Microstructural evolution of an aluminide coating on alloy 625 during wet air exposure at 900 °C and 1000 °C
Abstract
The microstructural changes of the aluminized alloy 625 during cyclic oxidation in air + 6% H2O at 900 °C and 1000 °C were analyzed using optical metallography (OM), scanning electron microscopy (SEM) with energy and wave length dispersive X-ray analysis (EDX/WDX) as well as electron backscatter diffraction (EBSD). An in-house developed thermodynamic-kinetic procedure was employed to predict the microstructural evolution of aluminized alloy 625 during high temperature exposure by considering simultaneously occurring surface oxidation and interdiffusion processes. Because of the lack of mobility data for the relevant alloying elements in the σ-phase, assumptions for the mobilities were made based on the value of the mobilities in α-Cr. Despite these assumptions, the calculated results were found to be in good agreement with experimental observations. The complete depletion of β-NiAl in the coating observed during exposure at 1000 °C was correctly predicted by the model. The model was also able to infer dissolution of the precipitate phases α-Cr and σ in the interdiffusion zone during exposures at 900 °C and 1000 °C. The model was yet unable to predict the formation of the μ-phase in the alloy after 1000 h of exposure at 1000 °C. The developed modelling method offers the potentialmore »
- Publication Date:
- Research Org.:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- Sponsoring Org.:
- USDOE; China Scholarship Council
- OSTI Identifier:
- 1558506
- Grant/Contract Number:
- AC05-00OR22725
- Resource Type:
- Accepted Manuscript
- Journal Name:
- Surface and Coatings Technology
- Additional Journal Information:
- Journal Volume: 354; Journal Issue: C; Journal ID: ISSN 0257-8972
- Publisher:
- Elsevier
- Country of Publication:
- United States
- Language:
- English
- Subject:
- 36 MATERIALS SCIENCE; Aluminide coating; Alloy 625; Microstructure; Interdiffusion; Simulation; Thermodynamic-kinetic data
Citation Formats
Leng, Wencai, Pillai, Rishi R., Huczkowski, P., Naumenko, D., and Quadakkers, Willem Joseph. Microstructural evolution of an aluminide coating on alloy 625 during wet air exposure at 900 °C and 1000 °C. United States: N. p., 2018.
Web. doi:10.1016/j.surfcoat.2018.09.043.
Leng, Wencai, Pillai, Rishi R., Huczkowski, P., Naumenko, D., & Quadakkers, Willem Joseph. Microstructural evolution of an aluminide coating on alloy 625 during wet air exposure at 900 °C and 1000 °C. United States. https://doi.org/10.1016/j.surfcoat.2018.09.043
Leng, Wencai, Pillai, Rishi R., Huczkowski, P., Naumenko, D., and Quadakkers, Willem Joseph. Tue .
"Microstructural evolution of an aluminide coating on alloy 625 during wet air exposure at 900 °C and 1000 °C". United States. https://doi.org/10.1016/j.surfcoat.2018.09.043. https://www.osti.gov/servlets/purl/1558506.
@article{osti_1558506,
title = {Microstructural evolution of an aluminide coating on alloy 625 during wet air exposure at 900 °C and 1000 °C},
author = {Leng, Wencai and Pillai, Rishi R. and Huczkowski, P. and Naumenko, D. and Quadakkers, Willem Joseph},
abstractNote = {The microstructural changes of the aluminized alloy 625 during cyclic oxidation in air + 6% H2O at 900 °C and 1000 °C were analyzed using optical metallography (OM), scanning electron microscopy (SEM) with energy and wave length dispersive X-ray analysis (EDX/WDX) as well as electron backscatter diffraction (EBSD). An in-house developed thermodynamic-kinetic procedure was employed to predict the microstructural evolution of aluminized alloy 625 during high temperature exposure by considering simultaneously occurring surface oxidation and interdiffusion processes. Because of the lack of mobility data for the relevant alloying elements in the σ-phase, assumptions for the mobilities were made based on the value of the mobilities in α-Cr. Despite these assumptions, the calculated results were found to be in good agreement with experimental observations. The complete depletion of β-NiAl in the coating observed during exposure at 1000 °C was correctly predicted by the model. The model was also able to infer dissolution of the precipitate phases α-Cr and σ in the interdiffusion zone during exposures at 900 °C and 1000 °C. The model was yet unable to predict the formation of the μ-phase in the alloy after 1000 h of exposure at 1000 °C. The developed modelling method offers the potential to predict microstructural changes of aluminized nickel base alloys thus reducing cost and time consuming experimental efforts.},
doi = {10.1016/j.surfcoat.2018.09.043},
journal = {Surface and Coatings Technology},
number = C,
volume = 354,
place = {United States},
year = {Tue Sep 18 00:00:00 EDT 2018},
month = {Tue Sep 18 00:00:00 EDT 2018}
}
Free Publicly Available Full Text
Publisher's Version of Record
Other availability
Search WorldCat to find libraries that may hold this journal
Cited by: 14 works
Citation information provided by
Web of Science
Web of Science
Figures / Tables:
Table 1: Nominal chemical composition of alloy 625 in wt. %.
All figures and tables
(21 total)
Save to My Library
You must Sign In or Create an Account in order to save documents to your library.
Works referenced in this record:
The performance of Alloy 625 in long-term intermediate temperature applications
journal, January 1994
- Thomas, Charles; Tait, Peter
- International Journal of Pressure Vessels and Piping, Vol. 59, Issue 1-3
Sub-Scale Depletion and Enrichment Processes During High Temperature Oxidation of the Nickel Base Alloy 625 in the Temperature Range 900–1000 °C
journal, December 2010
- Chyrkin, A.; Huczkowski, P.; Shemet, V.
- Oxidation of Metals, Vol. 75, Issue 3-4
Effect of Specimen Thickness on Microstructural Changes During Oxidation of the NiCrW Alloy 230 at 950–1050°C
journal, September 2015
- Jalowicka, A.; Duan, R.; Huczkowski, P.
- JOM, Vol. 67, Issue 11
Oxidation behaviour and microstructural stability of alloy 625 during long-term exposure in steam
journal, June 2014
- Garcia-Fresnillo, L.; Chyrkin, A.; Böhme, C.
- Journal of Materials Science, Vol. 49, Issue 17
Alloy phase transformations driven by high temperature corrosion processes
journal, February 2002
- Young, David J.; Gleeson, Brian
- Corrosion Science, Vol. 44, Issue 2
Modelling compositional changes in nickel base alloy 602 CA during high temperature oxidation
journal, January 2015
- Chyrkin, A.; Sloof, W. G.; Pillai, R.
- Materials at High Temperatures, Vol. 32, Issue 1-2
The oxidation of finite samples of heat-resistant alloys
journal, January 1972
- Whittle, D. P.
- Corrosion Science, Vol. 12, Issue 11
Technical and Economical Aspects of Current Thermal Barrier Coating Systems for Gas Turbine Engines by Thermal Spray and EBPVD: A Review
journal, February 2008
- Feuerstein, Albert; Knapp, James; Taylor, Thomas
- Journal of Thermal Spray Technology, Vol. 17, Issue 2
Chromium Volatilization Rates from Cr2O3 Scales into Flowing Gases Containing Water Vapor
journal, November 2006
- Young, D. J.; Pint, B. A.
- Oxidation of Metals, Vol. 66, Issue 3-4
Development of NiCrAlY Alloys for Corrosion-Resistant Coatings and Thermal Barrier Coatings of Gas Turbine Components
journal, November 1999
- Nickel, H.; Clemens, D.; Quadakkers, W. J.
- Journal of Pressure Vessel Technology, Vol. 121, Issue 4
Oxidation characteristics of a platinized MCrAlY bond coat for TBC systems during cyclic oxidation at 1000 °C
journal, September 2005
- Quadakkers, W. J.; Shemet, V.; Sebold, D.
- Surface and Coatings Technology, Vol. 199, Issue 1
Current Research on the Surface Protection of Superalloys for Gas Turbine Engines
journal, October 1970
- Goward, G. W.
- JOM, Vol. 22, Issue 10
Progress in corrosion protection as a requirement for technical progress: Progress in corrosion protection
journal, July 2009
- Fürbeth, W.; Schütze, M.
- Materials and Corrosion, Vol. 60, Issue 7
Development of a metal dusting resistant functional coating by Sn and Al pack cementation
journal, August 2016
- Madloch, S.; Galetz, M. C.; Geers, C.
- Surface and Coatings Technology, Vol. 299
The influence of molybdenum on the degradation resistance of aluminized iron-nickel-base alloys in sulphidizing environments
journal, August 1992
- Green, S. W.; Stott, F. H.; Wood, N. J.
- Materials at High Temperatures, Vol. 10, Issue 3
Microstructural Study on Oxidation of Aluminized Coating on Inconel 625
journal, April 2002
- Khalid, F. A.; Hussain, N.; Qureshi, A. H.
- Journal of Materials Engineering and Performance, Vol. 11, Issue 2
Effect of gas flow rate on oxidation behaviour of alloy 625 in wet air in the temperature range 900-1000 °C: Effect of gas flow rate on oxidation behaviour of alloy 625
journal, July 2016
- Huczkowski, P.; Lehnert, W.; Angermann, H. -H.
- Materials and Corrosion, Vol. 68, Issue 2
Electron backscatter diffraction: Strategies for reliable data acquisition and processing
journal, September 2009
- Randle, Valerie
- Materials Characterization, Vol. 60, Issue 9
Identification of phases in zinc alloy powders using electron backscatter diffraction
journal, May 2006
- Perez, Martin G.; Kenik, Edward A.; O’Keefe, Matthew J.
- Materials Science and Engineering: A, Vol. 424, Issue 1-2
Application of electron backscatter diffraction to the study of phase transformations
journal, March 2007
- Gourgues-Lorenzon, A. F.
- International Materials Reviews, Vol. 52, Issue 2
Effect of magnetic transition on the lattice expansion of nickel
journal, March 1986
- Yousuf, M.; Sahu, P. C.; Jajoo, H. K.
- Journal of Physics F: Metal Physics, Vol. 16, Issue 3
Lattice parameters of Ni(γ), Ni3Al(γ') and Ni3Ga(γ') solid solutions with additions of transition and B-subgroup elements
journal, June 1985
- Mishima, Yoshinao; Ochiai, Shouichi; Suzuki, Tomoo
- Acta Metallurgica, Vol. 33, Issue 6
An alternative description of the structure of NaCd 2
journal, February 1987
- Yang, Q. -B.; Andersson, S.; Stenberg, L.
- Acta Crystallographica Section B Structural Science, Vol. 43, Issue 1
Soft X-Ray Emission Spectra of Aluminium in β-Phase Cu–Ni–Al and Cu–Mn–Al Alloys
journal, May 1983
- Tanaka, Kazuhide; Saito, Takamobu; Yasuda, Masabumi
- Journal of the Physical Society of Japan, Vol. 52, Issue 5
Vacuum‐evaporated films of chromium with the A‐15 structure
journal, May 1977
- Doherty, C. J.; Poate, J. M.; Voorhoeve, R. J. H.
- Journal of Applied Physics, Vol. 48, Issue 5
The crystal structure of Cr23C6
journal, October 1972
- Bowman, A. L.; Arnold, G. P.; Storms, E. K.
- Acta Crystallographica Section B Structural Crystallography and Crystal Chemistry, Vol. 28, Issue 10
Thermal Expansion of Some Transition Metal Carbides
journal, May 1958
- Elliott, Reed O.; Kempter, Charles P.
- The Journal of Physical Chemistry, Vol. 62, Issue 5
Magneto-optical properties of metallic ferromagnetic materials
journal, August 1983
- Buschow, K. H. J.; van Engen, P. G.; Jongebreur, R.
- Journal of Magnetism and Magnetic Materials, Vol. 38, Issue 1, p. 1-22
Precipitation Hardening in the Fe‐W System
journal, November 1941
- Smith, Charles S.
- Journal of Applied Physics, Vol. 12, Issue 11
A homogenization approach to diffusion simulations applied to α+γ Fe–Cr–Ni diffusion couples
journal, May 2006
- Larsson, Henrik; Engström, Anders
- Acta Materialia, Vol. 54, Issue 9
Multiphase diffusion simulations in 1D using the DICTRA homogenization model
journal, September 2009
- Larsson, Henrik; Höglund, Lars
- Calphad, Vol. 33, Issue 3
Gas nitriding of high vanadium steels—experiments and simulations
journal, September 2004
- Larsson, Henrik; Ågren, John
- Metallurgical and Materials Transactions A, Vol. 35, Issue 9
Thermo-Calc & DICTRA, computational tools for materials science
journal, June 2002
- Andersson, J-O; Helander, Thomas; Höglund, Lars
- Calphad, Vol. 26, Issue 2
Methods to increase computational efficiency of CALPHAD-based thermodynamic and kinetic models employed in describing high temperature material degradation
journal, June 2016
- Pillai, R.; Galiullin, T.; Chyrkin, A.
- Calphad, Vol. 53
Development of a diffusion mobility database for Ni-base superalloys
journal, February 2002
- Campbell, C. E.; Boettinger, W. J.; Kattner, U. R.
- Acta Materialia, Vol. 50, Issue 4
Assessment of the diffusion mobilites in the γ′ and B2 phases in the Ni–Al–Cr system
journal, September 2008
- Campbell, C. E.
- Acta Materialia, Vol. 56, Issue 16
On the properties of α/α+β ternary diffusion couples
journal, January 2000
- Boettinger, W. J.; Coriell, S. R.; Campbell, C. E.
- Acta Materialia, Vol. 48, Issue 2
Growth mechanisms of oxide scales on ODS alloys in the temperature range 1000-1100°C
journal, December 1990
- Quadakkers, W. J.
- Materials and Corrosion/Werkstoffe und Korrosion, Vol. 41, Issue 12
The prediction of breakaway oxidation for alumina forming ODS alloys using oxidation diagrams
journal, April 1994
- Quadakkers, W. J.; Bongartz, K.
- Materials and Corrosion/Werkstoffe und Korrosion, Vol. 45, Issue 4
Influence of Chemical Composition of Nickel Based Superalloy on the Formation of Aluminide Coatings
journal, January 2011
- Zielińska, M.; Sieniawski, J.; Yavorska, M.
- Archives of Metallurgy and Materials, Vol. 56, Issue 1
A contemporary view of nickel-base superalloys
journal, October 1966
- Sims, Chester T.
- JOM, Vol. 18, Issue 10
Future Directions in the Field of High-Temperature Corrosion Research
journal, February 2017
- Schütze, M.; Quadakkers, W. J.
- Oxidation of Metals, Vol. 87, Issue 5-6
The Metallurgy of Alloy 625
conference, January 1994
- Floreen, S.; Fuchs, G. E.; Yang, W. J.
- Superalloys 718, 625, 706 and Various Derivatives (1994)
Works referencing / citing this record:
Effect of surface modification on the hot corrosion resistance of Inconel 718 at 700 °C
journal, May 2019
- Kumar, Sharvan; Satapathy, Biswajeet; Pradhan, Dhananjay
- Materials Research Express, Vol. 6, Issue 8
Figures / Tables found in this record:
Figures/Tables have been extracted from DOE-funded journal article accepted manuscripts.