Large-scale additive manufacturing tooling for extrusion-compression molds
Carbon fiber reinforced polymer composites (CFPC) have been used in additive manufacturing (AM) due to both the high-strength-to-weight and superior-stiffness-to-weight ratios. CF AM is being considered for tooling applications. In AM, CFPCs are usually aligned along the deposition direction; however, it results in anisotropic thermal properties which affect the heat transfer and warpage of the final part. In this study, three male molds with different infill patterns were produced via the material extrusion additive manufacturing (EDF-AM) process. These include (a) 0°: infill pattern along the printing direction; (b) 90°: infill pattern perpendicular to the printing direction; and (c) 0°/90°: alternate layers along and perpendicular directions. The effect of the infill pattern on thermal conductivity was analyzed and observed that 0° infill (surface temperature: 79.2°C) had the highest conductivity; and 90° infill (surface temperature: 66.4°C) had the least.
- Research Organization:
- Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- USDOE Office of Energy Efficiency and Renewable Energy (EERE)
- Grant/Contract Number:
- AC05-00OR22725
- OSTI ID:
- 1831605
- Journal Information:
- Additive Manufacturing Letters, Journal Name: Additive Manufacturing Letters Vol. 1; ISSN 2772-3690
- Publisher:
- ElsevierCopyright Statement
- Country of Publication:
- United States
- Language:
- English
Similar Records
Reducing warpage in a hybrid large-scale additive manufacturing and compression molding process
High-performance molded composites using additively manufactured preforms with controlled fiber and pore morphology