Perovskites of type Ba/sub 8/Bsup(II)B/sub 2/sup(III)vacantU/sub 4/sup(VI)O/sub 24/ show polymorphic phase transformations of order disorder type. An 1:1 ordered orthorhombic HT form is transformed into a higher ordered LT modification with a fourfold cell content (four formula units Ba/sub 8/Bsup(II)B/sub 2/sup(III)vacantU/sub 4/O/sub 24/), compared to cubic 1:1 ordered perovskites A/sub 2/BMO/sub 6/. In the series Ba/sub 8/BaB/sub 2/sup(III)vacantW/sub 4/O/sub 24/ and Sr/sub 8/SrB/sub 2/sup(III)vacantW/sub 4/O/sub 24/ different ordering phenomena are observed. In comparison with 1:1 ordered cubic perovskites A/sub 2/BMO/sub 6/, the cell contains eight formula units A/sub 8/sup(II)Bsup(II) B/sub 2/sup(III)vacantW/sub 4/O/sub 2/4. The higher ordered cells with Usup(VI) and Wsup(VI) are face centered, which has its origin in an ordering of cationic vacancies.