- Materials Science and Engineering: A, Vol. 308, Issue 1-2
A Modified Johnson–Cook Model for Dynamic Response of Metals with an Explicit Strain- and Strain-Rate-Dependent Adiabatic Thermosoftening Effect
journal, June 2019
- Song, B.; Sanborn, B.
- Journal of Dynamic Behavior of Materials, Vol. 5, Issue 3