In situ investigation of high humidity stress corrosion cracking of 7075 aluminum alloy by three-dimensional (3D) X-ray synchrotron tomography
Abstract
In situ X-ray synchrotron tomography was used to investigate the stress corrosion cracking behavior of under-aged Al–Zn–Mg–Cu alloy in moisture. The discontinuous surface cracks (crack jumps) mentioned in the literature are actually a single continuous and tortuous crack when observed in three dimension (3D). Contrary to 2D measurements made at the surface which suggest non-uniform crack growth rates, 3D measurements of the crack length led to a much more accurate measurement of crack growth rates.
- Authors:
-
- Arizona State University, Tempe, AZ (United States). Materials Science and Engineering.
- Argonne National Lab. (ANL), Argonne, IL (United States). Advanced Photon Source
- Publication Date:
- Research Org.:
- Argonne National Laboratory (ANL), Argonne, IL (United States). Advanced Photon Source (APS)
- Sponsoring Org.:
- USDOE
- OSTI Identifier:
- 1221416
- Grant/Contract Number:
- AC02-06CH11357
- Resource Type:
- Accepted Manuscript
- Journal Name:
- Materials Research Letters
- Additional Journal Information:
- Journal Volume: 2; Journal Issue: 4; Journal ID: ISSN 2166-3831
- Publisher:
- Taylor and Francis
- Country of Publication:
- United States
- Language:
- English
- Subject:
- 36 MATERIALS SCIENCE; stress corrosion cracking; X-ray tomography; moisture; aluminum alloys
Citation Formats
Singh, S. S., Williams, J. J., Lin, M. F., Xiao, X., De Carlo, F., and Chawla, N. In situ investigation of high humidity stress corrosion cracking of 7075 aluminum alloy by three-dimensional (3D) X-ray synchrotron tomography. United States: N. p., 2014.
Web. doi:10.1080/21663831.2014.918907.
Singh, S. S., Williams, J. J., Lin, M. F., Xiao, X., De Carlo, F., & Chawla, N. In situ investigation of high humidity stress corrosion cracking of 7075 aluminum alloy by three-dimensional (3D) X-ray synchrotron tomography. United States. https://doi.org/10.1080/21663831.2014.918907
Singh, S. S., Williams, J. J., Lin, M. F., Xiao, X., De Carlo, F., and Chawla, N. Wed .
"In situ investigation of high humidity stress corrosion cracking of 7075 aluminum alloy by three-dimensional (3D) X-ray synchrotron tomography". United States. https://doi.org/10.1080/21663831.2014.918907. https://www.osti.gov/servlets/purl/1221416.
@article{osti_1221416,
title = {In situ investigation of high humidity stress corrosion cracking of 7075 aluminum alloy by three-dimensional (3D) X-ray synchrotron tomography},
author = {Singh, S. S. and Williams, J. J. and Lin, M. F. and Xiao, X. and De Carlo, F. and Chawla, N.},
abstractNote = {In situ X-ray synchrotron tomography was used to investigate the stress corrosion cracking behavior of under-aged Al–Zn–Mg–Cu alloy in moisture. The discontinuous surface cracks (crack jumps) mentioned in the literature are actually a single continuous and tortuous crack when observed in three dimension (3D). Contrary to 2D measurements made at the surface which suggest non-uniform crack growth rates, 3D measurements of the crack length led to a much more accurate measurement of crack growth rates.},
doi = {10.1080/21663831.2014.918907},
journal = {Materials Research Letters},
number = 4,
volume = 2,
place = {United States},
year = {Wed May 14 00:00:00 EDT 2014},
month = {Wed May 14 00:00:00 EDT 2014}
}
Free Publicly Available Full Text
Publisher's Version of Record
Other availability
Cited by: 34 works
Citation information provided by
Web of Science
Web of Science
Save to My Library
You must Sign In or Create an Account in order to save documents to your library.
Works referenced in this record:
Application of modern aluminum alloys to aircraft
journal, January 1996
- Starke, E. A.; Staley, J. T.
- Progress in Aerospace Sciences, Vol. 32, Issue 2-3
Stress corrosion cracking of aluminum alloys
journal, April 1975
- Speidel, Markus O.
- Metallurgical Transactions A, Vol. 6, Issue 4
Crack Propagation During Sustained-Load Cracking of Al-Zn-Mg-Cu Aluminum Alloys Exposed to Moist Air or Distilled Water
journal, September 2011
- Holroyd, N. J. Henry; Scamans, G. M.
- Metallurgical and Materials Transactions A, Vol. 42, Issue 13
The Postulated Mechanisms for Stress Corrosion Cracking of Aluminum Alloys: A Review of the Literature 1980-1989
journal, February 1991
- Burleigh, T. D.
- CORROSION, Vol. 47, Issue 2
Effect of Loading History on Stress Corrosion Cracking of 7075-T651 Aluminum Alloy in Saline Aqueous Environment
journal, November 2010
- Zhang, Jixi; Kalnaus, Sergiy; Behrooz, Majid
- Metallurgical and Materials Transactions A, Vol. 42, Issue 2
SKFM observation of SCC on SUS304 stainless steel
journal, January 2007
- Masuda, Hiroyuki
- Corrosion Science, Vol. 49, Issue 1
Discontinuous surface cracks during stress corrosion cracking of stainless steel single crystal
journal, November 2011
- Qiao, L. J.; Gao, K. W.; Volinsky, Alex A.
- Corrosion Science, Vol. 53, Issue 11
Incubation effects in precracked stress corrosion specimens from Al-Zn-Mg-Cu alloy 7075
journal, January 1979
- Dorward, R. C.; Hasse, K. R.
- Corrosion Science, Vol. 19, Issue 2
Comparison of SCC Thresholds and Environmentally Assisted Cracking in 7050-T7451 Aluminum Plate
journal, March 2012
- Arnold, Eric M.; Schubbe, Joel J.; Moran, Patrick J.
- Journal of Materials Engineering and Performance, Vol. 21, Issue 11
Characterization of Damage Evolution in SiC Particle Reinforced Al Alloy Matrix Composites by In-Situ X-Ray Synchrotron Tomography
journal, May 2011
- Williams, J. J.; Chapman, N. C.; Jakkali, V.
- Metallurgical and Materials Transactions A, Vol. 42, Issue 10
Understanding fatigue crack growth in aluminum alloys by in situ X-ray synchrotron tomography
journal, December 2013
- Williams, J. J.; Yazzie, K. E.; Padilla, E.
- International Journal of Fatigue, Vol. 57
On the Correlation Between Fatigue Striation Spacing and Crack Growth Rate: A Three-Dimensional (3-D) X-ray Synchrotron Tomography Study
journal, November 2011
- Williams, Jason J.; Yazzie, Kyle E.; Connor Phillips, N.
- Metallurgical and Materials Transactions A, Vol. 42, Issue 13
In Situ Three Dimentional (3D) X-Ray Synchrotron Tomography of Corrosion Fatigue in Al7075 Alloy
book, October 2012
- Singh, Sudhanshu S.; Williams, Jason J.; Xiao, X.
- Fatigue of Materials II: Advances and Emergences in Understanding
X-ray microtomographic observation of intergranular stress corrosion cracking in sensitised austenitic stainless steel
journal, September 2006
- Babout, L.; Marrow, T. J.; Engelberg, D.
- Materials Science and Technology, Vol. 22, Issue 9
Three dimensional observations and modelling of intergranular stress corrosion cracking in austenitic stainless steel
journal, June 2006
- Marrow, T. J.; Babout, L.; Jivkov, A. P.
- Journal of Nuclear Materials, Vol. 352, Issue 1-3
Diffraction contrast tomography for the study of polycrystalline stainless steel microstructures and stress corrosion cracking
journal, January 2011
- King, A.; Ludwig, W.; Engelberg, D.
- Revue de Métallurgie, Vol. 108, Issue 1
Damage evolution in SiC particle reinforced Al alloy matrix composites by X-ray synchrotron tomography
journal, October 2010
- Williams, J. J.; Flom, Z.; Amell, A. A.
- Acta Materialia, Vol. 58, Issue 18
Elastic-plastic analysis of edge-notched panels subjected to fixed grip loading
journal, January 1991
- Ahmad, Jalees; Papaspyropoulos, Victoria; Hopper, Allen T.
- Engineering Fracture Mechanics, Vol. 38, Issue 4-5
Works referencing / citing this record:
Initiation and short crack growth behaviour of environmentally induced cracks in AA5083 H131 investigated across time and length scales
journal, September 2019
- Gudla, Visweswara C.; Garner, Alistair; Storm, Malte
- Corrosion Reviews, Vol. 37, Issue 5