Abstract
New perovskite oxides of the formula AThV/sub 2/O/sub 6/ (A=Ca,Sr) have been prepared by reduction of the corresponding AThV/sub 2/O/sub 8/ under hydrogen atmosphere. CaThV/sub 2/O/sub 6/ crystallizes in an orthorhombic LaVO/sub 3/ type structure, while the strontium compound exhibiting cation-deficient nonstoichiometry. SrThsub(1-x)V/sub 2/O/sub 6/ (x approx. 0.4), is cubic. The magnetic susceptibility behaviour of the calcium compound is similar to that of V/sup 3 +/ perovskites, while the strontium compound exhibits a large increase in susceptibility below 130K, the behaviour being likely to be associated with the mixed-valence character of vanadium.
Citation Formats
Vidyasagar, K, and Gopalakrishnan, J.
New vanadium oxides with perovskite type structure: AThV/sub 2/O/sub 6/ (A=Ca,Sr).
India: N. p.,
1982.
Web.
Vidyasagar, K, & Gopalakrishnan, J.
New vanadium oxides with perovskite type structure: AThV/sub 2/O/sub 6/ (A=Ca,Sr).
India.
Vidyasagar, K, and Gopalakrishnan, J.
1982.
"New vanadium oxides with perovskite type structure: AThV/sub 2/O/sub 6/ (A=Ca,Sr)."
India.
@misc{etde_5815691,
title = {New vanadium oxides with perovskite type structure: AThV/sub 2/O/sub 6/ (A=Ca,Sr)}
author = {Vidyasagar, K, and Gopalakrishnan, J}
abstractNote = {New perovskite oxides of the formula AThV/sub 2/O/sub 6/ (A=Ca,Sr) have been prepared by reduction of the corresponding AThV/sub 2/O/sub 8/ under hydrogen atmosphere. CaThV/sub 2/O/sub 6/ crystallizes in an orthorhombic LaVO/sub 3/ type structure, while the strontium compound exhibiting cation-deficient nonstoichiometry. SrThsub(1-x)V/sub 2/O/sub 6/ (x approx. 0.4), is cubic. The magnetic susceptibility behaviour of the calcium compound is similar to that of V/sup 3 +/ perovskites, while the strontium compound exhibits a large increase in susceptibility below 130K, the behaviour being likely to be associated with the mixed-valence character of vanadium.}
journal = []
volume = {21:7}
journal type = {AC}
place = {India}
year = {1982}
month = {Jul}
}
title = {New vanadium oxides with perovskite type structure: AThV/sub 2/O/sub 6/ (A=Ca,Sr)}
author = {Vidyasagar, K, and Gopalakrishnan, J}
abstractNote = {New perovskite oxides of the formula AThV/sub 2/O/sub 6/ (A=Ca,Sr) have been prepared by reduction of the corresponding AThV/sub 2/O/sub 8/ under hydrogen atmosphere. CaThV/sub 2/O/sub 6/ crystallizes in an orthorhombic LaVO/sub 3/ type structure, while the strontium compound exhibiting cation-deficient nonstoichiometry. SrThsub(1-x)V/sub 2/O/sub 6/ (x approx. 0.4), is cubic. The magnetic susceptibility behaviour of the calcium compound is similar to that of V/sup 3 +/ perovskites, while the strontium compound exhibits a large increase in susceptibility below 130K, the behaviour being likely to be associated with the mixed-valence character of vanadium.}
journal = []
volume = {21:7}
journal type = {AC}
place = {India}
year = {1982}
month = {Jul}
}