The effect of grain boundary structure on the intergranular degradation behavior of solution annealed alloy 690 in high temperature, hydrogenated water

Kuang, Wenjun; Was, Gary S.

doi:10.1016/j.actamat.2019.10.041

Title: The effect of grain boundary structure on the intergranular degradation behavior of solution annealed alloy 690 in high temperature, hydrogenated water

Journal Article · 31 December 2019 · Acta Materialia

DOI: https://doi.org/10.1016/j.actamat.2019.10.041 · OSTI ID:1780203

;

Not Available

View Accepted Manuscript (Publisher)

Cite

Export

Save

Sponsoring Organization:: USDOE

OSTI ID:: 1780203

Journal Information:: Acta Materialia, Journal Name: Acta Materialia Journal Issue: C Vol. 182; ISSN 1359-6454

Publisher:: ElsevierCopyright Statement

Country of Publication:: United States

Language:: English

References (38)

The Relationship between Grain Boundary Character and the Intergranular Oxide Distribution in IN718 Superalloy Yang, S. L.; Krupp, U.; Christ, H. -J. Advanced Engineering Materials, Vol. 7, Issue 8 https://doi.org/10.1002/adem.200500036	journal	August 2005
Accelerated Stress Corrosion Crack Initiation of Alloys 600 and 690 in Hydrogenated Supercritical Water Moss, Tyler; Was, Gary S. Metallurgical and Materials Transactions A, Vol. 48, Issue 4 https://doi.org/10.1007/s11661-016-3898-4	journal	January 2017
The Effect of Temperature on the Preferential Intergranular Oxidation Susceptibility of Alloy 600 Bertali, G.; Burke, M. G.; Scenini, F. Metallurgical and Materials Transactions A, Vol. 49, Issue 5 https://doi.org/10.1007/s11661-018-4491-9	journal	February 2018
The effect of crystallographic parameters of interphase boundaries on their surface tension and parameters of the boundary diffusion Straumal, B. B.; Klinger, L. M.; Shvindlerman, L. S. Acta Metallurgica, Vol. 32, Issue 9 https://doi.org/10.1016/0001-6160(84)90081-6	journal	September 1984
The high-temperature internal oxidation and intergranular oxidation of nickel-chromium alloys Wood, G. C.; Stott, F. H.; Whittle, D. P. Corrosion Science, Vol. 23, Issue 1 https://doi.org/10.1016/0010-938X(83)90056-2	journal	January 1983
The IGSCC, sensitization, and microstructure study of Alloys 600 and 690 Kai, J. J.; Tsai, C. H.; Yu, G. P. Nuclear Engineering and Design, Vol. 144, Issue 3 https://doi.org/10.1016/0029-5493(93)90040-G	journal	November 1993
High angle grain boundary diffusion of chromium in niobium bicrystals Li, X. M.; Chou, Y. T. Acta Materialia, Vol. 44, Issue 9 https://doi.org/10.1016/1359-6454(96)00016-X	journal	September 1996
Study of grain boundary character along intergranular stress corrosion crack paths in austenitic alloys Gertsman, V. Y.; Bruemmer, S. M. Acta Materialia, Vol. 49, Issue 9 https://doi.org/10.1016/S1359-6454(01)00064-7	journal	May 2001
Diffusion of Zn along tilt grain boundaries in Al: pressure and orientation dependence Klugkist, P. Acta Materialia, Vol. 49, Issue 15 https://doi.org/10.1016/S1359-6454(01)00210-5	journal	September 2001
Grain-boundary structure effects on intergranular stress corrosion cracking of alloy X-750 Pan, Y.; Adams, B. L.; Olson, T. Acta Materialia, Vol. 44, Issue 12 https://doi.org/10.1016/S1359-6454(96)00125-5	journal	December 1996
Orientation dependence of Ge diffusion along symmetrical [111] tilt grain boundaries in Al Surholt, T.; Molodov, D. A.; Herzig, Chr. Acta Materialia, Vol. 46, Issue 15 https://doi.org/10.1016/S1359-6454(98)00237-7	journal	September 1998
Tracer diffusion of Au and Cu in a series of near Σ=5 (310)[001] symmetrical Cu tilt grain boundaries Budke, E.; Surholt, T.; Prokofjev, S. I. Acta Materialia, Vol. 47, Issue 2 https://doi.org/10.1016/S1359-6454(98)00381-4	journal	January 1999
The inclination dependence of gold tracer diffusion along a Σ3 twin grain boundary in copper Minkwitz, C.; Herzig, Chr.; Rabkin, E. Acta Materialia, Vol. 47, Issue 4 https://doi.org/10.1016/S1359-6454(98)00429-7	journal	March 1999
Structure-dependent intergranular oxidation in Ni–Fe polycrystalline alloy Yamaura, S.; Igarashi, Y.; Tsurekawa, S. Acta Materialia, Vol. 47, Issue 4 https://doi.org/10.1016/S1359-6454(99)00007-5	journal	March 1999
How oxidized grain boundaries fail Dugdale, Helen; Armstrong, David E. J.; Tarleton, Edmund Acta Materialia, Vol. 61, Issue 13 https://doi.org/10.1016/j.actamat.2013.05.012	journal	August 2013
Slip band–grain boundary interactions in commercial-purity titanium Guo, Y.; Britton, T. B.; Wilkinson, A. J. Acta Materialia, Vol. 76 https://doi.org/10.1016/j.actamat.2014.05.015	journal	September 2014
Insights into the stress corrosion cracking of solution annealed alloy 690 in simulated pressurized water reactor primary water under dynamic straining Kuang, Wenjun; Song, Miao; Was, Gary S. Acta Materialia, Vol. 151 https://doi.org/10.1016/j.actamat.2018.04.002	journal	June 2018
Microstructural characteristics of the oxide scale formed on 304 stainless steel in oxygenated high temperature water Kuang, Wenjun; Han, En-Hou; Wu, Xinqiang Corrosion Science, Vol. 52, Issue 11 https://doi.org/10.1016/j.corsci.2010.07.015	journal	November 2010
The mechanism of oxide film formation on Alloy 690 in oxygenated high temperature water Kuang, Wenjun; Wu, Xinqiang; Han, En-Hou Corrosion Science, Vol. 53, Issue 11 https://doi.org/10.1016/j.corsci.2011.07.038	journal	November 2011
Effect of grain boundary characteristics on the oxidation behavior of ferritic stainless steel Phaniraj, M. P.; Kim, Dong-Ik; Cho, Young Whan Corrosion Science, Vol. 53, Issue 12 https://doi.org/10.1016/j.corsci.2011.08.020	journal	December 2011
Influence of dissolved oxygen concentration on the oxide film formed on Alloy 690 in high temperature water Kuang, Wenjun; Wu, Xinqiang; Han, En-Hou Corrosion Science, Vol. 69 https://doi.org/10.1016/j.corsci.2012.12.003	journal	April 2013
The effects of grain boundary carbide density and strain rate on the stress corrosion cracking behavior of cold rolled Alloy 690 Kuang, Wenjun; Was, Gary S. Corrosion Science, Vol. 97 https://doi.org/10.1016/j.corsci.2015.04.020	journal	August 2015
Intergranular oxidation of Ni-based Alloy 600 in a simulated PWR primary water environment Lim, Yun Soo; Kim, Sung Woo; Hwang, Seong Sik Corrosion Science, Vol. 108 https://doi.org/10.1016/j.corsci.2016.02.040	journal	July 2016
The oxidation of alloy 690 in simulated pressurized water reactor primary water Kuang, Wenjun; Song, Miao; Wang, Peng Corrosion Science, Vol. 126 https://doi.org/10.1016/j.corsci.2017.07.004	journal	September 2017
The effect of cold rolling on grain boundary structure and stress corrosion cracking susceptibility of twins in alloy 690 in simulated PWR primary water environment Kuang, Wenjun; Was, Gary S.; Miller, Cody Corrosion Science, Vol. 130 https://doi.org/10.1016/j.corsci.2017.11.002	journal	January 2018
Temperature-dependent selective oxidation processes for Ni-5Cr and Ni-4Al Kruska, Karen; Schreiber, Daniel K.; Olszta, Matthew J. Corrosion Science, Vol. 139 https://doi.org/10.1016/j.corsci.2018.04.037	journal	July 2018
Mechanism of dislocation channel-induced irradiation assisted stress corrosion crack initiation in austenitic stainless steel McMurtrey, M. D.; Cui, B.; Robertson, I. Current Opinion in Solid State and Materials Science, Vol. 19, Issue 5 https://doi.org/10.1016/j.cossms.2015.04.001	journal	October 2015
Stress corrosion crack initiation in Alloy 690 in high temperature water Moss, Tyler; Kuang, Wenjun; Was, Gary S. Current Opinion in Solid State and Materials Science, Vol. 22, Issue 1 https://doi.org/10.1016/j.cossms.2018.02.001	journal	February 2018
Slip transfer and plastic strain accumulation across grain boundaries in Hastelloy X Abuzaid, Wael Z.; Sangid, Michael D.; Carroll, Jay D. Journal of the Mechanics and Physics of Solids, Vol. 60, Issue 6 https://doi.org/10.1016/j.jmps.2012.02.001	journal	June 2012
Strain incompatibilities and their role in intergranular cracking of irradiated 316L stainless steel West, E. A.; Was, G. S. Journal of Nuclear Materials, Vol. 441, Issue 1-3 https://doi.org/10.1016/j.jnucmat.2012.10.021	journal	October 2013
Analysis of stress corrosion cracking in alloy 718 following commercial reactor exposure Leonard, Keith J.; Gussev, Maxim N.; Stevens, Jacqueline N. Journal of Nuclear Materials, Vol. 466 https://doi.org/10.1016/j.jnucmat.2015.08.039	journal	November 2015
The effects of strain rate and carbon concentration on the dynamic strain aging of cold rolled Ni-based alloy in high temperature water Kuang, Wenjun; Was, Gary S. Scripta Materialia, Vol. 107 https://doi.org/10.1016/j.scriptamat.2015.05.033	journal	October 2015
Enhanced Oxygen Diffusion Along Internal Oxide–Metal Matrix Interfaces in Ni–Al Alloys During Internal Oxidation Martínez-Villafañe, A.; Stott, F. H.; Chacon-Nava, J. G. Oxidation of Metals, Vol. 57, Issue 3/4, p. 267-279 https://doi.org/10.1023/A:1014874202052	journal	April 2002
Enhanced diffusion of oxygen during internal oxidation of nickel-base alloys Whittle, D. P.; Shida, Y.; Wood, G. C. Philosophical Magazine A, Vol. 46, Issue 6 https://doi.org/10.1080/01418618208236942	journal	December 1982
Oxidation of nickel-base welds 182 and 82 in simulated primary water of pressurised water reactors Wehbi, M.; Couvant, T.; Duhamel, C. Materials at High Temperatures, Vol. 32, Issue 1-2 https://doi.org/10.1179/1878641314Y.0000000031	journal	January 2015
Pourbaix Diagrams for the Ternary System of Iron-Chromium-Nickel Beverskog, B.; Puigdomenech, I. CORROSION, Vol. 55, Issue 11 https://doi.org/10.5006/1.3283945	journal	November 1999
Degradation of Alloy 690 After Relatively Short Times Arioka, Koji; Staehle, Roger W.; Yamada, T. CORROSION, Vol. 72, Issue 10 https://doi.org/10.5006/2107	journal	October 2016
Precursor Evolution and Stress Corrosion Cracking Initiation of Cold-Worked Alloy 690 in Simulated Pressurized Water Reactor Primary Water Zhai, Ziqing; Toloczko, Mychailo; Kruska, Karen CORROSION, Vol. 73, Issue 10 https://doi.org/10.5006/2470	journal	May 2017

Similar Records

The effects of grain boundary carbide density and strain rate on the stress corrosion cracking behavior of cold rolled Alloy 690

Journal Article · 2015 · Corrosion Science · OSTI ID:1248436

Kuang, Wenjun; Was, Gary S.

The effect of cold rolling on grain boundary structure and stress corrosion cracking susceptibility of twins in alloy 690 in simulated PWR primary water environment

Journal Article · 2017 · Corrosion Science · OSTI ID:1562752

Kuang, Wenjun; Was, Gary S.; Miller, Cody; +4 more

Grain boundary selective oxidation and intergranular stress corrosion crack growth of high-purity nickel binary alloys in high-temperature hydrogenated water

Journal Article · 2017 · Corrosion Science · OSTI ID:1413459

Bruemmer, S. M.; Olszta, M. J.; Toloczko, M. B.; +1 more

Title: The effect of grain boundary structure on the intergranular degradation behavior of solution annealed alloy 690 in high temperature, hydrogenated water

Citation Formats

References (38)

Similar Records

Related Subjects