Spatial distribution of crystalline corrosion products formed during corrosion of stainless steel in concrete

Serdar, Marijana; Meral, Cagla; Kunz, Martin; Bjegovic, Dubravka; Wenk, Hans-Rudolf; Monteiro, Paulo J. M.

doi:10.1016/j.cemconres.2015.02.004

Title: Spatial distribution of crystalline corrosion products formed during corrosion of stainless steel in concrete

Full Record
Other Related Research

Authors:: Serdar, Marijana; Meral, Cagla; Kunz, Martin; Bjegovic, Dubravka; Wenk, Hans-Rudolf; Monteiro, Paulo J. M.

Publication Date:: Fri May 01 00:00:00 EDT 2015

Sponsoring Org.:: USDOE Office of Science (SC), Basic Energy Sciences (BES)

OSTI Identifier:: 1355803

Grant/Contract Number:: AC02-05CH11231

Resource Type:: Publisher's Accepted Manuscript

Journal Name:: Cement and Concrete Research

Additional Journal Information:: Journal Name: Cement and Concrete Research Journal Volume: 71 Journal Issue: C; Journal ID: ISSN 0008-8846

Publisher:: Elsevier

Country of Publication:: United States

Language:: English

Citation Formats


                    Serdar, Marijana, Meral, Cagla, Kunz, Martin, Bjegovic, Dubravka, Wenk, Hans-Rudolf, and Monteiro, Paulo J. M. Spatial distribution of crystalline corrosion products formed during corrosion of stainless steel in concrete.  United States: N. p., 2015. 
Web.  doi:10.1016/j.cemconres.2015.02.004.

Copy to clipboard


                    Serdar, Marijana, Meral, Cagla, Kunz, Martin, Bjegovic, Dubravka, Wenk, Hans-Rudolf, & Monteiro, Paulo J. M. Spatial distribution of crystalline corrosion products formed during corrosion of stainless steel in concrete.  United States.  https://doi.org/10.1016/j.cemconres.2015.02.004

Copy to clipboard


                    Serdar, Marijana, Meral, Cagla, Kunz, Martin, Bjegovic, Dubravka, Wenk, Hans-Rudolf, and Monteiro, Paulo J. M. Fri .  
"Spatial distribution of crystalline corrosion products formed during corrosion of stainless steel in concrete".  United States.  https://doi.org/10.1016/j.cemconres.2015.02.004.

Copy to clipboard


                    
@article{osti_1355803,

  title        = {Spatial distribution of crystalline corrosion products formed during corrosion of stainless steel in concrete},

  author       = {Serdar, Marijana and Meral, Cagla and Kunz, Martin and Bjegovic, Dubravka and Wenk, Hans-Rudolf and Monteiro, Paulo J. M.},

  abstractNote = {},

  doi          = {10.1016/j.cemconres.2015.02.004},

  journal      = {Cement and Concrete Research},

  number       = C,

  volume       = 71,

  place        = {United States},

  year         = {Fri May 01 00:00:00 EDT 2015},

  month        = {Fri May 01 00:00:00 EDT 2015}

}

Copy to clipboard

Journal Article:

Free Publicly Available Full Text

Accepted Manuscript (Publisher)

Publisher's Version of Record
https://doi.org/10.1016/j.cemconres.2015.02.004

Other availability

Search WorldCat to find libraries that may hold this journal

Citation Metrics:

Cited by: 22 works

Citation information provided by
Web of Science

Save / Share:

Export Metadata

Save to My Library

Similar Records in DOE PAGES and OSTI.GOV collections:

Spatial distribution of crystalline corrosion products formed during corrosion of stainless steel in concrete

Journal Article Serdar, Marijana ; Meral, Cagla ; Kunz, Martin ; ... - Cement and Concrete Research

The mineralogy and spatial distribution of nano-crystalline corrosion products that form in the steel/concrete interface were characterized using synchrotron X-ray micro-diffraction (μ-XRD). Two types of low-nickel high-chromium reinforcing steels embedded into mortar and exposed to NaCl solution were investigated. Corrosion in the samples was confirmed by electrochemical impedance spectroscopy (EIS). μ-XRD revealed that goethite (α-FeOOH) and akaganeite (β-FeOOH) are the main iron oxide–hydroxides formed during the chloride-induced corrosion of stainless steel in concrete. Goethite is formed closer to the surface of the steel due to the presence of chromium in the steel, while akaganeite is formed further away from themore »« less
https://doi.org/10.1016/J.CEMCONRES.2015.02.004
THOREX PILOT PLANT CORROSION STUDIES: I. CORROSION OF TYPES 304L AND 309SCb STAINLESS STEEL DURING PRODUCTION AND DEVELOPMENT PERIODS

Technical Report English, J L

The corrosion behavior of types 304L and 309SCb stainless steel was examined during the production and first half of the development periods of Thorex pilot plant operation between December 15, 1954 and November 10, 1955. The process vessels in which corrosion data were obtained included the batch dissolver tank the feed adjustment tank the AP catch tank and the BT vapor separator. There was no significant difference between the corrosion resistance of the two alloys in any of the environments. Vapor-phase corrosion attack in some vessels was more severe than solution-phase attack in the same vessels, Dependent upon the particularmore »« less
https://doi.org/10.2172/4242119

Full Text Available
THOREX PILOT PLANT CORROSION STUDIES: II. CORROSION OF TYPES 304L, 309SCb, AND 347 STAINLESS STEEL DURING DEVELOPMENT AND PRODUCTION-DEVELOPMENT PERIODS

Technical Report English, J L

Corrosion data for types 304L, 309SCb, and 347 stainless steel were obtained in a number of process vessels in the ORNL Thorex pilot plant during the development and the production-development periods of operation occurring between December 1954 and September 1956. Stressed corrosion-test specimens were exposed in the batch dissolver tank, the feed adjustment tank, the BT vapor separator, the A-column feed tuink, and the BTC catch tank Generally, types 304L and 3O9SCb stainless steel exhibited comparable corrosion resistance in all environments examined. Most of the studies were conducted with these two alloys. Severe corrosion damage was encountered in the vapormore »« less
https://doi.org/10.2172/4200667

Full Text Available
Corrosion of stainless steel during acetate production

Journal Article Qi, J S ; Lester, G C - Corrosion

Corrosion of types 304, 304L, 316, and 316L stainless steel (SS) during the esterification of acetic acid and alcohol or glycol ether was investigated. The catalyst for this reaction, sulfuric acid or para-toluene sulfonic acid (PTSA), was shown to cause more corrosion on reactor equipment than CH{sub 3}COOH under the process conditions commonly practiced in industry. The corrosive action of the catalyst occurred only in the presence of water. Thus, for the batch processes, corrosion occurred mostly during the initial stage of esterification, where water produced by the reaction created an aqueous environment. After water was distilled off, the corrosionmore »« less
https://doi.org/10.5006/1.3292146
CORROSION OF STAINLESS STEELS BY HNO$sub 3$-HF-Al(NO$sub 3$$)$$sub 3$ MIXTURES DURING EVAPORATION OF PLUTONIUM PRODUCT STREAMS

Technical Report Arehart, T. A. ; Runion, T. C.
https://doi.org/10.2172/4375013

Full Text Available

Similar Records