Abstract
Measurements have been performed of cubic-tetragonal transition temperatures and magnetic properties on a set of those samples of the binary system CuO-Fe/sub 2/O/sub 3/ which contain Fe/sub 2/O/sub 3/ more than stoichiometric CuFe/sub 2/O/sub 4/. A marked magnetic hardening was observed on a sample of 40CuO.60Fe/sub 2/O/sub 3/ which has been verified, through the X-ray analyses and measurements of Moessbauer spectra, to result from the precipitation of ..cap alpha..-Fe/sub 2/O/sub 3/ taking place during annealing.
Sugimoto, M
[1]
- Saitama Univ., Urawa (Japan)
Citation Formats
Sugimoto, M.
Cubic-tetragonal transformation and magnetic properties in copper ferrites with excess Fe/sub 2/O/sub 3/.
France: N. p.,
1977.
Web.
Sugimoto, M.
Cubic-tetragonal transformation and magnetic properties in copper ferrites with excess Fe/sub 2/O/sub 3/.
France.
Sugimoto, M.
1977.
"Cubic-tetragonal transformation and magnetic properties in copper ferrites with excess Fe/sub 2/O/sub 3/."
France.
@misc{etde_5363470,
title = {Cubic-tetragonal transformation and magnetic properties in copper ferrites with excess Fe/sub 2/O/sub 3/}
author = {Sugimoto, M}
abstractNote = {Measurements have been performed of cubic-tetragonal transition temperatures and magnetic properties on a set of those samples of the binary system CuO-Fe/sub 2/O/sub 3/ which contain Fe/sub 2/O/sub 3/ more than stoichiometric CuFe/sub 2/O/sub 4/. A marked magnetic hardening was observed on a sample of 40CuO.60Fe/sub 2/O/sub 3/ which has been verified, through the X-ray analyses and measurements of Moessbauer spectra, to result from the precipitation of ..cap alpha..-Fe/sub 2/O/sub 3/ taking place during annealing.}
journal = []
volume = {1}
place = {France}
year = {1977}
month = {Jan}
}
title = {Cubic-tetragonal transformation and magnetic properties in copper ferrites with excess Fe/sub 2/O/sub 3/}
author = {Sugimoto, M}
abstractNote = {Measurements have been performed of cubic-tetragonal transition temperatures and magnetic properties on a set of those samples of the binary system CuO-Fe/sub 2/O/sub 3/ which contain Fe/sub 2/O/sub 3/ more than stoichiometric CuFe/sub 2/O/sub 4/. A marked magnetic hardening was observed on a sample of 40CuO.60Fe/sub 2/O/sub 3/ which has been verified, through the X-ray analyses and measurements of Moessbauer spectra, to result from the precipitation of ..cap alpha..-Fe/sub 2/O/sub 3/ taking place during annealing.}
journal = []
volume = {1}
place = {France}
year = {1977}
month = {Jan}
}