High critical current density Bi 2 Sr 2 CaCu 2 O x /Ag wire containing oxide precursor synthesized from nano-oxides

Zhang, Yun; Johnson, Stephen; Naderi, Golsa; Chaubal, Manasi; Hunt, Andrew; Schwartz, Justin

doi:10.1088/0953-2048/29/9/095012

Title: High critical current density Bi ₂ Sr ₂ CaCu ₂ O _x /Ag wire containing oxide precursor synthesized from nano-oxides

Full Record
Other Related Research

Authors:: Zhang, Yun; Johnson, Stephen; Naderi, Golsa; Chaubal, Manasi; Hunt, Andrew; Schwartz, Justin

Publication Date:: Mon Aug 08 00:00:00 EDT 2016

Sponsoring Org.:: USDOE

OSTI Identifier:: 1286295

Grant/Contract Number:: SC0009705

Resource Type:: Publisher's Accepted Manuscript

Journal Name:: Superconductor Science and Technology

Additional Journal Information:: Journal Name: Superconductor Science and Technology Journal Volume: 29 Journal Issue: 9; Journal ID: ISSN 0953-2048

Publisher:: IOP Publishing

Country of Publication:: United Kingdom

Language:: English

Citation Formats


                    Zhang, Yun, Johnson, Stephen, Naderi, Golsa, Chaubal, Manasi, Hunt, Andrew, and Schwartz, Justin. High critical current density Bi 2 Sr 2 CaCu 2 O x /Ag wire containing oxide precursor synthesized from nano-oxides.  United Kingdom: N. p., 2016. 
Web.  doi:10.1088/0953-2048/29/9/095012.

Copy to clipboard


                    Zhang, Yun, Johnson, Stephen, Naderi, Golsa, Chaubal, Manasi, Hunt, Andrew, & Schwartz, Justin. High critical current density Bi 2 Sr 2 CaCu 2 O x /Ag wire containing oxide precursor synthesized from nano-oxides.  United Kingdom.  https://doi.org/10.1088/0953-2048/29/9/095012

Copy to clipboard


                    Zhang, Yun, Johnson, Stephen, Naderi, Golsa, Chaubal, Manasi, Hunt, Andrew, and Schwartz, Justin. Mon .  
"High critical current density Bi 2 Sr 2 CaCu 2 O x /Ag wire containing oxide precursor synthesized from nano-oxides".  United Kingdom.  https://doi.org/10.1088/0953-2048/29/9/095012.

Copy to clipboard


                    
@article{osti_1286295,

  title        = {High critical current density Bi 2 Sr 2 CaCu 2 O x /Ag wire containing oxide precursor synthesized from nano-oxides},

  author       = {Zhang, Yun and Johnson, Stephen and Naderi, Golsa and Chaubal, Manasi and Hunt, Andrew and Schwartz, Justin},

  abstractNote = {},

  doi          = {10.1088/0953-2048/29/9/095012},

  journal      = {Superconductor Science and Technology},

  number       = 9,

  volume       = 29,

  place        = {United Kingdom},

  year         = {Mon Aug 08 00:00:00 EDT 2016},

  month        = {Mon Aug 08 00:00:00 EDT 2016}

}

Copy to clipboard

Journal Article:

Free Publicly Available Full Text

Accepted Manuscript (Publisher)

Publisher's Version of Record
https://doi.org/10.1088/0953-2048/29/9/095012

Other availability

Search WorldCat to find libraries that may hold this journal

Citation Metrics:

Cited by: 56 works

Citation information provided by
Web of Science

Save / Share:

Export Metadata

Save to My Library

Similar Records in DOE PAGES and OSTI.GOV collections:

Dependence of critical current density on filament diameter in round multifilament Ag-sheathed Bi[sub 2]Sr[sub 2]CaCu[sub 2]O[sub [ital x]] wires processed in O[sub 2]

Journal Article Motowidlo, L R ; Galinski, G ; Ozeryansky, G ; ... - Applied Physics Letters; (United States)

Ag-sheathed Bi[sub 2]Sr[sub 2]CaCu[sub 2]O[sub [ital x]] round wires having 37 and 259 filaments, with filament diameters ranging from 11 to 100 [mu]m, were fabricated by the oxide-powder-in-tube method. They were heat treated using step-solidification melt processing in air and pure O[sub 2]. The transport critical current density was highest in wires processed in pure O[sub 2]. It increased with decreasing filament diameter and was highest [165 000 A/cm[sup 2] (4.2 K, O T)] in wires with 11 [mu]m filaments processed in O[sub 2].
https://doi.org/10.1063/1.112550
Understanding the densification process of Bi ₂ Sr ₂ CaCu ₂ O _x round wires with overpressure processing and its effect on critical current density

Journal Article Matras, M. R. ; Jiang, J. ; Larbalestier, D. C. ; ... - Superconductor Science and Technology

Not provided.
https://doi.org/10.1088/0953-2048/29/10/105005
Understanding the densification process of Bi ₂ Sr ₂ CaCu ₂ O _x round wires with overpressure processing and its effect on critical current density

Journal Article Matras, M. R. ; Jiang, J. ; Larbalestier, D. C. ; ... - Superconductor Science and Technology
Cited by 16
https://doi.org/10.1088/0953-2048/29/10/105005
High-field critical current densities in Bi sub 2 Sr sub 2 Ca sub 1 Cu sub 2 O sub 8+ x /Ag wires

Journal Article Heine, K ; Tenbrink, J ; Thoner, M - Applied Physics Letters; (USA)

Bi{sub 2}Sr{sub 2}Ca{sub 1}Cu{sub 2}O{sub 8+{ital x}}/Ag wires have been produced by using the powder in tube'' method and an appropriate annealing procedure. At 77 K these wires yield critical current densities up to 1.2{times}10{sup 3} A/cm{sup 2} in zero magnetic field. Using ac susceptibility measurements it is shown that flux creep is limiting the critical current density at temperatures above {similar to}20 K. At lower temperatures flux creep becomes insignificant. At 4.2 K critical current densities up to 5.5{times}10{sup 4} A/cm{sup 2} in zero magnetic field and up to 1.5{times}10{sup 4} A/cm{sup 2} in a field of 26 Tmore »« less
https://doi.org/10.1063/1.102295
Round multifilamentary high T_c Bi₂Sr₂CaCu₂O_x/Ag superconducting wires for high field magnets. Phase I Final Report

Technical Report Sengupta, Suvankar ; Revur, Ramachandra R ; Kopulwar, Utkarsh ; ...

The overall objective of the Small Business Research Program is to develop a reliable high quality Bi-2212 powder suitable for demonstration scale (> 1km lengths) multifilamentary round wires for magnets with fields above 15 T. For heat treating long length of wires, cables and magnets (or coils), the processing window needs to be increased. In an attempt to increase J_E and the processing heat treatment window of multifilamentary Bi-2212/Ag wires the impact of secondary phase (AEC) is investigated. During Phase I, the primary emphasis was given to produce powders with well dispersed (14,24)AEC particles. Two approaches were investigated. Optimization ofmore »« less

Similar Records

Title: High critical current density Bi 2 Sr 2 CaCu 2 O x /Ag wire containing oxide precursor synthesized from nano-oxides

Citation Formats

Title: High critical current density Bi ₂ Sr ₂ CaCu ₂ O _x /Ag wire containing oxide precursor synthesized from nano-oxides