Microstructure and magnetic properties of melt-spun Alnico-5 alloys

doi:10.1016/j.jmmm.2015.12.092

Title: Microstructure and magnetic properties of melt-spun Alnico-5 alloys

Article Details
Other Related Research

Authors:: Löwe, Konrad ; Dürrschnabel, Michael ; Molina-Luna, Leopoldo ; Madugundo, Rajasekhar ; Frincu, Bianca ; Kleebe, Hans-Joachim ; Gutfleisch, Oliver ; Hadjipanayis, George C.

Publication Date:: 2016-06-01

Type:: Publisher's Accepted Manuscript

Journal Name:: Journal of Magnetism and Magnetic Materials

Additional Journal Information:: Journal Volume: 407; Journal Issue: C; Related Information: CHORUS Timestamp: 2018-09-15 22:52:17; Journal ID: ISSN 0304-8853

Publisher:: Elsevier

Sponsoring Org:: USDOE

Country of Publication:: Netherlands

Language:: English

OSTI Identifier:: 1359362


                    Löwe, Konrad, Dürrschnabel, Michael, Molina-Luna, Leopoldo, Madugundo, Rajasekhar, Frincu, Bianca, Kleebe, Hans-Joachim, Gutfleisch, Oliver, and Hadjipanayis, George C. Microstructure and magnetic properties of melt-spun Alnico-5 alloys.  Netherlands: N. p.,  
        Web.  doi:10.1016/j.jmmm.2015.12.092.

Copy to clipboard


                    Löwe, Konrad, Dürrschnabel, Michael, Molina-Luna, Leopoldo, Madugundo, Rajasekhar, Frincu, Bianca, Kleebe, Hans-Joachim, Gutfleisch, Oliver, & Hadjipanayis, George C. Microstructure and magnetic properties of melt-spun Alnico-5 alloys.  Netherlands.  doi:10.1016/j.jmmm.2015.12.092.

Copy to clipboard


                    Löwe, Konrad, Dürrschnabel, Michael, Molina-Luna, Leopoldo, Madugundo, Rajasekhar, Frincu, Bianca, Kleebe, Hans-Joachim, Gutfleisch, Oliver, and Hadjipanayis, George C. 2016.  
        "Microstructure and magnetic properties of melt-spun Alnico-5 alloys".  Netherlands.  
        doi:10.1016/j.jmmm.2015.12.092.

Copy to clipboard


                    
@article{osti_1359362,

  title        = {Microstructure and magnetic properties of melt-spun Alnico-5 alloys},

  author       = {Löwe, Konrad and Dürrschnabel, Michael and Molina-Luna, Leopoldo and Madugundo, Rajasekhar and Frincu, Bianca and Kleebe, Hans-Joachim and Gutfleisch, Oliver and Hadjipanayis, George C.},

  abstractNote = {},

  doi          = {10.1016/j.jmmm.2015.12.092},

  journal      = {Journal of Magnetism and Magnetic Materials},

  number       = C,

  volume       = 407,

  place        = {Netherlands},

  year         = {2016},

  month        = {6}

}

Copy to clipboard

Free Publicly Accessible Full Text
Accepted Manuscript (Publisher)
Publisher's Version of Record
10.1016/j.jmmm.2015.12.092
https://doi.org/10.1016/j.jmmm.2015.12.092

Citation Metrics
Cited by: 3works
Citation information provided by
Web of Science

Save / Share this Record
Export Metadata
- Endnote
- RIS
- Excel
- CSV
- XML
Save to My Library
Send to Email

Send to Email

Email address:

Content:

Similar Records

Similar records in DOE PAGES and OSTI.GOV collections:

Controlling the microstructure and associated magnetic properties of Ni _0.2Mn _3.2Ga _0.6 melt-spun ribbons by annealing

Journal Article Khan, Mahmud ; Alshammari, Ohud ; Balasubramanian, Balamurugan ; ... March 2017 - AIP Advances

Here we report on the structural and magnetic properties of Ni _0.2Mn _3.2Ga _0.6 melt-spun ribbons. The as-spun ribbons were found to exhibit mixed cubic phases that transform to non-cubic structure upon annealing. Additionally, an amorphous phase was found to co-exist in all ribbons. The SEM images show that minor grain formation occurs on the as-spun ribbons. However, the formation of extensive nano-grains was observed on the surfaces of the annealed ribbons. While the as-spun ribbons exhibit predominantly paramagnetic behavior, the ribbons annealed under various thermal conditions were found to be ferromagnetic with a Curie temperature of about 380 K.more »« less
Full Text Available
Controlling the microstructure and associated magnetic properties of Ni _0.2 Mn _3.2 Ga _0.6 melt-spun ribbons by annealing

Journal Article Khan, Mahmud ; Alshammari, Ohud ; Balasubramanian, Balamurugan ; ... May 2017 - AIP Advances

Full Text Available
Magnetic properties and microstructure of melt-spun Nd-Fe-Ga-B alloys

Journal Article - in OSTI.gov collection Panagiotopoulos, I. ; Murthy, A.S. ; Hadjipanayis, G.C. November 1995 - IEEE Transactions on Magnetics

The magnetic and microstructural properties of melt-spun Nd{sub 18}Fe{sub 76{minus}X}Ga{sub X}B{sub 6} alloys have been studied as a function of Ga content. Coercivities of 17 kOe were obtained in underquenched samples having a large grain size of 500 nm. Samples prepared at wheel speeds of 15--19 m/sec, as well as overquenched (40 m/sec) and subsequently annealed, gave coercivities of around 20 kOe with no significant improvement of H{sub c} upon Ga substitution. In Ga-free samples prepared by annealing highly overquenched ribbons (at 60 m/sec) only moderate coercive fields could be achieved (14 kOe). These samples had grain sizes of 70--100more »« less
Full Text Available
Effect of wheel speed on magnetic and mechanical properties of melt spun Fe-6.5 wt.% Si high silicon steel

Journal Article Ouyang, Gaoyuan ; Jensen, Brandt ; Tang, Wei ; ... May 2018 - AIP Advances

Full Text Available
Effect of TiC additions to the microstructure and magnetic properties of Nd{sub 9.5}Fe{sub 84.5}B{sub 6} melt-spun ribbons

Journal Article - in OSTI.gov collection Kramer, M.J. ; Li, C.P. ; Dennis, K.W. ; ... June 1998 - Journal of Applied Physics

Rapidly solidified samples of Nd{sub 9.5}Fe{sub 84.5}B{sub 6} with and without 3 at.{percent} TiC were prepared by melt spinning and melt extraction and then annealed in vacuum (3{times}10{sup {minus}6} Torr) at temperatures from 600 to 750{degree}C. For alloys melt spun under similar conditions, the overquenched state was achieved at wheel speeds {gt}10 m/s for the TiC added alloy while {gt}20 m/s was necessary without TiC. The overquenched samples contained a smaller fraction of {alpha}-Fe in smaller grains than the undercooled samples where Fe dendrites formed near the free surface during solidification. These Fe dendrites were not removed by annealing. Inmore »« less
Full Text Available

Access journal articles and accepted manuscripts resulting from DOE research funding

Title: Microstructure and magnetic properties of melt-spun Alnico-5 alloys

Access journal articles and accepted manuscripts
resulting from DOE research funding