Abstract
A new perovskite La sub(2/3)(Mg sub(1/2)W sub(1/2))O/sub 3/ having an orthorhombic multiple-cell was synthesized. The lattice constants were a = 7.8157(5) A, b = 7.8344(6) A and c = 2 x 7.9067(6) A. The superstructure was found to be due to a NaCl-type ordering of B ions as well as an ordering of A-site vacancies.
Torii, Y
[1]
- Government Industrial Research Inst., Nagoya (Japan)
Citation Formats
Torii, Y.
Synthesis and superstructure of La sub(2/3) (Mg sub(1/2)W sub(1/2))O/sub 3/.
Japan: N. p.,
1979.
Web.
Torii, Y.
Synthesis and superstructure of La sub(2/3) (Mg sub(1/2)W sub(1/2))O/sub 3/.
Japan.
Torii, Y.
1979.
"Synthesis and superstructure of La sub(2/3) (Mg sub(1/2)W sub(1/2))O/sub 3/."
Japan.
@misc{etde_5167129,
title = {Synthesis and superstructure of La sub(2/3) (Mg sub(1/2)W sub(1/2))O/sub 3/}
author = {Torii, Y}
abstractNote = {A new perovskite La sub(2/3)(Mg sub(1/2)W sub(1/2))O/sub 3/ having an orthorhombic multiple-cell was synthesized. The lattice constants were a = 7.8157(5) A, b = 7.8344(6) A and c = 2 x 7.9067(6) A. The superstructure was found to be due to a NaCl-type ordering of B ions as well as an ordering of A-site vacancies.}
journal = []
volume = {1979:10}
journal type = {AC}
place = {Japan}
year = {1979}
month = {Oct}
}
title = {Synthesis and superstructure of La sub(2/3) (Mg sub(1/2)W sub(1/2))O/sub 3/}
author = {Torii, Y}
abstractNote = {A new perovskite La sub(2/3)(Mg sub(1/2)W sub(1/2))O/sub 3/ having an orthorhombic multiple-cell was synthesized. The lattice constants were a = 7.8157(5) A, b = 7.8344(6) A and c = 2 x 7.9067(6) A. The superstructure was found to be due to a NaCl-type ordering of B ions as well as an ordering of A-site vacancies.}
journal = []
volume = {1979:10}
journal type = {AC}
place = {Japan}
year = {1979}
month = {Oct}
}