Antibacterial dental adhesive resins containing nitrogen-doped titanium dioxide nanoparticles
Abstract
The development of dental adhesive resins with long-lasting antibacterial properties is a possible solution to overcome the problem of secondary caries in modern adhesive dentistry.Objectives: (i) Synthesis and characterization of nitrogen-doped titanium dioxide nanoparticles (N_TiO2), (ii) topographical, compositional and wettability characterization of thin-films (unaltered and experimental) and, (iii) antibacterial efficacy of N_TiO2-containing dental adhesives against Streptococcus mutans biofilms.Materials and methods: Nanoparticles were synthesized and characterized using different techniques. Specimens (diameter = 12 mm, thickness ≅ 15 μm) of OptiBond Solo Plus (Kerr Corp., USA) and experimental adhesives [50, 67 and 80% (v/v)] were fabricated, photopolymerized (1000 mW/cm2, 1 min) and UV-sterilized (254 nm, 800,000 μJ/cm2) for microscopy, spectroscopy, wettability and antibacterial testing. Wettability was assessed with a contact angle goniometer by dispensing water droplets (2 μL) onto four random locations of each specimen (16 drops/group). Drop profiles were recorded (1 min, 25 frames/s, 37 °C) and contact angles were calculated at time = 0 s (θINITIAL) and time = 59 s (θFINAL). Antibacterial testing was performed by growing S. mutans (UA159-ldh, JM10) biofilms for either 3 or 24 h (anaerobic conditions, 37 °C) with or without continuous light irradiation (410 ± 10 nm, 3 h = 38.75 J/cm2, 24 hmore »
- Authors:
-
[1];
- Univ. of Oklahoma Health Sciences Center, Oklahoma City, OK (United States)
- Univ. of Oklahoma, Norman, OK (United States)
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- Publication Date:
- Research Org.:
- Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)
- Sponsoring Org.:
- USDOE Office of Science (SC), Basic Energy Sciences (BES)
- OSTI Identifier:
- 1470843
- Grant/Contract Number:
- AC05-00OR22725
- Resource Type:
- Accepted Manuscript
- Journal Name:
- Materials Science and Engineering. C, Biomimetic Materials, Sensors and Systems
- Additional Journal Information:
- Journal Volume: 93; Journal Issue: C; Journal ID: ISSN 0928-4931
- Publisher:
- Elsevier
- Country of Publication:
- United States
- Language:
- English
- Subject:
- 36 MATERIALS SCIENCE
Citation Formats
Esteban Florez, Fernando Luis, Hiers, Rochelle Denise, Larson, Preston, Johnson, Matthew, O'Rear, Edgar, Rondinone, Adam J., and Khajotia, Sharukh Soli. Antibacterial dental adhesive resins containing nitrogen-doped titanium dioxide nanoparticles. United States: N. p., 2018.
Web. doi:10.1016/j.msec.2018.08.060.
Esteban Florez, Fernando Luis, Hiers, Rochelle Denise, Larson, Preston, Johnson, Matthew, O'Rear, Edgar, Rondinone, Adam J., & Khajotia, Sharukh Soli. Antibacterial dental adhesive resins containing nitrogen-doped titanium dioxide nanoparticles. United States. https://doi.org/10.1016/j.msec.2018.08.060
Esteban Florez, Fernando Luis, Hiers, Rochelle Denise, Larson, Preston, Johnson, Matthew, O'Rear, Edgar, Rondinone, Adam J., and Khajotia, Sharukh Soli. Sat .
"Antibacterial dental adhesive resins containing nitrogen-doped titanium dioxide nanoparticles". United States. https://doi.org/10.1016/j.msec.2018.08.060. https://www.osti.gov/servlets/purl/1470843.
@article{osti_1470843,
title = {Antibacterial dental adhesive resins containing nitrogen-doped titanium dioxide nanoparticles},
author = {Esteban Florez, Fernando Luis and Hiers, Rochelle Denise and Larson, Preston and Johnson, Matthew and O'Rear, Edgar and Rondinone, Adam J. and Khajotia, Sharukh Soli},
abstractNote = {The development of dental adhesive resins with long-lasting antibacterial properties is a possible solution to overcome the problem of secondary caries in modern adhesive dentistry.Objectives: (i) Synthesis and characterization of nitrogen-doped titanium dioxide nanoparticles (N_TiO2), (ii) topographical, compositional and wettability characterization of thin-films (unaltered and experimental) and, (iii) antibacterial efficacy of N_TiO2-containing dental adhesives against Streptococcus mutans biofilms.Materials and methods: Nanoparticles were synthesized and characterized using different techniques. Specimens (diameter = 12 mm, thickness ≅ 15 μm) of OptiBond Solo Plus (Kerr Corp., USA) and experimental adhesives [50, 67 and 80% (v/v)] were fabricated, photopolymerized (1000 mW/cm2, 1 min) and UV-sterilized (254 nm, 800,000 μJ/cm2) for microscopy, spectroscopy, wettability and antibacterial testing. Wettability was assessed with a contact angle goniometer by dispensing water droplets (2 μL) onto four random locations of each specimen (16 drops/group). Drop profiles were recorded (1 min, 25 frames/s, 37 °C) and contact angles were calculated at time = 0 s (θINITIAL) and time = 59 s (θFINAL). Antibacterial testing was performed by growing S. mutans (UA159-ldh, JM10) biofilms for either 3 or 24 h (anaerobic conditions, 37 °C) with or without continuous light irradiation (410 ± 10 nm, 3 h = 38.75 J/cm2, 24 h = 310.07 J/cm2) against the surfaces of sterile specimens.Results: N_TiO2 was successfully prepared using solvothermal methods. Doped-nanoparticles displayed higher light absorption levels when compared to undoped titania. Experimental adhesives demonstrated superior antibacterial efficacy in dark conditions.Conclusions: The findings presented herein suggest that N_TiO2 is a feasible antibacterial agent against cariogenic biofilms.},
doi = {10.1016/j.msec.2018.08.060},
journal = {Materials Science and Engineering. C, Biomimetic Materials, Sensors and Systems},
number = C,
volume = 93,
place = {United States},
year = {Sat Sep 01 00:00:00 EDT 2018},
month = {Sat Sep 01 00:00:00 EDT 2018}
}
Free Publicly Available Full Text
Publisher's Version of Record
Other availability
Search WorldCat to find libraries that may hold this journal
Cited by: 32 works
Citation information provided by
Web of Science
Web of Science
Save to My Library
You must Sign In or Create an Account in order to save documents to your library.
Works referenced in this record:
Defining the Normal Bacterial Flora of the Oral Cavity
journal, November 2005
- Aas, J. A.; Paster, B. J.; Stokes, L. N.
- Journal of Clinical Microbiology, Vol. 43, Issue 11
Streptococcus mutans, Caries and Simulation Models
journal, March 2010
- Forssten, Sofia D.; Björklund, Marika; Ouwehand, Arthur C.
- Nutrients, Vol. 2, Issue 3
Nanotechnology-based restorative materials for dental caries management
journal, August 2013
- Melo, Mary A. S.; Guedes, Sarah F. F.; Xu, Hockin H. K.
- Trends in Biotechnology, Vol. 31, Issue 8
pH-Activated Nanoparticles for Controlled Topical Delivery of Farnesol To Disrupt Oral Biofilm Virulence
journal, February 2015
- Horev, Benjamin; Klein, Marlise I.; Hwang, Geelsu
- ACS Nano, Vol. 9, Issue 3
Control of oral biofilms: Control of oral biofilms
journal, December 2010
- Flemmig, Thomas F.; Beikler, Thomas
- Periodontology 2000, Vol. 55, Issue 1
Clinical diagnosis of recurrent caries
journal, October 2005
- MjÖR, Ivar A.
- The Journal of the American Dental Association, Vol. 136, Issue 10
Review of the current status and challenges for dental posterior restorative composites: clinical, chemistry, and physical behavior considerations. Summary of discussion from the Portland Composites Symposium (POCOS) June 17?19, 2004, Oregon Health & Science University, Portland, Oregon
journal, January 2005
- Sakaguchi, R.
- Dental Materials, Vol. 21, Issue 1
A Clinical Study of Amalgam Failures
journal, October 1949
- Healey, Harry J.; Phillips, Ralph W.
- Journal of Dental Research, Vol. 28, Issue 5
An improved self-curing acrylic restoration and comparison with silicate cement restorations
journal, May 1964
- Fusayama, Takao; Hosoda, Hiroyasu; Iwamoto, Tsugio
- The Journal of Prosthetic Dentistry, Vol. 14, Issue 3
Reasons for replacement of restorations in permanent teeth in general dental practice
journal, December 2000
- Mjör, Ivar A.; Moorhead, Jacquelyn E.; Dahl, Jon E.
- International Dental Journal, Vol. 50, Issue 6
Survival and reasons for failure of amalgam versus composite posterior restorations placed in a randomized clinical trial
journal, June 2007
- Bernardo, Mario; Luis, Henrique; Martin, Michael D.
- The Journal of the American Dental Association, Vol. 138, Issue 6
Degradation, Fatigue, and Failure of Resin Dental Composite Materials
journal, August 2008
- Drummond, J. L.
- Journal of Dental Research, Vol. 87, Issue 8
Confocal laser scanning microscopic analysis of early plaque formed on resin composite and human enamel: EARLY PLAQUE ON RESIN COMPOSITE AND ENAMEL
journal, July 2003
- Konishi, N.; Torii, Y.; Kurosaki, A.
- Journal of Oral Rehabilitation, Vol. 30, Issue 8
Microbial accumulation and vitality on different restorative materials
journal, September 1993
- Hahn, R.; Weiger, R.; Netuschil, L.
- Dental Materials, Vol. 9, Issue 5
Effects of Various Resin Composite (Co)monomers and Extracts on Two Caries-associated Micro-organisms in vitro
journal, January 1998
- Hansel, C.; Leyhausen, G.; Mai, U. E. H.
- Journal of Dental Research, Vol. 77, Issue 1
Chemical composition of salivary integuments formed in vivo on solids with some established surface characteristics
journal, October 1975
- Sönju, T.; Glantz, P. -O.
- Archives of Oral Biology, Vol. 20, Issue 10
In vitro attachment of Streptococcus sanguis to dental crown and bridge cements
journal, April 1976
- ØRstavik, Dag; ØRstavik, Jon
- Journal of Oral Rehabilitation, Vol. 3, Issue 2
Auger analysis of integuments formed on different dental filling materials in vivo
journal, January 1982
- Skjørland, Kjeld Kr.
- Acta Odontologica Scandinavica, Vol. 40, Issue 3
Mutans Streptococci in Plaque from Margins of Amalgam, Composite, and Glass-ionomer Restorations
journal, March 1990
- Svanberg, M.; Mjör, I. A.; Ørstavik, D.
- Journal of Dental Research, Vol. 69, Issue 3
Long-term release of chlorhexidine from dental adhesive resin system using human serum albumin nanoparticles
journal, February 2014
- Kim, Hyun-Jin; Kwon, Tae-Yub; Kim, Kyo-Han
- Polymer Bulletin, Vol. 71, Issue 4
A polymeric system for the intra-oral delivery of an anti-fungal agent
journal, September 2001
- Patel, M. P.; Cruchley, A. T.; Coleman, D. C.
- Biomaterials, Vol. 22, Issue 17
Chlorhexidine-releasing methacrylate dental composite materials
journal, December 2005
- Leung, Danny; Spratt, David A.; Pratten, Jonathan
- Biomaterials, Vol. 26, Issue 34
Controlled Release of Chlorhexidine from UDMA-TEGDMA Resin
journal, October 2006
- Anusavice, K. J.; Zhang, N. -Z.; Shen, C.
- Journal of Dental Research, Vol. 85, Issue 10
Antibacterial resin monomers based on quaternary ammonium and their benefits in restorative dentistry
journal, August 2012
- Imazato, Satoshi; Chen, Ji-hua; Ma, Sai
- Japanese Dental Science Review, Vol. 48, Issue 2
Antibacterial activity of cured dental resin incorporating the antibacterial monomer MDPB and an adhesion-promoting monomer
journal, March 1998
- Imazato, S.; Imai, T.; Russell, R. R. B.
- Journal of Biomedical Materials Research, Vol. 39, Issue 4
Silver compounds used in dentistry for caries management: A review
journal, July 2012
- Peng, J. J. -Y.; Botelho, M. G.; Matinlinna, J. P.
- Journal of Dentistry, Vol. 40, Issue 7
A New “Silver-Bullet” to treat caries in children – Nano Silver Fluoride: A randomised clinical trial
journal, August 2014
- dos Santos, Valdeci Elias; Filho, Arnoldo Vasconcelos; Ribeiro Targino, Andrea Gadelha
- Journal of Dentistry, Vol. 42, Issue 8
The antimicrobial sensitivity of Streptococcus mutans to nanoparticles of silver, zinc oxide, and gold
journal, September 2008
- Hernández-Sierra, Juan Francisco; Ruiz, Facundo; Cruz Pena, Diana Corina
- Nanomedicine: Nanotechnology, Biology and Medicine, Vol. 4, Issue 3
Antibacterial, physical and mechanical properties of flowable resin composites containing zinc oxide nanoparticles
journal, May 2013
- Tavassoli Hojati, Sara; Alaghemand, Homayoon; Hamze, Faeze
- Dental Materials, Vol. 29, Issue 5
Photocatalytic inactivation of biofilms on bioactive dental adhesives: Photocatalytic Inactivation of Biofilms
journal, July 2013
- Cai, Yanling; Strømme, Maria; Melhus, Åsa
- Journal of Biomedical Materials Research Part B: Applied Biomaterials, Vol. 102, Issue 1
Photocatalytic Antibacterial Effects Are Maintained on Resin-Based TiO2 Nanocomposites after Cessation of UV Irradiation
journal, October 2013
- Cai, Yanling; Strømme, Maria; Welch, Ken
- PLoS ONE, Vol. 8, Issue 10
Photocatalysis induces bioactivity of an organic polymer based material
journal, January 2014
- Cai, Yanling; Strømme, Maria; Zhang, Peng
- RSC Adv., Vol. 4, Issue 101
Photoelectrochemical sterilization of microbial cells by semiconductor powders
journal, August 1985
- Matsunaga, Tadashi; Tomoda, Ryozo; Nakajima, Toshiaki
- FEMS Microbiology Letters, Vol. 29, Issue 1-2, p. 211-214
Photocatalytic disinfection using titanium dioxide: spectrum and mechanism of antimicrobial activity
journal, April 2011
- Foster, Howard A.; Ditta, Iram B.; Varghese, Sajnu
- Applied Microbiology and Biotechnology, Vol. 90, Issue 6
A review on the visible light active titanium dioxide photocatalysts for environmental applications
journal, August 2012
- Pelaez, Miguel; Nolan, Nicholas T.; Pillai, Suresh C.
- Applied Catalysis B: Environmental, Vol. 125
Mechanisms of lipid peroxidation
journal, January 1985
- Girotti, Albert W.
- Journal of Free Radicals in Biology & Medicine, Vol. 1, Issue 2
Bactericidal Activity of Photocatalytic TiO2 Reaction: toward an Understanding of Its Killing Mechanism
journal, September 1999
- Maness, Pin-Ching; Smolinski, Sharon; Blake, Daniel M.
- Applied and Environmental Microbiology, Vol. 65, Issue 9
Visible-Light-Induced Bactericidal Activity of a Nitrogen-Doped Titanium Photocatalyst against Human Pathogens
journal, September 2006
- Wong, Ming-Show; Chu, Wen-Chen; Sun, Der-Shan
- Applied and Environmental Microbiology, Vol. 72, Issue 9
Solar and UVC-induced mutation in human cells and inhibition by deoxynucleosides
journal, September 1989
- Musk, P.; Campbell, R.; Staples, J.
- Mutation Research Letters, Vol. 227, Issue 1
Disinfection Kinetics and Contribution of Reactive Oxygen Species When Eliminating Bacteria with TiO2 Induced Photocatalysis
journal, January 2014
- Cai, Yanling; Strømme, Maria; Welch, Ken
- Journal of Biomaterials and Nanobiotechnology, Vol. 05, Issue 03
Visible-Light Photocatalysis in Nitrogen-Doped Titanium Oxides
journal, July 2001
- Asahi, R.
- Science, Vol. 293, Issue 5528
Origin of Photoactivity of Nitrogen-Doped Titanium Dioxide under Visible Light
journal, December 2006
- Livraghi, Stefano; Paganini, Maria Cristina; Giamello, Elio
- Journal of the American Chemical Society, Vol. 128, Issue 49
Shape-Controlled Synthesis of Highly Crystalline Titania Nanocrystals
journal, October 2009
- Dinh, Cao-Thang; Nguyen, Thanh-Dinh; Kleitz, Freddy
- ACS Nano, Vol. 3, Issue 11
Highly Active TiO 2- x N x Visible Photocatalyst Prepared by N-Doping in Et 3 N/EtOH Fluid under Supercritical Conditions
journal, April 2008
- Huo, Yuning; Bian, Zhengfeng; Zhang, Xinyu
- The Journal of Physical Chemistry C, Vol. 112, Issue 16
Real-time assessment of Streptococcus mutans biofilm metabolism on resin composite
journal, October 2016
- Esteban Florez, Fernando Luis; Hiers, Rochelle Denise; Smart, Kristin
- Dental Materials, Vol. 32, Issue 10
N-doped TiO2: Theory and experiment
journal, October 2007
- Di Valentin, Cristiana; Finazzi, Emanuele; Pacchioni, Gianfranco
- Chemical Physics, Vol. 339, Issue 1-3
Preparation of nitrogen-doped titanium dioxide with visible-light photocatalytic activity using a facile hydrothermal method
journal, July 2008
- Peng, Feng; Cai, Lingfeng; Huang, Lei
- Journal of Physics and Chemistry of Solids, Vol. 69, Issue 7
Antibacterial and antifungal activity of photoactivated ZnO nanoparticles in suspension
journal, November 2013
- Kairyte, Kristina; Kadys, Arunas; Luksiene, Zivile
- Journal of Photochemistry and Photobiology B: Biology, Vol. 128
Characterization and photoactivity of Pt/N-doped TiO2 synthesized through a sol–gel process at room temperature
journal, July 2015
- Huang, Bing-Shun; Tseng, Hui-Hsin; Su, En-Chin
- Journal of Nanoparticle Research, Vol. 17, Issue 7
Surface properties of dental polymers: measurements of contact angles, roughness and fluoride release
journal, September 2008
- Namen, Fátima; Galan Jr., João; Oliveira, José Farias de
- Materials Research, Vol. 11, Issue 3
Effect of Disinfectant Solutions on the Surface Free Energy and Wettability of Filling Material
journal, July 2011
- Prado, Maíra; de Assis, Danielle Ferreira; Gomes, Brenda P. F. A.
- Journal of Endodontics, Vol. 37, Issue 7
Photodynamic therapy for periodontal diseases: State of the art
journal, May 2005
- Meisel, Peter; Kocher, Thomas
- Journal of Photochemistry and Photobiology B: Biology, Vol. 79, Issue 2
Photodynamic Effects of Curcumin Against Cariogenic Pathogens
journal, July 2012
- Araújo, Natália Costa; Fontana, Carla Raquel; Bagnato, Vanderlei Salvador
- Photomedicine and Laser Surgery, Vol. 30, Issue 7
Influence of blue light on Streptococcus mutans re-organization in biofilm
journal, November 2012
- Chebath-Taub, Daniella; Steinberg, Doron; Featherstone, John D. B.
- Journal of Photochemistry and Photobiology B: Biology, Vol. 116
Synergic antibacterial effect between visible light and hydrogen peroxide on Streptococcus mutans
journal, March 2006
- Feuerstein, Osnat; Moreinos, Daniel; Steinberg, Doron
- Journal of Antimicrobial Chemotherapy, Vol. 57, Issue 5
Effect of Twice-Daily Blue Light Treatment on Matrix-Rich Biofilm Development
journal, July 2015
- Lins de Sousa, Denise; Araújo Lima, Ramille; Zanin, Iriana Carla
- PLOS ONE, Vol. 10, Issue 7
Works referencing / citing this record:
Fueling a Hot Debate on the Application of TiO2 Nanoparticles in Sunscreen
journal, July 2019
- Sharma, Shweta; Sharma, Rohit K.; Gaur, Kavita
- Materials, Vol. 12, Issue 14
Application of Antimicrobial Nanoparticles in Dentistry
journal, March 2019
- Song, Wenjing; Ge, Shaohua
- Molecules, Vol. 24, Issue 6
Metal‐Based Nanomaterials in Biomedical Applications: Antimicrobial Activity and Cytotoxicity Aspects
journal, March 2020
- Makvandi, Pooyan; Wang, Chen‐yu; Zare, Ehsan Nazarzadeh
- Advanced Functional Materials, Vol. 30, Issue 22
Effect of titanium dioxide nanoparticle reinforcement on flexural strength of denture base resin: A systematic review and meta-analysis
journal, November 2020
- Bangera, Madhu Keshava; Kotian, Ravindra; N., Ravishankar
- Japanese Dental Science Review, Vol. 56, Issue 1
Fueling a Hot Debate on the Application of TiO2 Nanoparticles in Sunscreen
journal, July 2019
- Sharma, Shweta; Sharma, Rohit K.; Gaur, Kavita
- Materials, Vol. 12, Issue 14
Application of Antimicrobial Nanoparticles in Dentistry
journal, March 2019
- Song, Wenjing; Ge, Shaohua
- Molecules, Vol. 24, Issue 6