Investigations on the binary systems chromium-, columbium-, nickel-, and thorium-boron are reported. The titanium-boron system is discussed, and it is shown that the phase TiB, previously assumed to have zincblende structure, probably has a face-centered titanium lattice with boron in the octahedral interstices. In the chromium-boron system, the structure of the eta phase has been determined. It has the composition Cr/sub 3/B/sub 4/ and is isomorphous with Ta/sub 3/B/sub 4/ and Mn/sub 3/B/sub 4/. Some data for the delta phase are also given. For the columbium-boron system, a phase analysis has been carried out. The structures of three of the intermediary phases, CbB, Cb/sub 3/B/sub 2/, and CbB/sub 2/ (with extended homogeneity range), have been determined. They are isomorphous with corresponding phases of the tantalum-boron system. A brief phase analysis of the nickel-boron system showed the existence of a phase with lower boron content than Ni/sub 2/B, which has not been previously reported. In the thorium-boron system a new phase, probably with a complicated structure, was found with a boron content of about 50 at. %.