Bubble formation and lattice parameter changes resulting from He irradiation of defect-fluorite Gd2Zr2O7

doi:10.1016/j.actamat.2016.05.045

Title: Bubble formation and lattice parameter changes resulting from He irradiation of defect-fluorite Gd2Zr2O7

Full Record
Other Related Research

Authors:

; Patel, Maulik K.; Aguiar, Jeffery A.; Zhang, Yanwen; Crespillo, Miguel L.; Wen, Juan; Xue, Haizhou; Wang, Yongqiang; Weber, William J.

Publication Date:: 2016-08-01

Sponsoring Org.:: USDOE

OSTI Identifier:: 1323577

Grant/Contract Number:: NE0000693

Resource Type:: Publisher's Accepted Manuscript

Journal Name:: Acta Materialia

Additional Journal Information:: Journal Name: Acta Materialia Journal Volume: 115 Journal Issue: C; Journal ID: ISSN 1359-6454

Publisher:: Elsevier

Country of Publication:: United States

Language:: English

Citation Formats


                    Taylor, Caitlin A., Patel, Maulik K., Aguiar, Jeffery A., Zhang, Yanwen, Crespillo, Miguel L., Wen, Juan, Xue, Haizhou, Wang, Yongqiang, and Weber, William J. Bubble formation and lattice parameter changes resulting from He irradiation of defect-fluorite Gd2Zr2O7.  United States: N. p., 2016. 
        Web.  doi:10.1016/j.actamat.2016.05.045.

Copy to clipboard


                    Taylor, Caitlin A., Patel, Maulik K., Aguiar, Jeffery A., Zhang, Yanwen, Crespillo, Miguel L., Wen, Juan, Xue, Haizhou, Wang, Yongqiang, & Weber, William J. Bubble formation and lattice parameter changes resulting from He irradiation of defect-fluorite Gd2Zr2O7.  United States.  doi:10.1016/j.actamat.2016.05.045.

Copy to clipboard


                    Taylor, Caitlin A., Patel, Maulik K., Aguiar, Jeffery A., Zhang, Yanwen, Crespillo, Miguel L., Wen, Juan, Xue, Haizhou, Wang, Yongqiang, and Weber, William J. Mon .  
        "Bubble formation and lattice parameter changes resulting from He irradiation of defect-fluorite Gd2Zr2O7".  United States.  doi:10.1016/j.actamat.2016.05.045.

Copy to clipboard


                    
@article{osti_1323577,

  title        = {Bubble formation and lattice parameter changes resulting from He irradiation of defect-fluorite Gd2Zr2O7},

  author       = {Taylor, Caitlin A. and Patel, Maulik K. and Aguiar, Jeffery A. and Zhang, Yanwen and Crespillo, Miguel L. and Wen, Juan and Xue, Haizhou and Wang, Yongqiang and Weber, William J.},

  abstractNote = {},

  doi          = {10.1016/j.actamat.2016.05.045},

  journal      = {Acta Materialia},

  number       = C,

  volume       = 115,

  place        = {United States},

  year         = {2016},

  month        = {8}

}

Copy to clipboard

Journal Article:

Free Publicly Available Full Text

Accepted Manuscript (Publisher)

Publisher's Version of Record
DOI: 10.1016/j.actamat.2016.05.045

Other availability

Search WorldCat to find libraries that may hold this journal

Citation Metrics:

Cited by: 2 works

Citation information provided by
Web of Science

Save / Share:

Export Metadata

Save to My Library

Similar Records in DOE PAGES and OSTI.GOV collections:

Bubble Formation and Lattice Parameter Changes Resulting from He Irradiation of Defect-Fluorite Gd2Zr2O7

Journal Article Taylor, Caitlin A. ; Patel, Maulik K. ; Aguiar, Jeffery A. ; ... - Acta Materialia

Pyrochlores have long been considered as potential candidates for advanced ceramic waste-forms for the immobilization of radioactive waste nuclides. This work provides evidence that Gd2Zr2O7, often considered the most radiation tolerant pyrochlore, could be susceptible to radiation damage in the form of bubble nucleation at the highest He doses expected over geological time. Ion irradiations were utilized to experimentally simulate the radiation damage and He accumulation produced by ..alpha..-decay. Samples were pre-damaged using 7 MeV Au3+ to induce the pyrochlore to defect-fluorite phase transformation, which would occur due to ..alpha..-recoil damage within several hundred years of storage in a Gd2Zr2O7more »« less
DOI: 10.1016/j.actamat.2016.05.045
Bubble formation and lattice parameter changes resulting from He irradiation of defect-fluorite Gd₂Zr₂O₇

Journal Article Taylor, Caitlin A. ; Patel, Maulik K. ; Aguiar, Jeffery A. ; ... - Acta Materialia

We report that pyrochlores have long been considered as potential candidates for advanced ceramic waste-forms for the immobilization of radioactive waste nuclides. This work provides evidence that Gd₂Zr₂O₇, often considered the most radiation tolerant pyrochlore, could be susceptible to radiation damage in the form of bubble nucleation at the highest He doses expected over geological time. Ion irradiations were utilized to experimentally simulate the radiation damage and He accumulation produced by α-decay. Samples were pre-damaged using 7 MeV Au³⁺ to induce the pyrochlore to defect-fluorite phase transformation, which would occur due to α-recoil damage within several hundred years of storagemore »« less
DOI: 10.1016/j.actamat.2016.05.045
LATTICE PARAMETER CHANGE BY POINT DEFECTS IN IRRADIATED ALUMINUM.

Journal Article Peisl, H ; Waidelich, W - pp 489-95 of Interaction of Radiation with Solids. Bishay, Adli (ed.). New York, Plenum Press, 1967.
DOI: 10.1007/978-1-4899-5549-4_31
Lattice parameter changes and point defect reactions in low temperature electron irradiated AlAs

Journal Article Gaber, A ; Zillgen, H ; Ehrhart, P ; ... - Journal of Applied Physics

X-ray diffraction was employed to investigate damage accumulation and the subsequent thermally activated annealing reactions in AlAs layers on GaAs substrates. Irradiations were performed at 4.6 K with 2.5 MeV electrons up to a total dose of 2{times}10{sup 19} electrons/cm{sup 2}. The irradiation-induced increase of the lattice parameter amounts to about half of the changes observed in the GaAs substrates. There is a major annealing step near room temperature, a rather continuous annealing up to 500 K, and a final recovery stage between 700 and 900 K. The observations are discussed in relation to the resistance of AlAs against amorphizationmore »« less
DOI: 10.1063/1.366302
Combined effects of radiation damage and He accumulation on bubble nucleation in Gd₂Ti₂O₇

Journal Article Taylor, Caitlin A. ; Patel, Maulik K. ; Aguiar, Jeffery A. ; ... - Journal of Nuclear Materials

Pyrochlores have long been considered as host phases for long-term immobilization of radioactive waste nuclides that would undergo α-decay for hundreds of thousands of years. This work utilizes ion-beam irradiations to examine the combined effects of radiation damage and He accumulation on bubble formation in Gd₂Ti₂O₇ over relevant waste-form timescales. Helium bubbles are not observed in pre-damaged Gd₂Ti₂O₇ implanted with 2 × 10¹⁶ He/cm², even after post-implantation irradiations with 7 MeV Au³⁺ at 300, 500, and 700 K. However, He bubbles with average diameters of 1.5 nm and 2.1 nm are observed in pre-damaged (amorphous) Gd₂Ti₂O₇ and pristine Gd₂Ti₂O₇, respectively,more »« less
Cited by 2
DOI: 10.1016/j.jnucmat.2016.07.043

Full Text Available

Similar Records