Effects of laser shock peening on SCC behavior of Alloy 600 in tetrathionate solution

Telang, Abhishek; Gill, Amrinder S.; Teysseyre, Sebastien; Mannava, Seetha R.; Qian, Dong; Vasudevan, Vijay K.

doi:10.1016/j.corsci.2014.10.045

Title: Effects of laser shock peening on SCC behavior of Alloy 600 in tetrathionate solution

Full Record
Other Related Research

Authors:: Telang, Abhishek; Gill, Amrinder S.; Teysseyre, Sebastien; Mannava, Seetha R.; Qian, Dong; Vasudevan, Vijay K.

Publication Date:: Thu Jan 01 00:00:00 EST 2015

Sponsoring Org.:: USDOE

OSTI Identifier:: 1253220

Resource Type:: Publisher's Accepted Manuscript

Journal Name:: Corrosion Science

Additional Journal Information:: Journal Name: Corrosion Science Journal Volume: 90 Journal Issue: C; Journal ID: ISSN 0010-938X

Publisher:: Elsevier

Country of Publication:: United Kingdom

Language:: English

Citation Formats


                    Telang, Abhishek, Gill, Amrinder S., Teysseyre, Sebastien, Mannava, Seetha R., Qian, Dong, and Vasudevan, Vijay K. Effects of laser shock peening on SCC behavior of Alloy 600 in tetrathionate solution.  United Kingdom: N. p., 2015. 
Web.  doi:10.1016/j.corsci.2014.10.045.

Copy to clipboard


                    Telang, Abhishek, Gill, Amrinder S., Teysseyre, Sebastien, Mannava, Seetha R., Qian, Dong, & Vasudevan, Vijay K. Effects of laser shock peening on SCC behavior of Alloy 600 in tetrathionate solution.  United Kingdom.  https://doi.org/10.1016/j.corsci.2014.10.045

Copy to clipboard


                    Telang, Abhishek, Gill, Amrinder S., Teysseyre, Sebastien, Mannava, Seetha R., Qian, Dong, and Vasudevan, Vijay K. Thu .  
"Effects of laser shock peening on SCC behavior of Alloy 600 in tetrathionate solution".  United Kingdom.  https://doi.org/10.1016/j.corsci.2014.10.045.

Copy to clipboard


                    
@article{osti_1253220,

  title        = {Effects of laser shock peening on SCC behavior of Alloy 600 in tetrathionate solution},

  author       = {Telang, Abhishek and Gill, Amrinder S. and Teysseyre, Sebastien and Mannava, Seetha R. and Qian, Dong and Vasudevan, Vijay K.},

  abstractNote = {},

  doi          = {10.1016/j.corsci.2014.10.045},

  journal      = {Corrosion Science},

  number       = C,

  volume       = 90,

  place        = {United Kingdom},

  year         = {Thu Jan 01 00:00:00 EST 2015},

  month        = {Thu Jan 01 00:00:00 EST 2015}

}

Copy to clipboard

Journal Article:

Free Publicly Available Full Text

Accepted Manuscript (Publisher)

Publisher's Version of Record
https://doi.org/10.1016/j.corsci.2014.10.045

Other availability

Search WorldCat to find libraries that may hold this journal

Citation Metrics:

Cited by: 47 works

Citation information provided by
Web of Science

Save / Share:

Export Metadata

Save to My Library

Similar Records in DOE PAGES and OSTI.GOV collections:

EFFECTS OF LASER SHOCK PEENING ON SCC BEHAVIOR OF ALLOY 600

Conference Telang, Abhishek ; Gill, Amrinder ; Mannava, S. R. ; ...

In this study, the effects of laser shock peening (LSP) on stress corrosion cracking (SCC) behavior of Alloy 600 in tetrathionate solution were investigated. The degree of sensitization was quantified using double loop electrochemical potentiokinetic reactivation (DLEPR) tests. The sensitized Alloy 600 was demonstrated to be susceptible to intergranular SCC in tetrathionate solution. Following LSP, residual stresses and the amount of plastic strain introduced in Alloy 600 were characterized. The effects of LSP on SCC susceptibility of Alloy 600 in tetrathionate solution were evaluated by slow strain rate tests and constant load tests. Results indicate a significant increase in resistancemore »« less
Full Text Available
The effect of shot peening on transition SCC of Alloy 600 steam generator tubing

Conference Vaccaro, F P ; Miglin, B P ; Monter, J V ; ...

Electrochemical caustic testing demonstrated shot peening to be an effective remedial measure for primary side transition stress corrosion cracking of mill-annealed Alloy 600 steam generator tubing. Dye penetrant inspection and extensive metallographic examinations failed to detect any evidence of crack initiation on the shot peened ID surfaces of 17 transitions roller expanded to between 2% and 6% wall thinning and tested for at least 15 days. Only three small cracks (0.003'' deep or 6% throughwall) were observed in the roller expanded region of one transition in a tube specimen severely deformed to 11% wall thinning. In contrast, all but twomore »« less
Effects of shot peening on corrosion and stress corrosion cracking behaviors of sensitized Alloy 600 in thiosulfate solution

Journal Article Tsai, W T ; Chang, C S ; Lee, J T - Corrosion (Houston); (United States)

Effects of shot peening on the corrosion and stress corrosion cracking (SCC) behaviors of sensitized alloy 600 (UNSN06600) were studied. Electrochemical potentiokinetic reactivation (EPR) tests in 0.01 M sulfuric acid (H[sub 2]SO[sub 4]) + 0.001 M potassium thiocyanate (KSCN) solution and immersion tests in boiling 25% nitric acid (HNO[sub 3]) solution were used to evaluate the effect of heat treatment on the degree of sensitization of alloy 600. Potentiodynamic polarization tests in 0.01 M sodium thiosulfate (Na[sub 2]S[sub 2]O[sub 3]) solution at 95 C revealed shot peening increased the anodic current density (CD) of the alloy. However, SCC tests usingmore »« less
https://doi.org/10.5006/1.3293507
Study of the IGA/SCC behavior of Alloy 600 and 690 in high temperature solutions

Book Tsujikawa, S ; Yashima, S ; Ohnishi, K ; ...

IGA/SCC of Alloy 600 steam generator (SG) tubes in the secondary side has been recognized as a matter of great concern for PWRs. IGA/SCC behavior of Alloy 600 and 690 in high temperature solutions were studied using CERT method under potentiostatic conditions. The IGA/SCC susceptible regions were investigated as the function of pH and electrode potential. To understand the cause of IGA/SCC, the electrochemical measurements and surface film analysis were also performed in acidic and alkaline solutions. To verify the results of CERT test, the long term model boiler tests were also carried out. Thermally treated Alloy 690 showed highermore »« less
Study of IGA/SCC behavior of alloy 600 and 690 SG tubing materials in high temperature solutions

Book Tsujikawa, S ; Yashima, S ; Hattori, T ; ...

Intergranular attack/stress corrosion cracking (IGA/SCC) of Alloy 600 Steam Generator (SG) tubes in the secondary side has been recognized as a matter of great concern for PWRs. Here, IGA/SCC behavior of Alloy 600 and 690 in high temperature solutions was studied using constant extension rate testing (CERT) method under potentiostatic conditions. The IGA/SCC susceptible regions were investigated as a function of pH and electrode potential. The IGA/SCC resistance of SG tubing materials were ranked as, MA600 = TT600 {much_lt} TT690 in acidic solutions, and MA600 < TT600 < TT690 in alkaline solutions. TT690 showed higher corrosion resistance than MA600 andmore »« less

Similar Records