The effects of annealing of evaporated tin sulphide thin films (SnS) are described. The films were initially deposited onto glass substrate, followed by annealing in an encapsulated carbon block under the running argon gas at 310 degree Celsius. Short time annealing of the films results in a slight change of the compositions to a mix SnS/SnS sub 2 compound, and the tendency of increasing SnS sub 2 formation was observed on the films annealed for longer periods up to 20 hours. X-ray results showed the transformation of SnS peaks (040) and (080) to predominantly SnS sub 2 peaks - (001), (100), (101), and (110). The associated absorption coefficients measured on the films were found to be greater than 10 sup 5 cm sup -1, with indication of higher photon energy leading to the formation of SnS sub 2 compound.