Title: Calcia-magnesia-alumino-silicate (CMAS)-induced degradation and failure of air plasma sprayed yttria-stabilized zirconia thermal barrier coatings

Authors:
; ; ; ; ;
Publication Date:
Sponsoring Org.:
USDOE
OSTI Identifier:
1352941
Grant/Contract Number:  
N00014-15-1-2375; N00014-12-1-0175
Resource Type:
Publisher's Accepted Manuscript
Journal Name:
Acta Materialia
Additional Journal Information:
Journal Name: Acta Materialia Journal Volume: 105 Journal Issue: C; Journal ID: ISSN 1359-6454
Publisher:
Elsevier
Country of Publication:
United States
Language:
English

Citation Formats

Krause, Amanda R., Garces, Hector F., Dwivedi, Gopal, Ortiz, Angel L., Sampath, Sanjay, and Padture, Nitin P.. Calcia-magnesia-alumino-silicate (CMAS)-induced degradation and failure of air plasma sprayed yttria-stabilized zirconia thermal barrier coatings. United States: N. p., 2016. Web. https://doi.org/10.1016/j.actamat.2015.12.044.
Krause, Amanda R., Garces, Hector F., Dwivedi, Gopal, Ortiz, Angel L., Sampath, Sanjay, & Padture, Nitin P.. Calcia-magnesia-alumino-silicate (CMAS)-induced degradation and failure of air plasma sprayed yttria-stabilized zirconia thermal barrier coatings. United States. https://doi.org/10.1016/j.actamat.2015.12.044
Krause, Amanda R., Garces, Hector F., Dwivedi, Gopal, Ortiz, Angel L., Sampath, Sanjay, and Padture, Nitin P.. Mon . "Calcia-magnesia-alumino-silicate (CMAS)-induced degradation and failure of air plasma sprayed yttria-stabilized zirconia thermal barrier coatings". United States. https://doi.org/10.1016/j.actamat.2015.12.044.
@article{osti_1352941,
title = {Calcia-magnesia-alumino-silicate (CMAS)-induced degradation and failure of air plasma sprayed yttria-stabilized zirconia thermal barrier coatings},
author = {Krause, Amanda R. and Garces, Hector F. and Dwivedi, Gopal and Ortiz, Angel L. and Sampath, Sanjay and Padture, Nitin P.},
abstractNote = {},
doi = {10.1016/j.actamat.2015.12.044},
journal = {Acta Materialia},
number = C,
volume = 105,
place = {United States},
year = {2016},
month = {2}
}

Journal Article:
Free Publicly Available Full Text
Publisher's Version of Record
https://doi.org/10.1016/j.actamat.2015.12.044

Citation Metrics:
Cited by: 20 works
Citation information provided by
Web of Science

Save / Share:

Works referenced in this record:

A delamination mechanism for thermal barrier coatings subject to calcium–magnesium–alumino-silicate (CMAS) infiltration
journal, February 2005


Role of environment deposits and operating surface temperature in spallation of air plasma sprayed thermal barrier coatings
journal, December 1996


The Tetragonal-Monoclinic Transformation in Zirconia: Lessons Learned and Future Trends
journal, September 2009


Thermal-gradient testing of thermal barrier coatings under simultaneous attack by molten glassy deposits and its mitigation
journal, May 2010


Role of Ferroelasticity in Toughening of Zirconia Ceramics
journal, February 1998


Phase Stability of t′-Zirconia-Based Thermal Barrier Coatings: Mechanistic Insights: Phase Stability of t′-Zirconia-Based TBCs
journal, May 2011


Microstructural characterization of the interaction between 8YPSZ (EB-PVD) thermal barrier coatings and a synthetic CAS
journal, January 2014


On a ferroelastic mechanism governing the toughness of metastable tetragonal-prime ( t ′) yttria-stabilized zirconia
journal, February 2007

  • Mercer, C.; Williams, J. R.; Clarke, D. R.
  • Proceedings of the Royal Society A: Mathematical, Physical and Engineering Sciences, Vol. 463, Issue 2081
  • DOI: 10.1098/rspa.2007.1829

Air-plasma-sprayed thermal barrier coatings that are resistant to high-temperature attack by glassy deposits
journal, December 2010


Steady-state cracking in brittle substrates beneath adherent films
journal, January 1989


Novel thermal barrier coatings that are resistant to high-temperature attack by glassy deposits
journal, December 2007


Rietveld refinement guidelines
journal, February 1999

  • McCusker, L. B.; Von Dreele, R. B.; Cox, D. E.
  • Journal of Applied Crystallography, Vol. 32, Issue 1
  • DOI: 10.1107/S0021889898009856

Composition effects of thermal barrier coating ceramics on their interaction with molten Ca–Mg–Al–silicate (CMAS) glass
journal, September 2012


Thermal barrier coatings technology: critical review, progress update, remaining challenges and prospects
journal, August 2013


Turbine airfoil degradation in the persian gulf war
journal, December 1994

  • Smialek, James L.; Archer, Frances A.; Garlick, Ralph G.
  • JOM, Vol. 46, Issue 12
  • DOI: 10.1007/BF03222663

Thermal-barrier coatings for more efficient gas-turbine engines
journal, October 2012

  • Clarke, David R.; Oechsner, Matthias; Padture, Nitin P.
  • MRS Bulletin, Vol. 37, Issue 10
  • DOI: 10.1557/mrs.2012.232

Thermochemical Interaction of Thermal Barrier Coatings with Molten CaO?MgO?Al 2 O 3 ?SiO 2 (CMAS) Deposits
journal, October 2006


Environmental degradation of thermal-barrier coatings by molten deposits
journal, October 2012

  • Levi, Carlos G.; Hutchinson, John W.; Vidal-Sétif, Marie-Hélène
  • MRS Bulletin, Vol. 37, Issue 10
  • DOI: 10.1557/mrs.2012.230

2ZrO 2 ·Y 2 O 3 Thermal Barrier Coatings Resistant to Degradation by Molten CMAS: Part II, Interactions with Sand and Fly Ash
journal, September 2014

  • Krause, Amanda R.; Garces, Hector F.; Senturk, Bilge S.
  • Journal of the American Ceramic Society, Vol. 97, Issue 12
  • DOI: 10.1111/jace.13209

The mechanics of coating delamination in thermal gradients
journal, June 2007


2ZrO 2 ·Y 2 O 3 Thermal Barrier Coatings Resistant to Degradation by Molten CMAS: Part I, Optical Basicity Considerations and Processing
journal, September 2014

  • Krause, Amanda R.; Senturk, Bilge S.; Garces, Hector F.
  • Journal of the American Ceramic Society, Vol. 97, Issue 12
  • DOI: 10.1111/jace.13210

Degradation of Thermal-Barrier Coatings at Very High Temperatures
journal, October 1994


Mitigation of damage from molten fly ash to air-plasma-sprayed thermal barrier coatings
journal, September 2011

  • Gledhill, Andrew D.; Reddy, Kongara M.; Drexler, Julie M.
  • Materials Science and Engineering: A, Vol. 528, Issue 24
  • DOI: 10.1016/j.msea.2011.06.041

In situ Raman spectroscopy studies of high-temperature degradation of thermal barrier coatings by molten silicate deposits
journal, April 2014


Mechanisms of cracking and delamination within thick thermal barrier systems in aero-engines subject to calcium-magnesium-alumino-silicate (CMAS) penetration
journal, August 2008

  • Krämer, S.; Faulhaber, S.; Chambers, M.
  • Materials Science and Engineering: A, Vol. 490, Issue 1-2
  • DOI: 10.1016/j.msea.2008.01.006

Phase Evolution upon Aging of Air-Plasma Sprayed t ′-Zirconia Coatings: I-Synchrotron X-Ray Diffraction
journal, October 2012


The influence of oxides on the performance of advanced gas turbines
journal, January 2008


Jet Engine Coatings for Resisting Volcanic Ash Damage
journal, April 2011

  • Drexler, Julie M.; Gledhill, Andrew D.; Shinoda, Kentaro
  • Advanced Materials, Vol. 23, Issue 21
  • DOI: 10.1002/adma.201004783

WinPLOTR: A Windows Tool for Powder Diffraction Pattern Analysis
journal, October 2001


Thermal Barrier Coatings for Gas-Turbine Engine Applications
journal, April 2002