Crack growth in laser powder bed fusion fabricated alloy 718 at 650 °C under static and cyclic loading

Ostergaard, Halsey E.; Pribe, Joshua D.; Hasib, M. Tarik; Siegmund, Thomas; Kruzic, Jamie J.

doi:10.1016/j.ijfatigue.2025.108810

Title: Crack growth in laser powder bed fusion fabricated alloy 718 at 650 °C under static and cyclic loading

Journal Article · 31 March 2025 · International Journal of Fatigue

DOI: https://doi.org/10.1016/j.ijfatigue.2025.108810 · OSTI ID:2506828

;

; Hasib, M. Tarik; Siegmund, Thomas;

Not Available

View Journal Article

Cite

Export

Save

Sponsoring Organization:: USDOE

Grant/Contract Number:: FE0011796

OSTI ID:: 2506828

Journal Information:: International Journal of Fatigue, Journal Name: International Journal of Fatigue Journal Issue: C Vol. 193; ISSN 0142-1123

Publisher:: ElsevierCopyright Statement

Country of Publication:: United Kingdom

Language:: English

References (29)

Slightly curved or kinked cracks Cotterell, B.; Rice, J. R. International Journal of Fracture, Vol. 16, Issue 2 https://doi.org/10.1007/BF00012619	journal	April 1980
Frequency and wave-form effects on the fatigue crack growth behavior of alloy 718 at 298 K and 823 K Clavel, M.; Pineau, A. Metallurgical Transactions A, Vol. 9, Issue 4 https://doi.org/10.1007/BF02646402	journal	April 1978
Fatigue crack deflection and fracture surface contact: Micromechanical models Suresh, S. Metallurgical Transactions A, Vol. 16, Issue 2 https://doi.org/10.1007/BF02816051	journal	February 1985
Metallurgical control of fatigue crack propagation in superalloys Chang, K. -M.; Henry, M. F.; Benz, M. G. JOM, Vol. 42, Issue 12 https://doi.org/10.1007/BF03220467	journal	December 1990
Inconel 718 produced by laser powder bed fusion: an overview of the influence of processing parameters on microstructural and mechanical properties Marques, Ana; Cunha, Ângela; Silva, Mariana Rodrigues The International Journal of Advanced Manufacturing Technology, Vol. 121, Issue 9-10 https://doi.org/10.1007/s00170-022-09693-0	journal	July 2022
A Grain Boundary Fracture Model for Predicting Dynamic Embrittlement and Oxidation-Induced Cracking in Superalloys Chan, Kwai S. Metallurgical and Materials Transactions A, Vol. 46, Issue 6 https://doi.org/10.1007/s11661-015-2860-1	journal	March 2015
On the Dwell-Fatigue Crack Propagation Behavior of a High-Strength Ni-Base Superalloy Manufactured by Selective Laser Melting Deng, Dunyong; Eriksson, Robert; Peng, Ru Lin Metallurgical and Materials Transactions A, Vol. 51, Issue 2 https://doi.org/10.1007/s11661-019-05548-8	journal	December 2019
Dynamic embrittlement of boron-doped Ni3Al alloys at 600°C Liu, C. T.; White, C. L. Acta Metallurgica, Vol. 35, Issue 3 https://doi.org/10.1016/0001-6160(87)90187-8	journal	March 1987
The development of columnar grain and single crystal high temperature materials through directional solidification Versnyder, Francis I.; Shank, M. E. Materials Science and Engineering, Vol. 6, Issue 4 https://doi.org/10.1016/0025-5416(70)90050-9	journal	October 1970
The effect of microstructure and environment on the crack growth behaviour of Inconel 718 alloy at 650 °C under fatigue, creep and combined loading Pédron, J. P.; Pineau, A. Materials Science and Engineering, Vol. 56, Issue 2 https://doi.org/10.1016/0025-5416(82)90167-7	journal	November 1982
Effect of environment on the rupture behavior of alloys 909 and 718 Hayes, R. W.; Smith, D. F.; Wanner, E. A. Materials Science and Engineering: A, Vol. 177, Issue 1-2 https://doi.org/10.1016/0921-5093(94)90476-6	journal	April 1994
Effect of load ratio and maximum stress intensity on the fatigue threshold in Ti–6Al–4V Boyce, B. L.; Ritchie, R. O. Engineering Fracture Mechanics, Vol. 68, Issue 2 https://doi.org/10.1016/S0013-7944(00)00099-0	journal	February 2001
The effect of grain-boundary-engineering-type processing on oxygen-induced cracking of IN718 Krupp, Ulrich; Kane, William M.; Liu, Xinyu Materials Science and Engineering: A, Vol. 349, Issue 1-2 https://doi.org/10.1016/S0921-5093(02)00753-0	journal	May 2003
Oxygen-induced intergranular cracking of a Ni-base alloy at elevated temperatures—an example of dynamic embrittlement Pfaendtner, J. A.; McMahon Jr, C. J. Acta Materialia, Vol. 49, Issue 16 https://doi.org/10.1016/S1359-6454(01)00005-2	journal	September 2001
Structure-dependent intergranular oxidation in Ni–Fe polycrystalline alloy Yamaura, S.; Igarashi, Y.; Tsurekawa, S. Acta Materialia, Vol. 47, Issue 4 https://doi.org/10.1016/S1359-6454(99)00007-5	journal	March 1999
High temperature fatigue of nickel-base superalloys – A review with special emphasis on deformation modes and oxidation Pineau, Andre; Antolovich, Stephen D. Engineering Failure Analysis, Vol. 16, Issue 8 https://doi.org/10.1016/j.engfailanal.2009.01.010	journal	December 2009
Room and elevated temperature fatigue crack propagation behavior of Inconel 718 alloy fabricated by laser powder bed fusion Kim, Sumin; Choi, Heesoo; Lee, Jehyun International Journal of Fatigue, Vol. 140 https://doi.org/10.1016/j.ijfatigue.2020.105802	journal	November 2020
Near-threshold fatigue crack growth in laser powder bed fusion produced alloy 718 Ostergaard, Halsey E.; Pribe, Joshua D.; Tarik Hasib, M. International Journal of Fatigue, Vol. 163 https://doi.org/10.1016/j.ijfatigue.2022.107041	journal	October 2022
A critical review on the microstructure and mechanical properties correlation of additively manufactured nickel-based superalloys Shahwaz, Md.; Nath, Prekshya; Sen, Indrani Journal of Alloys and Compounds, Vol. 907 https://doi.org/10.1016/j.jallcom.2022.164530	journal	June 2022
Microstructural influence on fatigue crack propagation during high cycle fatigue testing of additively manufactured Alloy 718 Balachandramurthi, Arun Ramanathan; Moverare, Johan; Dixit, Nikhil Materials Characterization, Vol. 149 https://doi.org/10.1016/j.matchar.2019.01.018	journal	March 2019
A comparison study of the dwell-fatigue behaviours of additive and conventional IN718: The role of dislocation substructure on the cracking behaviour Deng, Dunyong; Peng, Ru Lin; Moverare, Johan Materials Science and Engineering: A, Vol. 797 https://doi.org/10.1016/j.msea.2020.140072	journal	October 2020
A state-of-the-art review on fatigue performance of powder bed fusion-built alloy 718 Sadeghi, Esmaeil; Karimi, Paria; Esmaeilizadeh, Reza Progress in Materials Science, Vol. 133 https://doi.org/10.1016/j.pmatsci.2022.101066	journal	March 2023
Fatigue crack growth behaviour of Inconel 718 with high temperature hold times Gustafsson, David; Moverare, Johan; Johansson, Sten Procedia Engineering, Vol. 2, Issue 1 https://doi.org/10.1016/j.proeng.2010.03.118	journal	April 2010
Effects of Stress Ratio and Hold-Time on Fatigue Crack Growth in Alloy 718 Shahinian, P.; Sadananda, K. Journal of Engineering Materials and Technology, Vol. 101, Issue 3 https://doi.org/10.1115/1.3443681	journal	July 1979
A Critical Analysis of Crack Propagation Laws Paris, P.; Erdogan, F. Journal of Basic Engineering, Vol. 85, Issue 4 https://doi.org/10.1115/1.3656900	journal	December 1963
Dynamic Embrittlement — Time–dependent Quasi–brittle Intergranular Fracture at High Temperatures Krupp, U. International Materials Reviews, Vol. 50, Issue 2 https://doi.org/10.1179/174328005X14320	journal	March 2005
Gas phase embrittlement and time dependent cracking of nickel based superalloys Woodford, D. A. Energy Materials, Vol. 1, Issue 1 https://doi.org/10.1179/174892306X99679	journal	March 2006
Fatigue crack propagation in nickel-base superalloys – effects of microstructure, load ratio, and temperature King, J. E. Materials Science and Technology, Vol. 3, Issue 9 https://doi.org/10.1179/mst.1987.3.9.750	journal	September 1987
SAGBO Mechanism on High Temperature Cracking Behavior of Ni-base Superalloys Carpenter, W.; Kang, B. S. -J.; Chang, K. M. Superalloys 718, 625, 706 and Various Derivatives (1997) https://doi.org/10.7449/1997/Superalloys_1997_679_688	conference	January 1997

Similar Records

Near-threshold fatigue crack growth in laser powder bed fusion produced alloy 718

Journal Article · 2022 · International Journal of Fatigue · OSTI ID:1873931

Ostergaard, Halsey E.; Pribe, Joshua D.; Tarik Hasib, M.; +3 more

Transient creep‐fatigue crack growth in creep‐brittle materials: Application to Alloy 718

Journal Article · 2022 · Fatigue and Fracture of Engineering Materials and Structures · OSTI ID:1876460

Pribe, Joshua D.; Ostergaard, Halsey E.; Siegmund, Thomas; +1 more

Sustained-load crack-growth in Inconel 718 under nonisothermal conditions

Journal Article · 1985 · J. Eng. Mater. Technol.; (United States) · OSTI ID:6218194

Haritos, G K; Miller, D L; Nicholas, T

Title: Crack growth in laser powder bed fusion fabricated alloy 718 at 650 °C under static and cyclic loading

Citation Formats

References (29)

Similar Records

Related Subjects