Solid solubility, phase transitions, thermal expansion, and compressibility in Sc1−Al F3

Morelock, Cody R.; Gallington, Leighanne C.; Wilkinson, Angus P.

doi:10.1016/j.jssc.2014.11.007

Title: Solid solubility, phase transitions, thermal expansion, and compressibility in Sc1−Al F3

Full Record
Other Related Research

Authors:: Morelock, Cody R.; Gallington, Leighanne C.; Wilkinson, Angus P.

Publication Date:: Sun Feb 01 00:00:00 EST 2015

Sponsoring Org.:: USDOE Office of Science (SC), Basic Energy Sciences (BES)

OSTI Identifier:: 1246686

Grant/Contract Number:: AC02-06CH11357

Resource Type:: Publisher's Accepted Manuscript

Journal Name:: Journal of Solid State Chemistry

Additional Journal Information:: Journal Name: Journal of Solid State Chemistry Journal Volume: 222 Journal Issue: C; Journal ID: ISSN 0022-4596

Publisher:: Elsevier

Country of Publication:: United States

Language:: English

Citation Formats


                    Morelock, Cody R., Gallington, Leighanne C., and Wilkinson, Angus P. Solid solubility, phase transitions, thermal expansion, and compressibility in Sc1−Al F3.  United States: N. p., 2015. 
Web.  doi:10.1016/j.jssc.2014.11.007.

Copy to clipboard


                    Morelock, Cody R., Gallington, Leighanne C., & Wilkinson, Angus P. Solid solubility, phase transitions, thermal expansion, and compressibility in Sc1−Al F3.  United States.  https://doi.org/10.1016/j.jssc.2014.11.007

Copy to clipboard


                    Morelock, Cody R., Gallington, Leighanne C., and Wilkinson, Angus P. Sun .  
"Solid solubility, phase transitions, thermal expansion, and compressibility in Sc1−Al F3".  United States.  https://doi.org/10.1016/j.jssc.2014.11.007.

Copy to clipboard


                    
@article{osti_1246686,

  title        = {Solid solubility, phase transitions, thermal expansion, and compressibility in Sc1−Al F3},

  author       = {Morelock, Cody R. and Gallington, Leighanne C. and Wilkinson, Angus P.},

  abstractNote = {},

  doi          = {10.1016/j.jssc.2014.11.007},

  journal      = {Journal of Solid State Chemistry},

  number       = C,

  volume       = 222,

  place        = {United States},

  year         = {Sun Feb 01 00:00:00 EST 2015},

  month        = {Sun Feb 01 00:00:00 EST 2015}

}

Copy to clipboard

Journal Article:

Free Publicly Available Full Text

Accepted Manuscript (Publisher)

Publisher's Version of Record
https://doi.org/10.1016/j.jssc.2014.11.007

Other availability

Search WorldCat to find libraries that may hold this journal

Citation Metrics:

Cited by: 46 works

Citation information provided by
Web of Science

Save / Share:

Export Metadata

Save to My Library

Similar Records in DOE PAGES and OSTI.GOV collections:

Solid solubility, phase transitions, thermal expansion, and compressibility in Sc{sub 1−x}Al{sub x}F{sub 3}

Journal Article Morelock, Cody R. ; Gallington, Leighanne C. ; Wilkinson, Angus P., E-mail: angus.wilkinson@chemistry.gatech.edu ; ... - Journal of Solid State Chemistry

With the goal of thermal expansion control, the synthesis and properties of Sc{sub 1−x}Al{sub x}F{sub 3} were investigated. The solubility limit of AlF{sub 3} in ScF{sub 3} at ∼1340 K is ∼50%. Solid solutions (x≤0.50) were characterized by synchrotron powder diffraction at ambient pressure between 100 and 900 K and at pressures <0.414 GPa while heating from 298 to 523 K. A phase transition from cubic to rhombohedral is observed. The transition temperature increases smoothly with Al{sup 3+} content, approaching 500 K at the solid solubility limit, and also upon compression at fixed Al{sup 3+} content. The slope of themore »« less
https://doi.org/10.1016/J.JSSC.2014.11.007
Solid solubility, phase transitions, thermal expansion, and compressibility in Sc[subscript 1;#8722;x]A[subscript x]F[subscript 3]

Journal Article Morelock, Cody R. ; Gallington, Leighanne C. ; Wilkinson, Angus P. - J. Solid State Chem.
https://doi.org/10.1016/j.jssc.2014.11.007
Internal stress and solid solubility effects on the thermal expansivity of Al-Si eutectic alloys

Conference Hahn, T A ; Armstrong, R W - Int. J. Thermophys.; (United States)

Thermal expansion measurements are reported for a number of as-cast Al-Si eutectic alloys including a Sr-modified alloy which gives nearly spherical Si particles. The measurements were obtained by heating and cooling over repeated temperature cycles between room temperature and 500/degree/C. In general, lower expansivity values were measured on the cooling cycle as compared with the heating cycle, resulting in a net positive permanent deformation at room temperature. Analytical solutions are described for the thermal expansivity of a concentric-spheres model for a Si particle contained within an Al matrix. The effect of plastic flow in the Al is included. Overall, themore »« less
Thin film combinatorial sputtering of Al-Ce alloys: Investigating the phase separation of as-deposited solid solutions and determining the coefficient of thermal expansion

Journal Article Emery, Reece ; Rios, Orlando R. ; Thompson, Michael J. ; ... - Journal of Alloys and Compounds

Al_xCe_100–x thin films with a composition range of ~75.0 < x < 99.5 at% (36.5 < x < 97.5 wt%) were synthesized via combinatorial co-sputtering from an Al and an Al₅₀Ce₅₀ target. The crystal structure, phase fraction, film morphology, electrical resistivity, and temperature-dependent coefficients of thermal expansion (CTE) are all correlated to the Al_xCe_100–x composition. The as-deposited films form a metastable solid-solution, and annealing leads to the formation of the thermodynamically stable two-phase system of Al and the α-Al₁₁Ce₃ intermetallic. Temperature dependent x-ray diffraction (XRD) reveals that the two phases expand independently of one another, and the thin film Almore »« less
https://doi.org/10.1016/j.jallcom.2022.165271

Full Text Available
Thermal expansion in the garnet-type solid electrolyte (Li 7 - x Al x /3 )La 3 Zr 2 O 12 as a function of Al content

Journal Article Hubaud, Aude A. ; Schroeder, David J. ; Ingram, Brian J. ; ... - Journal of Alloys and Compounds

The thermal expansion (TE) coefficients of the lithium-stable lithium-ion conducting garnet lithium lanthanum zirconium oxide (LLZ) and the effect of aluminum substitution were measured from room temperature up to 700 °C by a synchrotron-based X-ray diffraction. The typical TE value measured for the most reported composition (LLZ doped with 0.3 wt.% or 0.093 mol% aluminum) was 15.498 × 10-6 K-1, which is approximately twice the value reported for other garnet-type structures. As the Al(III) concentration has been observed to strongly affect the structure observed and the ionic conductivity, we also assessed its role on thermal expansion and noted only amore »« less
https://doi.org/10.1016/j.jallcom.2015.05.067

Similar Records