Evaluating and predicting molecular mechanisms of adhesive degradation during field and accelerated aging of photovoltaic modules
Abstract
Abstract Extending photovoltaic (PV) module lifetimes beyond 30 years is a goal of significant priority. A challenge that must first be addressed, however, is the development of a predictive reliability model that captures the synergy of terrestrial stressors on module degradation, particularly at encapsulant interfaces. Using a metrology designed specifically for PV modules, a comprehensive study of the widely used ethylene vinyl acetate encapsulant was performed in which encapsulant adhesion was evaluated as a function of environmental stressors (UV exposure, temperature, and humidity) for modules aged both under accelerated lab and internationally located field conditions for months to nearly 3 decades. Mechanical and chemical characterization methods are combined with fundamental polymer reaction engineering to unravel the degradation processes active at the molecular scale that lead to encapsulant delamination. An analytical and modular model framework is put forward enabling the prediction of long‐term PV module durability, starting from fundamental principles at the molecular level and explicitly accounting for bond rupture events in the bulk encapsulant and at the encapsulant interfaces. Successful parameter tuning to adhesion data indicates a dominant occurrence of deacetylation, β ‐scission, and hydrolytic depolymerization, respectively. The model contributes to the longstanding challenge of predicting module lifetimes in any geographicmore »
- Authors:
-
- Stanford Univ., CA (United States); Exponent, Menlo Park, CA (United States)
- Stanford Univ., CA (United States); Ghent Univ. (Belgium)
- National Renewable Energy Lab. (NREL), Golden, CO (United States)
- Stanford Univ., CA (United States)
- Publication Date:
- Research Org.:
- National Renewable Energy Laboratory (NREL), Golden, CO (United States)
- Sponsoring Org.:
- USDOE Office of Energy Efficiency and Renewable Energy (EERE), Renewable Power Office. Solar Energy Technologies Office
- OSTI Identifier:
- 1466665
- Alternate Identifier(s):
- OSTI ID: 1460125
- Report Number(s):
- NREL/JA-5K00-72240
Journal ID: ISSN 1062-7995
- Grant/Contract Number:
- AC36-08GO28308; DE‐AC36‐08GO28308
- Resource Type:
- Accepted Manuscript
- Journal Name:
- Progress in Photovoltaics
- Additional Journal Information:
- Journal Volume: 26; Journal Issue: 12; Journal ID: ISSN 1062-7995
- Publisher:
- Wiley
- Country of Publication:
- United States
- Language:
- English
- Subject:
- 14 SOLAR ENERGY; 36 MATERIALS SCIENCE; adhesion; interface delamination; photovoltaic encapsulation; polymer degradation; predictive model
Citation Formats
Tracy, Jared, D'hooge, Dagmar R., Bosco, Nick, Delgado, Chris, and Dauskardt, Reinhold. Evaluating and predicting molecular mechanisms of adhesive degradation during field and accelerated aging of photovoltaic modules. United States: N. p., 2018.
Web. doi:10.1002/pip.3045.
Tracy, Jared, D'hooge, Dagmar R., Bosco, Nick, Delgado, Chris, & Dauskardt, Reinhold. Evaluating and predicting molecular mechanisms of adhesive degradation during field and accelerated aging of photovoltaic modules. United States. https://doi.org/10.1002/pip.3045
Tracy, Jared, D'hooge, Dagmar R., Bosco, Nick, Delgado, Chris, and Dauskardt, Reinhold. Fri .
"Evaluating and predicting molecular mechanisms of adhesive degradation during field and accelerated aging of photovoltaic modules". United States. https://doi.org/10.1002/pip.3045. https://www.osti.gov/servlets/purl/1466665.
@article{osti_1466665,
title = {Evaluating and predicting molecular mechanisms of adhesive degradation during field and accelerated aging of photovoltaic modules},
author = {Tracy, Jared and D'hooge, Dagmar R. and Bosco, Nick and Delgado, Chris and Dauskardt, Reinhold},
abstractNote = {Abstract Extending photovoltaic (PV) module lifetimes beyond 30 years is a goal of significant priority. A challenge that must first be addressed, however, is the development of a predictive reliability model that captures the synergy of terrestrial stressors on module degradation, particularly at encapsulant interfaces. Using a metrology designed specifically for PV modules, a comprehensive study of the widely used ethylene vinyl acetate encapsulant was performed in which encapsulant adhesion was evaluated as a function of environmental stressors (UV exposure, temperature, and humidity) for modules aged both under accelerated lab and internationally located field conditions for months to nearly 3 decades. Mechanical and chemical characterization methods are combined with fundamental polymer reaction engineering to unravel the degradation processes active at the molecular scale that lead to encapsulant delamination. An analytical and modular model framework is put forward enabling the prediction of long‐term PV module durability, starting from fundamental principles at the molecular level and explicitly accounting for bond rupture events in the bulk encapsulant and at the encapsulant interfaces. Successful parameter tuning to adhesion data indicates a dominant occurrence of deacetylation, β ‐scission, and hydrolytic depolymerization, respectively. The model contributes to the longstanding challenge of predicting module lifetimes in any geographic location while minimizing time‐consuming and costly aging studies.},
doi = {10.1002/pip.3045},
journal = {Progress in Photovoltaics},
number = 12,
volume = 26,
place = {United States},
year = {Fri Jul 13 00:00:00 EDT 2018},
month = {Fri Jul 13 00:00:00 EDT 2018}
}
Web of Science
Works referenced in this record:
Accelerated UV test methods and selection criteria for encapsulants of photovoltaic modules
conference, May 2008
- Kempe, Michael D.
- 2008 33rd IEEE Photovolatic Specialists Conference (PVSC)
Moisture transport, adhesion, and corrosion protection of PV module packaging materials
journal, October 2006
- Jorgensen, G.; Terwilliger, K.; Delcueto, J.
- Solar Energy Materials and Solar Cells, Vol. 90, Issue 16
Determining the degree of crosslinking of ethylene vinyl acetate photovoltaic module encapsulants—A comparative study
journal, September 2013
- Hirschl, Ch.; Biebl–Rydlo, M.; DeBiasio, M.
- Solar Energy Materials and Solar Cells, Vol. 116
Investigation of UV aging influences on the crystallization of ethylene-vinyl acetate copolymer via successive self-nucleation and annealing treatment
journal, December 2009
- Jin, Jing; Chen, Shuangjun; Zhang, Jun
- Journal of Polymer Research, Vol. 17, Issue 6
Potential-induced degradation in photovoltaic modules: a critical review
journal, January 2017
- Luo, Wei; Khoo, Yong Sheng; Hacke, Peter
- Energy & Environmental Science, Vol. 10, Issue 1
The thermal degradation of poly(vinyl acetate) and poly(ethylene-co-vinyl acetate), Part I: Experimental study of the degradation mechanism
journal, April 2008
- Rimez, B.; Rahier, H.; Van Assche, G.
- Polymer Degradation and Stability, Vol. 93, Issue 4
Cohesive element modeling of viscoelastic fracture: application to peel testing of polymers
journal, March 2000
- Rahulkumar, P.; Jagota, A.; Bennison, S. J.
- International Journal of Solids and Structures, Vol. 37, Issue 13
Estimating service lifetimes of a polymer encapsulant for photovoltaic modules from accelerated testing
conference, January 1996
- Czanderna, A. W.; Pern, F. J.
- Conference Record of the Twenty Fifth IEEE Photovoltaic Specialists Conference - 1996
Determination of the crystallinity of polyethylene/?-olefin copolymers by thermal analysis: Relationship of the heat of fusion of 100% polyethylene crystal and the density
journal, June 2002
- Mirabella, Francis M.; Bafna, Ayush
- Journal of Polymer Science Part B: Polymer Physics, Vol. 40, Issue 15
Degradation of thermally-cured silicone encapsulant under terrestrial UV
journal, December 2016
- Cai, Can; Miller, David C.; Tappan, Ian A.
- Solar Energy Materials and Solar Cells, Vol. 157
Aspects of the thermal oxidation of ethylene vinyl acetate copolymer
journal, May 2000
- Allen, Norman S.; Edge, Michele; Rodriguez, Miguel
- Polymer Degradation and Stability, Vol. 68, Issue 3
Multi angle laser light scattering evaluation of field exposed thermoplastic photovoltaic encapsulant materials
journal, January 2016
- Kempe, Michael D.; Miller, David C.; Wohlgemuth, John H.
- Energy Science & Engineering, Vol. 4, Issue 1
Moisture-assisted subcritical debonding of a polymer/metal interface
journal, February 2002
- Kook, Seung-Yeop; Dauskardt, Reinhold H.
- Journal of Applied Physics, Vol. 91, Issue 3
Analysis of degradation mechanisms of crystalline silicon PV modules after 12 years of operation in Southern Europe
journal, January 2011
- Sánchez-Friera, Paula; Piliougine, Michel; Peláez, Javier
- Progress in Photovoltaics: Research and Applications, Vol. 19, Issue 6
Effect of strain-dependent cohesive zone model on predictions of crack growth resistance
journal, August 1996
- Tvergaard, V.; Hutchinson, J. W.
- International Journal of Solids and Structures, Vol. 33, Issue 20-22
Adhesion and debonding kinetics of photovoltaic encapsulation in moist environments: Adhesion and debonding kinetics of photovoltaic encapsulation
journal, July 2015
- Novoa, Fernando D.; Miller, David C.; Dauskardt, Reinhold H.
- Progress in Photovoltaics: Research and Applications, Vol. 24, Issue 2
Acetic acid production and glass transition concerns with ethylene-vinyl acetate used in photovoltaic devices
journal, February 2007
- Kempe, Michael D.; Jorgensen, Gary J.; Terwilliger, Kent M.
- Solar Energy Materials and Solar Cells, Vol. 91, Issue 4
Encapsulation and backsheet adhesion metrology for photovoltaic modules: Adhesion in photovoltaic modules
journal, September 2016
- Tracy, Jared; Bosco, Nick; Novoa, Fernando
- Progress in Photovoltaics: Research and Applications, Vol. 25, Issue 1
The strength of highly elastic materials
journal, August 1967
- Lake, G. J.; Thomas, A. G.
- Proceedings of the Royal Society of London. Series A. Mathematical and Physical Sciences, Vol. 300, Issue 1460, p. 108-119
Equating damp heat testing with field failures of PV modules
conference, June 2013
- Wohlgemuth, John H.; Kempe, Michael D.
- 2013 IEEE 39th Photovoltaic Specialists Conference (PVSC)
Origin of damp-heat induced cell degradation
journal, September 2013
- Peike, C.; Hoffmann, S.; Hülsmann, P.
- Solar Energy Materials and Solar Cells, Vol. 116
Accelerated and outdoor aging effects on photovoltaic module interfacial adhesion properties
journal, September 2008
- Jorgensen, G. J.; McMahon, T. J.
- Progress in Photovoltaics: Research and Applications, Vol. 16, Issue 6
The performance of crystalline silicon photovoltaic solar modules after 22 years of continuous outdoor exposure
journal, January 2005
- Dunlop, Ewan D.; Halton, David
- Progress in Photovoltaics: Research and Applications, Vol. 14, Issue 1
Ultraviolet light test and evaluation methods for encapsulants of photovoltaic modules
journal, February 2010
- Kempe, Michael D.
- Solar Energy Materials and Solar Cells, Vol. 94, Issue 2
Defining Threshold Values of Encapsulant and Backsheet Adhesion for PV Module Reliability
journal, November 2017
- Bosco, Nick; Eafanti, Joshua; Kurtz, Sarah
- IEEE Journal of Photovoltaics, Vol. 7, Issue 6
Model-based design of the polymer microstructure: bridging the gap between polymer chemistry and engineering
journal, January 2015
- D'hooge, Dagmar R.; Van Steenberge, Paul H. M.; Derboven, Pieter
- Polymer Chemistry, Vol. 6, Issue 40
The thermo-mechanical degradation of ethylene vinyl acetate used as a solar panel adhesive and encapsulant
journal, July 2016
- Badiee, A.; Ashcroft, I. A.; Wildman, R. D.
- International Journal of Adhesion and Adhesives, Vol. 68
The results of performance measurements of field-aged crystalline silicon photovoltaic modules
journal, June 2009
- Skoczek, Artur; Sample, Tony; Dunlop, Ewan D.
- Progress in Photovoltaics: Research and Applications, Vol. 17, Issue 4
Effect of Wetting Liquids on the Strength of Adhesion of Viscoelastic Material
journal, March 1972
- Gent, A. N.; Schultz, J.
- The Journal of Adhesion, Vol. 3, Issue 4
Development and first results of the width-tapered beam method for adhesion testing of photovoltaic material systems
conference, June 2016
- Bosco, Nick; Tracy, Jared; Dauskardt, Reinhold
- 2016 IEEE 43rd Photovoltaic Specialists Conference (PVSC)
Encapsulation of PV modules using ethylene vinyl acetate copolymer as a pottant: A critical review
journal, September 1996
- Czanderna, A. W.; Pern, F. J.
- Solar Energy Materials and Solar Cells, Vol. 43, Issue 2
Compressive-shear adhesion characterization of polyvinyl-butyral and ethylene-vinyl acetate at different curing times before and after exposure to damp-heat conditions: Compressive-shear adhesion characterization of PVB and EVA
journal, September 2012
- Chapuis, Valentin; Pélisset, Ségolène; Raeis-Barnéoud, Marylène
- Progress in Photovoltaics: Research and Applications, Vol. 22, Issue 4
Encapsulant Adhesion to Surface Metallization on Photovoltaic Cells
journal, November 2017
- Tracy, Jared; Bosco, Nick; Dauskardt, Reinhold
- IEEE Journal of Photovoltaics, Vol. 7, Issue 6
Photovoltaic module performance and durability following long-term field exposure
conference, January 1999
- King, D. L.; Quintana, M. A.; Kratochvil, J. A.
- National center for photovoltaics (NCPV) 15th program review meeting, AIP Conference Proceedings
Evaluation of the aging behavior of ethylene copolymer films for solar applications under accelerated weathering conditions
journal, July 2009
- Oreski, G.; Wallner, G. M.
- Solar Energy, Vol. 83, Issue 7
Thermodynamics of Crystallization in High Polymers: Poly-(ethylene) 1
journal, July 1958
- Quinn, F. A.; Mandelkern, L.
- Journal of the American Chemical Society, Vol. 80, Issue 13
The strength of multi-scale modeling to unveil the complexity of radical polymerization
journal, July 2016
- D’hooge, Dagmar R.; Van Steenberge, Paul H. M.; Reyniers, Marie-Françoise
- Progress in Polymer Science, Vol. 58
Defining Threshold Values of Encapsulant and Backsheet Adhesion for PV Module Reliability
conference, June 2017
- Bosco, Nick; Eafanti, Joshua; Kurtz, Sarah
- 2017 IEEE 44th Photovoltaic Specialists Conference (PVSC), 2017 IEEE 44th Photovoltaic Specialist Conference (PVSC)
Encapsulant Adhesion to Surface Metallization on Photovoltaic Cells
conference, June 2017
- Tracy, Jared; Bosco, Nick; Dauskardt, Reinhold
- 2017 IEEE 44th Photovoltaic Specialists Conference (PVSC), 2017 IEEE 44th Photovoltaic Specialist Conference (PVSC)
Investigation of the photodegradation behaviors of an ethylene/vinyl acetate copolymer solar cell encapsulant and effects of antioxidants on the photostability of the material
journal, January 2007
- Ayutthaya, S. Isarankura Na; Wootthikanokkhan, J.
- Journal of Applied Polymer Science, Vol. 107, Issue 6
Outdoor weathering of PV modules — Effects of various climates and comparison with accelerated laboratory testing
conference, June 2011
- Herrmann, W.; Bogdanski, N.
- 2011 37th IEEE Photovoltaic Specialists Conference (PVSC)
Comparison of PV module performance before and after 11 and 20 years of field exposure
conference, June 2011
- Chamberlin, C. E.; Rocheleau, M. A.; Marshall, M. W.
- 2011 37th IEEE Photovoltaic Specialists Conference (PVSC)
Works referencing / citing this record:
A 3D Printable Thermal Energy Storage Crystalline Gel Using Mask-Projection Stereolithography
journal, October 2018
- Mao, Yuchen; Miyazaki, Takuya; Sakai, Kohei
- Polymers, Vol. 10, Issue 10
A 3D Printable Thermal Energy Storage Crystalline Gel Using Mask-Projection Stereolithography
journal, October 2018
- Mao, Yuchen; Miyazaki, Takuya; Sakai, Kohei
- Polymers, Vol. 10, Issue 10
Influence of Different Stabilization Systems and Multiple Ultraviolet A (UVA) Aging/Recycling Steps on Physicochemical, Mechanical, Colorimetric, and Thermal-Oxidative Properties of ABS
journal, January 2020
- Fiorio, Rudinei; Villanueva Díez, Sara; Sánchez, Alberto
- Materials, Vol. 13, Issue 1
Functional fluorinated polymer materials and preliminary self-healing behavior
journal, January 2019
- Banerjee, Sanjib; Tawade, Bhausaheb V.; Améduri, Bruno
- Polymer Chemistry, Vol. 10, Issue 16
Fluorescence imaging analysis of depth‐dependent degradation in photovoltaic laminates: insights to the failure
journal, December 2019
- Lyu, Yadong; Fairbrother, Andrew; Kim, Jae Hyun
- Progress in Photovoltaics: Research and Applications, Vol. 28, Issue 2